Firm joins were obtained between Ti(C,N)-based cermet and steel with Ag-Cu-Zn-Ni filler metal by vacuum brazing. The effects of techno-logical parameters such as brazing temperature, holding time, and filler thickness on the shear strength of the joints were investigated. The microstructure of welded area and the reaction products of the filler metal were examined by scanning electron microscopy (SEM), metal-lographic microscope (OM), energy-dispersive X-ray analysis (EDS), and X-ray diffraction (XRD). The brazing temperature of 870℃, holding time of 15 min, and filler thickness of 0.4 mm are a set of optimum technological parameters, under which the maximum shear strength of the joints, 176.5 MPa, is achieved. The results of microstructure show that the wettability of the fdler metal on Ti(C,N)-based cermet and steel is well. A mutual solution layer and a diffusion layer exist between the welding base materials and the filler metal.
参考文献
| [1] | Jung J.K;Kang S;Kang S .Effect of ultra-fine powders on the microstructure of Ti(CN)-xWC-Ni cermets[J].Acta Mater,2004,52:1379. |
| [2] | Ettmayer P;Kolaska H;Lengauer W;Ettmayer P.Kolaska H. Lengauer W.Ti(C,N)cermets-metallurgy and properties[J].Int J Refract Met Hard Mater,1995(13):343. |
| [3] | Ahn S.Y;Kang S;Kang S .Effect of WC particle size on microstructure and rim composition in the Ti(C_0.7N_0.3)-WC-Ni system[J].Scripta Materialia,2006,55:1015. |
| [4] | Hiroshi M.Advances in Joining Newer Structure Materials[M].Pemamon Press,London,1990:137. |
| [5] | Rice J.P;Paxton D.M;Weil K.S;Rice J.P Paxton D.M and Weil K.S .Oxidation behavior of a commercial gold-based braze alloy for ceramic-to-metal joining[J].Cream Eng Sci Proc,2002,23:809. |
| [6] | Zhang C.G;Qiao G.J;Jin Z.H;Zhang C.G Qiao G.J and Jin Z.H .Active brazing of pure alumina to kovar alloy based on the partial transient liquid phase(PTLP)technique with Ni-Ti interlayer[J].Journal of the European Ceramic Society,2002,22:2181. |
| [7] | Vianceo P.T;Stephens J.J;Hlava P.F;Walker C.A .Titanium scavenging in Ag-Cu-Ti active braze joints[J].Weld Res,2003,82:268. |
| [8] | Chaumat G;Drevet B;Vernier L;Chaumat G Drevet B and Vernier L .Reactive brazing study of a silicon nitride to metal joining[J].Journal of Fur Ceram Soc,1997,17:1925. |
| [9] | Zhang L.X;Feng J.C;Feng J.C .Ag-Cu-Zn alloy for brazing TiC cermet/steel[J].Materials Letters,2005,59:110. |
| [10] | Kliauga A.M;Travessa D;Ferrante M;Kliauga A.M Travessa D and Ferrante M .Al_2O_3/Ti interlayer/AISI 304 diffusion bonded joint:microstructural characterization of the two interfaces[J].Materials Characterization,2001,46:65. |
| [11] | Travessa D.;Ferrante M.;den Ouden G. .Diffusion bonding of aluminium oxide to stainless steel using stress relief interlayers[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):287-296. |
| [12] | Matsuoka S.I .Ultrasonic welding of ceramic/metal[J].Journal of Materials Processing Technology,1994,47:185. |
| [13] | Feng J.C;Zhang L.X;Zhang L.X .Interface structure and mechanical properties of the brazed joint of TiC cermet and steel[J].Journal of the European Ceramic Society,2006,26:1287. |
| [14] | Elsawy A.H;Fahmy M.F;Fahmy M.F .Brazing of Si_3N_4 ceramic to copper[J].Journal of Materials Processing Technology,1998,77:266. |
| [15] | Sciti D;Bellosi A;Bellosi A .Bonding of zirconia to super alloy with the active brazing technique[J].Journal of the European Ceramic Society,2001,21:45. |
| [16] | Arroyave R;Eagar T.W;Eagar T.W .Metal substrate effects on the thermochemistry of active brazing interfaces[J].Acta Mater,2003,51:4871. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%