This work described the preparation of dysprosium oxide, Dy2O3, nanoparticles using the homogeneous precipitation method. Dy3+ions were precipitated using NaOH solution. The obtained product was filtered, dried, and then calcined for 1 h at the temperature range of 300-700 °C in static air. The calcination temperature of the Dy-precursor was chosen based on its decomposi-tion as indicated by the TGA analysis. The crystalline structure and surface morphology of the calcined solids were studied by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM) and X-ray pho-toelectron spectroscopy (XPS). The obtained results revealed that Dy2O3 with crystallites size of 11-21 nm was formed at 500 °C. Such value increased to 25-37 nm for the sample calcined at 700 °C.
参考文献
| [1] | Sreethawong T;Chavadej S;Ngamsinlapasathian S;Yoshikawa S .A simple route utilizing surfactant-assisted templating sol-gel process for synthesis of mesoporous Dy2O3 nanocrystal[J].Journal of Colloid and Interface Science,2006(1):219-224. |
| [2] | Pan T-M;Chang W-T;Chiu F-C .Structural properties and electrical characteristics of high-k Dy2O3 gate dielectrics[J].Applied Surface Sinence,2011,257(09):3964. |
| [3] | E. N. MASLEN;V. A. STRELTSOV;N. ISHIZAWA .A Synchrotron X-ray Study of the Electron Density in C-Type Rare Earth Oxides[J].Acta Crystallographica. Section B, Section B. Structural Science,1996(3):414-422. |
| [4] | Tang M;Valdez JA;Lu P;Gosnell GE;Wetteland CJ;Sickafus KE .A cubic-to-monoclinic structural transformation in the sesquioxide DY2O3 induced by ion irradiation[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2004(1):71-76. |
| [5] | X.L. SUN;A.I.Y.TOK;R. HUEBNER .Phase transformation of ultrafine rare earth oxide powders synthesized by radio frequency plasma spraying[J].Journal of the European Ceramic Society,2007(1):125-130. |
| [6] | Sharma, N.D.;Singh, J.;Dogra, S.;Varandani, D.;Poswal, H.K.;Sharma, S.M.;Bandyopadhyay, A.K. .Pressure-induced anomalous phase transformation in nano-crystalline dysprosium sesquioxide[J].Journal of Raman Spectroscopy: An International Journal for Original Work in All Aspects of Raman Spectroscopy, Including Higher Order Processes, and Also Brillouin- and Rayleigh Scattering,2011(3):438-444. |
| [7] | M. Chandrasekhar;D.V. Sunitha;N. Dhananjaya;H. Nagabhushana;S.C. Sharma;B.M. Nagabhushana;C. Shivakumara;R.P.S. Chakradhar .Structural and phase dependent thermo and photoluminescent properties of Dy(OH)_3 and Dy_2O_3 nanorods[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2012(8):2085-2094. |
| [8] | Chandrasekhar, M.;Sunitha, D.V.;Dhananjaya, N.;Nagabhushana, H.;Sharma, S.C.;Nagabhushana, B.M.;Shivakumara, C.;Chakradhar, R.P.S. .Thermoluminescence response in gamma and UV irradiated Dy _2O _3 nanophosphor[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2012(7):1798-1806. |
| [9] | Kattel,K.;Park,J.Y.;Xu,W.;Kim,H.G.;Lee,E.J.;Bony,B.A.;Heo,W.C.;Jin,S.;Baeck,J.S.;Chang,Y.;Kim,T.J.;Bae,J.E.;Chae,K.S.;Lee,G.H. .Paramagnetic dysprosium oxide nanoparticles and dysprosium hydroxide nanorods as T 2 MRI contrast agents[J].Biomaterials,2012(11):3254-3261. |
| [10] | He, B.;Zhao, L.;Wang, W.;Chen, F.;Xia, C. .Electro-catalytic activity of Dy_2O_3 as a solid oxide fuel cell anode material[J].Electrochemistry communications,2011(2):194-196. |
| [11] | Wang C M;Wang J F;Su W B;Chen H C,Wang C L,Zhang J L,Zang G Z,Qi P,Gai Z G,Ming B Q .Im-provement in the nonlinear electrical characteristics of SnO2 ceramic varistors with Dy2O3 additive[J].Mater Sci Eng B,2006,127(2-3):112. |
| [12] | Inoue H;Sato S;Takahashi R;Izawa Y,Ohno H,Takaha-shi K .Dehydration of 1,4-butanediol over supported rare earth oxide catalysts[J].Appl Catal A,2009,352(1-2):66. |
| [13] | G.A.M. Hussein;W.J. Kroenke;B. Goda;K. Miyaji .Formation of dysprosium oxide from the thermal decomposition of hydrated dysprosium acetate and oxalate Thermoanalytical and microscopic studies[J].Journal of analytical & applied pyrolysis,1997(1):35-51. |
| [14] | Hussein G A M;Korban H;Goda B;Miyaji K .Physico-chemical characterization of the formation course of dys-prosium oxide from hydrated dysprosium nitrate; ther-moanalytical and microscopic studies[J].Colloids Surf A,1997,125(01):63. |
| [15] | Krishna Chandar, N.;Jayavel, R. .Synthesis and photoluminescence properties of HMT passivated Dy _2O _3 nanoparticles[J].Physica, E. Low-dimensional systems & nanostructures,2012(7/8):1315-1319. |
| [16] | Hosokawa S;Iwamoto S;Inoue M .Synthesis of nano-hollow-shaped rare earth oxides by glycothermal treatment of rare earth acetates and subsequent calcination[J].Journal of Alloys and Compounds,2008,457(1-2):510. |
| [17] | Xu Chun Song;Yi Fan Zheng;Yun Wang .Selected-control synthesis of dysprosium hydroxide and oxide nanorods by adjusting hydrothermal temperature[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2008(5):1106-1111. |
| [18] | Zhang N;Yi R;Zhou L B;Gao G H Shi R R Qiu G Z Liu X H .Lanthanide hydroxide nanorods and their thermal decomposition to lanthanide oxide nanorods[J].Materials Chemistry and Physics,2009,114(01):160. |
| [19] | Krishna Chandar, N.;Jayavel, R. .Wet chemical synthesis and characterization of pure and cerium doped Dy _2O _3 nanoparticles[J].The journal of physics and chemistry of solids,2012(9):1164-1169. |
| [20] | Happy;Tok AIY;Su LT;Boey FYC;Ng SH .Homogeneous precipitation of DY2O3 nanoparticies-effects of synthesis parameters[J].Journal of nanoscience and nanotechnology,2007(3):907-915. |
| [21] | Masoud Salavati-Niasari;Jaber Javidi;Fatemeh Davar;Alireza Amini Fazl .Sonochemical synthesis of Dy_2(CO_3)_3 nanoparticles and their conversion to Dy_2O_3 and Dy(OH)_3: Effects of synthesis parameters[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2010(2):500-506. |
| [22] | D'assun;Giolito I;Ionashiro M .Thermal decom-position of the hydrated basic carbonates of lanthanides and yttrium[J].Thermochimica Acta,1989,137(02):319. |
| [23] | D'assun;Ionashiro M;Rasera D E;Giolito I .Thermal decomposition of the hydrated basic carbonates of lanthanides and yttrium in CO2 atmosphere[J].Thermo-chim Acta,1993,219(o L M):225. |
| [24] | Ferrari J L;Parreira R L T;Pires A M;Lima S A M Davolos M R .A route to obtain Gd2O3:Nd3+with different particle size[J].Materials Chemistry and Physics,2011,127(1-2):40. |
| [25] | Jim-Long Her;Tung-Ming Pan;Chih-Hung Lu .Unipolar resistive switching behavior in Dy_2O_3 films for nonvolatile memory applications[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2012(17):5706-5709. |
| [26] | Han K D;Zhang Y J;Cheng T;Fang Z Y Gao M R Xu Z Y Yin X B .Self-assembled synthesis and photolumines-cence properties of uniform Dy2O3 microspheres and tripod-like structures[J].Materials Chemistry and Physics,2009,114(01):430. |
| [27] | Pan T M;Lu C H .Effect of postdeposition annealing on the structural and electrical properties of thin Dy2TiO5 di-electrics[J].THIN SOLID FILMS,2011,519(22):8149. |
| [28] | Qiu Ping;Secco Richard A.;Balog Paul S.;Huang Yining .Effect of multi-stage dehydration on electrical conductivity of zeolite A[J].Solid state ionics,1999(3/4):281-285. |
| [29] | Wang Y;Mori T;Li J-G;Drennan J .Synthesis,characteriza-tion,and electrical conduction of 10 mol.%Dy2O3-doped CeO2 ceramics[J].J Eur Ceram Soc,2005,25(06):949. |
| [30] | Tian CY.;Chan SW. .Ionic conductivities, sintering temperatures and microstructures of bulk ceramic CeO2 doped with Y2O3[J].Solid state ionics,2000(1/2):89-102. |
| [31] | Y. W. Zhang;S. Jin;Y. Yang .Electrical conductivity enhancement in nanocrystalline (RE_(2)O_(3))_(0.08)(ZrO_(2))_(0.92) (RE=Sc, Y) thin films[J].Applied physics letters,2000(21):3409-3411. |
| [32] | S. Shrestha;C.M.Y. Yeung;C. Nunnerley;S.C. Tsang .Comparison of morphology and electrical conductivity of various thin films containing nano-crystalline praseodymium oxide particles[J].Sensors and Actuators, A. Physical,2007(1):191-198. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%