The influence of cooling rate and addition of La and Ce on the formation of nanoporous copper by chemical dealloying of Cu15Al85 alloy was studied. The components and microstructures of nanoporous copper were characterized by utilizing X-ray diffrac-tion, field emission scanning electron microscopy and energy dispersive X-ray analysis. N2 adsorption/desorption experiments were used to evaluate specific surface areas of samples. The results showed that, with the increase of cooling rate, phase composition of precursor alloy almost had no change, the ligament size of nanoporous copper had a decrease trend, and specific surface area in-creased gradually. And it was found that the specific surface area of the nanoporous copper obtained by Cu15Al85 alloy containing La and Ce was 63.258 m2/g, which was more than 11.739 m2/g compared with the nanoporous copper dealloying by Cu15Al85 alloy without La and Ce under the same conditions.
参考文献
| [1] | Bond G C;Thompson D T .Catalysis by gold[J].Catalyst Reviews,1999,41:319. |
| [2] | You TY.;Niwa O.;Tomita M.;Hirono S. .Characterization of platinum nanoparticle-embedded carbon film electrode and its detection of hydrogen peroxide[J].Analytical chemistry,2003(9):2080-2085. |
| [3] | Weissmuller J.;Viswanath RN.;Kramer D.;Zimmer P.;Wurschum R.;Gleiter H. .Charge-induced reversible strain in a metal[J].Science,2003(5617):312-315. |
| [4] | Joo S H;Choi S J;Kwa K J;Liu Z .Ordered nanoporous arrays of carbon supporting high dispersions of platinum nanoparticles[J].Nature,2001,412:169. |
| [5] | Zhang Z H;Wang Y;Qi Z;Somsen C,Wang X G,Zhao C C .Fabrication and characterization of nanoporous gold composites through chemical dealloying of two phase Al-Au alloys[J].Journal of Materials Chemistry,2009,19:6042. |
| [6] | Thorp J C;Sieradzki K;Tang L;Crozier P A,Misra A .Formation of nanoporous noble metal thin films by elec-trochemical dealloying of PtxSi1-x[J].Applied Physics Letters,2006,88:033110. |
| [7] | Wang X G;Qi Z;Zhao C C;Wang W M,Zhang Z H .In-fluence of alloy composition and dealloying solution on the formation and microstructure of monolithic nanopor-ous silver through chemical dealloying of Al-Ag alloys[J].Journal of Physical Chemistry C,2009,113:13139. |
| [8] | Qi Z;Zhao C C;Wang X G;Lin J K,Shao W,Zhang Z H,Bian X F .Formation and characterization of monolithic nanoporous copper by chemical dealloying of Al-Cu al-loys[J].Journal of Physical Chemistry C,2009,113:6694. |
| [9] | Liu W B;Zhang S C;Li N;Zheng J W,Xing Y L .Influence of phase constituent and proportion in initial Al-Cu alloys on formation of monolithic nanoporous cop-per through chemical dealloying in an alkaline solution[J].Corrosion Science,2011,53:809. |
| [10] | Zhang Z H;Wang Y;Wang Y Z;Wang X G Qi Z Ji H Zhao C C .Formation of ultrafine nanoporous gold related to surface diffusion of gold adatoms during dealloying of Al2Au in an alkaline solution[J].Scripta Materialia,2010,62:137. |
| [11] | Seker E;Gaskins JT;Bart-Smith H;Zhu J;Reed ML;Zangari G;Kelly R;Begley MR .The effects of post-fabrication annealing on the mechanical properties of freestanding nanoporous gold structures[J].Acta materialia,2007(14):4593-4602. |
| [12] | Zhang Z H;Bian X F;Wang Y .Microstructural charac-terization of a rapidly solidified Al-5Sb alloy[J].Journal of Alloys and Compounds,2003,351:184. |
| [13] | Josh Snyder;Piyapong Asanithi;Alan B. Dalton;Jonah Erlebacher .Stabilized Nanoporous Metals By Dealloying Ternary Alloy Precursors[J].Advanced Materials,2008(24):4883-4886. |
| [14] | Wang X G;Frenzel J;Wang W M;Ji H,Qi Z,Zhang Z H,Eggeler G .Length-scale modulated and electrocatalytic activity enhanced nanoporous gold by doping[J].Journal of Physical Chemistry C,2011,115:4456. |
| [15] | Zuo X R;Zhong Z G .Effect of united refining and modi-fication on mechanical properties of A356 aluminium al-loys[J].Transactions of Nonferrous Metals Society of China,2006,16:1419. |
| [16] | Wang S H;Zhou H P;Kang Y P .The influence of rare earth elements on microstructures and properties of 6061 aluminum alloy vacuum-brazed joints[J].Journal of Alloys and Compounds,2003,352:79. |
| [17] | Li P F;Wu Z G;Wang Y L;Gao X Z,Wang Z Y,Li Z Q .Effect of cerium on mechanical performance and electrical conductivity of aluminum rod for electrical purpose[J].Journal of Rare Earths,2006,24:355. |
| [18] | Li M;Zhou Y Z;Geng H R .Fabrication of nanoporous copper ribbons by dealloying of Al-Cu alloys[J].Journal of Porous Materials,2012,19:791. |
| [19] | Luo X K;Li R;Liu Z Q;Huang L,Shi M J,Xu T,Zhang T .Three-dimensional nanoporous copper with high surface area by dealloying Mg-Cu-Y metallic glasses[J].Materials Letters,2012,76:96. |
| [20] | 于彦冲,陈伟庆,郑宏光.铈及混合稀土对Fe-36Ni低膨胀合金凝固组织的影响[J].中国稀土学报,2012(02):175-180. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%