Amorphous GdTbFeCo magnetic thin films were successfully prepared on glass substrates by RF magnetron sputtering system from a mosaic target.The influences of sputtering parameters on the magnetooptical properties GdTbFeCo thin film were investigated by the variable control method.And the influence mechanism was analyzed in detail.After the sputtering parameters were optimized,it was found that when the distance between target and substrate was 72 mm,the thin film thickness was 120 nm,and the sputtering power,sputtering pressure and sputtering time was 75 W,0.5 Pa and 613 s,respectively,the coercivity with perpendicular anisotropy could be as high as 6735 Oe,and the squareness ratio of the hysteresis loop was almost equal to 1.
参考文献
| [1] | T. Rahman;X. Liu;A. Morisako .TbFeco film with W underlayer and overlayer for perpendicular magnetic recording[J].Journal of Magnetism and Magnetic Materials,2005(0):250-254. |
| [2] | M. Futamoto;N. Inaba .Microstructure and micromagnetics of future thin-film media[J].Journal of Magnetism and Magnetic Materials,1999(1/3):36-43. |
| [3] | Manfred E. Schabes;Eric E. Fullerton;David T. Margulies .Theory of antiferromagnetically coupled magnetic recording media[J].IEEE Transactions on Magnetics,2001(4 Pt.1):1432-1434. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%