Aluminum foam sandwich was prepared by rolling-bonding/powder metallurgical foaming technology,and the effects of rolling on bond strength of face sheet/powders and powder density were studied.Moreover,the foaming agent,TiH2,was heat treated and a certain amount of Mg was added into powder in an attempt to understand how the stability and uniformity of foam was improved.The experimental results show that the foaming precursors with ideal quality were obtained by rolling-bonding process.When rolling reduction is 67%,the consistency of powders reach to 99.87%.Throughout consideration of the bonding of face sheet/core layer powders and deformation characteristic of powders,the optimum rolling reduction is 60%-70%.Cracks and drainage during foaming were inhibited by heat treatment of foaming agent TiH2 and the addition of a certain amount of Mg.The optimum heat treatment way of TiH2 is that heat preserving 1 hour at 450 ℃;the amount of adding Mg is 1wt%.
参考文献
| [1] | H.-W. Seeliger .Aluminium Foam Sandwich (AFS) Ready for Market Introduction[J].Advanced Engineering Materials,2004(6):448-451. |
| [2] | Carolin Korner;Robert F. Singer .Processing of metal foams- challenges and opportunities[J].Advanced Engineering Materials,2000(4):159-165. |
| [3] | Matijasevic-Lux B;Banhart J;Fiechter S;Gorke O;Wanderka N .Modification of titanium hydride for improved aluminium foam manufacture[J].Acta materialia,2006(7):1887-1900. |
| [4] | J. BANHART;D. BELLMANN;H. CLEMENS .INVESTIGATION OF METAL FOAM FORMATION BY MICROSCOPY AND ULTRA SMALL-ANGLE NEUTRON SCATTERING[J].Acta materialia,2001(17):3409-3420. |
| [5] | F. von Zeppelin;M. Hirscher;H. Stanzick .Desorption of hydrogen from blowing agents used for foaming metals[J].Composites science and technology,2003(16):2293-2300. |
| [6] | I.Duarte;J.Banhart .A Study of Aluminium Foam Formation—Kinetics and Microstructure[J].Acta materialia,2000(9):2349-2362. |
| [7] | Stobener K;Lehmhus D;Avalle M;Peroni L;Busse M .Aluminum foam-polymer hybrid structures (APM aluminum foam) in compression testing[J].International Journal of Solids and Structures,2008(21):5627-5641. |
| [8] | 张敏,祖国胤,姚广春.镁的添加对制备泡沫铝夹芯板泡孔稳定性的影响[J].功能材料,2007(04):576-579. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%