The preforms with high SiC volume fraction (>50%) were successfully fabricated by two bonding methods. Moreover, the dimensional change, compressive strength, and microstructure of SiC preforms were investigated, and the bonding mechanism among SiC particulates in preforms was also discussed. Results show that, after heating to 1 100? and holding for 2 h, a uniform and interconnected structure in the SiC preforms can be obtained by using starch, stearic acid, and graphite respectively as the pore-forming agents, which benefi ts the subsequent infi ltration by the molten metals. More neck-like-jointing among SiC particulate by using graphite as the pore-forming agent improves the dimensional accuracy and compressive strength of the preform. Besides, the properties of the preforms by the binder bonding are better than those by the oxidation bonding, which is mainly because the mixed neck-like-jointing and binder at high temperature provide effective bonding together.
参考文献
| [1] | Kaczmar J.W.;Pietrzak K. .The production and application of metal matrix composite materials[J].Journal of Materials Processing Technology,2000(1/3):58-67. |
| [2] | Huaping Xiong;Bowen Xiong;Huan Yu;Jiaqi Zhao;Yuhui Zheng;Ying Luo;Zhifeng Xu;Peilan Zhu .Effects of binders on dimensional accuracy and mechanical properties of SiC particulates preforms fabricated by selective laser sintering[J].Composites, Part B. Engineering,2013(1):480-483. |
| [3] | Satoh Akinobu .Water glass bonding[J].Sensors and Actuators, A. Physical,1999(2):160-168. |
| [4] | H. S. Lee;S. H. Hong .Pressure infiltration casting process and thermophysical properties of high volume fraction SiC_p/Al metal matrix composites[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(8):1057-1064. |
| [5] | Hongwen Zhang;Josh Loukus;Adam Loukus .Improvement Of The Bonding Interface In Hybrid Fiber/particle Preform Reinforced Al Matrix Composite[J].Materials Letters,2009(2):310-312. |
| [6] | Zuzana Zivcova;Eva Gregorova;Willi Pabst .Thermal conductivity of porous alumina ceramics prepared using starch as a pore-forming agent[J].Journal of the European Ceramic Society,2009(3):347-353. |
| [7] | P. Romano;F. J. Velasco;J. M. Torralba;N. Candela .Processing of M2 powder metallurgy high-speed steel by means of starch consolidation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):1-7. |
| [8] | Xiaojian Mao;Shiwei Wang;Shunzo Shimai .Porous ceramics with tri-modal pores prepared by foaming and starch consolidation[J].CERAMICS INTERNATIONAL,2008(1):107-112. |
| [9] | Qiang Zhang;Xiangyu Ma;Gaohui Wu .Interfacial microstructure of SiCp/Al composite produced by the pressureless infiltration technique[J].CERAMICS INTERNATIONAL,2013(5):4893-4897. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%