In Situ HRTEM Observation of Electron-Irradiation-Induced Amorphization and Dissolution of the E (Al18Cr2Mg3) Phase in 7475 Al Alloy

1.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China

2.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China

3.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China

4.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China

5.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China

6.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China

7.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China

基金项目: The work was financially supported by the 111 Project (No.B08040) of China and National Natural Science Foundation of China (No.51071125).

[1]	A. T. Motta;L. M. Howe;P. R. Okamoto .Amorphization of Zr_Fe under electron irradiation[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,1999(s12):174-186.
[2]	T. Nagase;Y. Umakoshi .Mater Phase stability of amorphous and crystalline phases in melt-spun Zr_(66.7)Cu_(33.3) alloy under electron irradiation[J].Scripta materialia,2003(9):1237-1242.
[3]	R. F. Egerton;P. Li;M. Malac .Radiation damage in the TEM and SEM[J].Micron: The international research and review journal for microscopy,2004(6):399-409.

上一张下一张

计量

作者相关

文章评分

材料期刊网