对Fe52Co34Hf7B6Cu1非晶合金进行了低频磁脉冲处理,研究低温真空退火对磁脉冲处理Fe52Co34Hf7B6Cu1非晶软磁性能的影响. 结果表明, 磁脉冲处理导致非晶合金发生纳米晶化,析出晶态相α-Fe(Co), 晶粒尺寸为5-10 nm, 形成的纳米晶粒弥散分布于非晶基体的双相纳米合金中. 对磁脉冲处理的试样进行低温真空退火,可以进一步优化纳米合金的软磁性能, 在100 ℃退火可以得到最佳的软磁性能.
The nanocrystalline Fe52Co34Hf7B6Cu1 soft magnatic alloys composed of bcc-Fe nanocrystals embedded in a residual amorphous matrix were obtained by the magneto-crystallization of melt-spun ribbons. In order to improve the soft magnetic properties of double--phase Fe(Co)--based nanocrystalline alloy, the nanocrystalline alloy specimens were vacuum annealed for 30 min at 100, 200 and 300 ℃. The results showed that the treatment of magnetic pulsing on the amorphous alloy resulted in the nanocrystallization, the grain size of precipitated α-Fe(Co) nanocrystallized phase was 5-10 nm. The low-temperature vacuum annealing of magnetic pulsed specimens further improved the soft magnetic properties of nanocrystalline alloy. The influence of annealing at 100 ℃ for 30 min on the properties is most obvious.
参考文献
[1] | |
[2] | |
[3] | |
[4] | |
[5] | |
[6] | |
[7] | |
[8] | |
[9] | |
[10] | |
[11] | |
[12] | |
[13] | |
[14] | |
[15] | |
[16] | |
[17] | |
[18] | |
[19] | |
[20] | |
[21] | |
[22] | |
[23] | |
[24] | |
[25] | |
[26] | |
[27] | |
[28] | |
[29] | |
[30] | |
[31] | |
[32] | |
[33] | |
[34] | |
[35] | |
[36] | |
[37] | |
[38] | |
[39] | |
[40] | |
[41] | |
[42] | |
[43] | |
[44] | |
[45] | |
[46] | |
[47] | |
[48] | |
[49] | |
[50] | |
[51] | |
[52] | |
[53] | |
[54] | Kowalczyk M, Ferenc J, Liang X B, Kulik T.  |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%