The compressive strength developing process and the microstructure of cement-asphalt mortar (CA mortar) were investigated.The fluidity of CA mortar has a great influence on its strength.The optimum value of spread diameter of slump flow test is in the range of 300 to 400 mm.The compressive strength of CA mortar keeps a relatively high growth rate in 56 days and grows slowly afterwards.The residual water of hydration in CA mortar freezes under minus environmental temperature which can lead to a significant reduction of the strength of CA mortar.Increasing A/C retards asphalt emulsion splitting and thus prolongs the setting process of CA mortar.The hydration products of cement form the major structural framework of hardened CA mortar and asphalt is a weak phase in the framework but improves the viscoelastic behavior of CA mortar.Therefore,asphalt emulsion should be used as much as possible on the condition that essential performance criterions of CA mortar are satisfied.
参考文献
| [1] | Fazhou Wang;Zhichao Liu;Tao Wang;Shuguang Hu .A novel method to evaluate the setting process of cement and asphalt emulsion in CA mortar[J].Materials and structures,2008(4):643-647. |
| [2] | 赵东田,王铁成,刘学毅,伍林.板式无碴轨道CA砂浆的配制和性能[J].天津大学学报,2008(07):793-799. |
| [3] | 左景奇,姜其斌,蔡彬芬.板式轨道CA砂浆专用沥青乳液的试验研究[J].铁道建筑技术,2005(02):68-70. |
| [4] | 金守华,陈秀方,杨军.板式无碴轨道用CA砂浆的关键技术[J].中国铁道科学,2006(02):20-25. |
| [5] | 王发洲,王涛,胡曙光,刘志超,高涛,陈亮.CA砂浆的流变特性[J].武汉大学学报（工学版）,2008(04):69-72. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%