In Situ TEM Observation on Martensitic Transformation during Tensile Deformation of SUS304 Metastable Austenitic Stainless Steel

1.Department of Plasticity Technology, School of Materials Science and Engineering, Shanghai Jiao Tong University,Shanghai 200030,China

2.Department of Plasticity Technology, School of Materials Science and Engineering, Shanghai Jiao Tong University,Shanghai 200030,China

3.Department of Mechanical Engineering, Northwestern University, Evanston, IL 60208-3109, USA

4.Department of Plasticity Technology, School of Materials Science and Engineering, Shanghai Jiao Tong University,Shanghai 200030,China

5.Department of Plasticity Technology, School of Materials Science and Engineering, Shanghai Jiao Tong University,Shanghai 200030,China

基金项目: This work was financially supported by the National Natural Science Foundation of China (No.51105248).

Keywords： In situ TEM

[1]	L. Bracke;L. Kestens;J. Penning .Transformation mechanism of α′-martensite in an austenitic Fe–Mn–C–N alloy[J].Scripta materialia,2007(5):385-388.
[2]	J. Talonen;H. Hanninen .Formation of shear bands and strain-induced martensite during plastic deformation of metastable austenitic stainless steels[J].Acta materialia,2007(18):6108-6118.
[3]	A.Y. Chen;H.H. Ruan;J. Wang .The influence of strain rate on the microstructure transition of 304 stainless steel[J].Acta materialia,2011(9):3697-3709.
[4]	S. Allain;J.-P. Chateau;O. Bouaziz .A physical model of the twinning-induced plasticity effect in a high manganese austenitic steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(0):143-147.
[5]	R.D.K. MISRA;S. NAYAK;P.K.C. VENKATASURYA;V. RAMUNI;M.C. SOMANI;L.P. KARJALAINEN .Nanograined/Ultrafine-Grained Structure and Tensile Deformation Behavior of Shear Phase Reversion-Induced 301 Austenitic Stainless Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2010(8):2162-2174.

上一张下一张

计量

作者相关

文章评分

材料期刊网