The aim of this work was to prepare MgF2 translucent ceramic by using nanopowders as raw materials and to study its properties.The MgF2 nanopowders were prepared using chemical precipitation and the translucent ceramics were fabricated by hot-pressing sintering in a vacuum environment. X-ray diffraction analysis showed that the powders were homogeneous with an average particles size about 13 nm. By comparing the results of transmission electron microscopy, it could be concluded that the porous structure of precursor powders could be improved by calcination. The SEM images of MgF2 indicated that the as-prepared ceramics were well densified at 900℃. The photo of the ceramic sample showed that high translucence is a main breakthrough in the ifeld of MgF2 materials preparation. For the translucent ceramic sample sintered at 900℃, the Vickers hardness and density were 5.55 GPa and 98.74%, respectively, and its highest transmittance with thickness of 1mm reached 87% in the wavelength from 2.5 μm to 10 μm, all which made it advantageous to be a kind of infrared windows and dome materials.
参考文献
| [1] | Nandiyanto, A.B.D.;Iskandar, F.;Ogi, T.;Okuyama, K. .Nanometer to submicrometer magnesium fluoride particles with controllable morphology[J].Langmuir: The ACS Journal of Surfaces and Colloids,2010(14):12260-12266. |
| [2] | Lin WY;Hon MH;Yang SJ .Effect of Grain Growth on Hot-Pressed Optical Magnesium Fluoride Ceramics[J].Journal of the American Ceramic Society,1988,71(03):C-136-C-137. |
| [3] | Chen SC;Min HH;Sheng JY .Effects of Calcination and Hot-Pressing Temperatures of Magnesium Fluoride Powder on Its Optical Property[J].Japanese Journal of Applied Physics,1990,29(12):2751-2754. |
| [4] | Chang CS;Hon MH;Yang SJ .The Optical Properties of Hot-pressed Magnesium Fluoride and Single-crystal Magnesium Fluoride in the 0.1 to 9 0 μm Range[J].Journal of Materials Science,1991,26(06):1627-1630. |
| [5] | Recker K;Leckebusch R .Vapor Phase Growth of Single Crystals of High-Melting Fluorides. I Magnesium Fluoride[J].Journal of Crystal Growth,1969,5(02):125-131. |
| [6] | Rice HH;Garey MJ .Sintering of Magnesium Fluoride[J].American Ceramic Society of Bulletin,1967,46(12):1149-1153. |
| [7] | MALTSEV MV;Udalova LV;Goryachev AY et al.Fabrication of Optical-ceramic Preforms without Mechanical Treatment[J].Soviet J Opt Technol,1993,60(01):67-69. |
| [8] | Shirakawa Y;Harada T;Sashida N et al.Preparation of MgF2 Sintered Body by Normal Sintering Combined with Capsule-free Hot-isostatic Pressing Treatment[J].Nippon seramikkusu kyokai gakujutsu ronbunshi,1999,107(12):1137-1139. |
| [9] | Nofar M;Hosseini HRM;Shivaee HA .The dependency of optical properties on density for hot pressed MgF2[J].Infrared physics and technology,2008(6):546-549. |
| [10] | Buckner DA;Hafner HC;Kreidl NJ .Hot-Pressing Magnesium Fluoride[J].Journal of the American Ceramic Society,1962,45(09):435-438. |
| [11] | Chen SC;Min HH .Texture Effect of Hot-pressed Magnesium Fluoride on Optical Transmittance[J].Materials Chemistry and Physics,2003),81:27-32. |
| [12] | Ikesue A.;Kamata K.;Furusato I. .FABRICATION OF POLYCRYSTALLINE, TRANSPARENT YAG CERAMICS BY A SOLID-STATE REACTION METHOD[J].Journal of the American Ceramic Society,1995(1):225-228. |
| [13] | Ikesue A.;Kamata K.;Yoshida K.;Kinoshita T. .FABRICATION AND OPTICAL PROPERTIES OF HIGH-PERFORMANCE POLYCRYSTALLINE ND-YAG CERAMICS FOR SOLID-STATE LASERS[J].Journal of the American Ceramic Society,1995(4):1033-1040. |
| [14] | Yu.L. Kopylov;V.B. Kravchenko;A.A. Komarov;Z.M. Lebedeva;V.V. Shemet .Nd:Y_2O_3 nanopowders for laser ceramics[J].Optical materials,2007(10):1236-1239. |
| [15] | Zhang J;Wang SW;An LQ;Liu M;Chen LD .Infrared to visible upconversion luminescence in Er3+: Y2O3 transparent ceramics[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2007(0):8-10. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%