Red phosphors, Li2Sr0.996SiO4: Pr3+0.004, with different hydrothermal conditions were prepared via hydrothermal synthesis and then heat-treatment. The chemical structures of the phosphors were identified with X-ray diffraction (XRD). Surface morpho-logical features were observed by scanning electron microscopic (SEM) investigation. Spectra of excitation and emission for the phosphors were also obtained by a spectrophotometer. Results showed that the optimum conditions were as follows: pH value of so-lution was 1–2, reaction temperature was at 180 oC for 24 h. The as-prepared phosphors exhibited two excitation dominant peaks at 451 and 486 nm, attributed to transitions of3H4→3P2 and3H4→3P0 of Pr3+, respectively. A narrow emission peak at 610 nm corre-sponded to the energy level transition of3P0→3H6 of Pr3+ under excitation of light at 451 nm, which indicated promising candidate red phosphors for blue LED chips.
参考文献
[1] | Han R J;Wang L;Chen K Z;Yang S B .Photolumines-cence properties of Y3Al5O12:Eu nanocrystallites prepared by co-precipitation method using a mixed precipitator of NH4HCO3 and NH3·H2O[J].Mater Sci Eng,B,2010,166:41. |
[2] | Soares M R N;Nico C;Oliveira D;Peres M, Rino L, Fer-nandes A J S, Monteiro T, Mosta F .Red light from ZrO2:Eu3+ nanostructures[J].Mater Sci Eng,B,2012,177:712. |
[3] | Liao J S;Zhang S A;You H Y;Wen H R Chen J L You W X .Energy transfer and luminescence properties of Eu3+-doped NaTb(WO4)2 phosphor prepared by a facile hydrothermal method[J].Optical Materials,2011,33:953. |
[4] | Qin L;Huang Y L;Tsuboi Taiju;Seo Hyo Jin .The red-emitting phosphors of Eu3+-activated MR2(MoO4)4(M=Ba,Sr,Ca;R=La3+,Gd3+,Y3+)for light emitting diodes[J].Materials Research Bulletin,2012,47:4498. |
[5] | Xie R J;Hirosaki N .Silicon-based oxynitride and nitride phosphors for white LEDs-A review[J].SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS,2007,8:588. |
[6] | Kenneth J. Vampola;Natalie N. Fellows;Hisashi Masa;Stuart E. Brinkley;Motoko Furukawa;Roy B. Chung;Hitoshi Sato;Junichi Sonoda;Hirohiko Hirasawa;Michael Iza;Steven P. DenBaars;Shuji Nakamura .Highly efficient broad-area blue and white light-emitting diodes on bulk GaN substrates[J].Physica Status Solidi, A. Applied Research,2009(2):200-202. |
[7] | Narukawa Y;Sano M;Sakamoto T;Yamada T;Mukai T .Successful fabrication of white light emitting diodes by using extremely high external quantum efficiency blue chips[J].Physica Status Solidi, A. Applied Research,2008(5):1081-1085. |
[8] | Schubert, EF;Kim, JK .Solid-state light sources getting smart[J].Science,2005(5726):1274-1278. |
[9] | Xie RJ;Hirosaki N;Sakuma K;Yamamoto Y;Mitomo M .Eu2+-doped Ca-alpha-SiAlON: A yellow phosphor for white light-emitting diodes[J].Applied physics letters,2004(26):5404-5406. |
[10] | Zhang K;Liu H Z;Wu Y T;Hu W B .Co-precipitation synthesis and luminescence behavior of Ce-doped yttrium aluminum garnet(YAG:Ce)phosphor:The effect of pre-cipitant[J].Journal of Alloys and Compounds,2008,453(1-2):265. |
[11] | Yang H;Lee D K;Kim Y S .Spectral variations of nano-sized Y3Al5O12:Ce phosphors via co-doping/substitution and their white LED characteristics[J].Materials Chemistry and Physics,2009,114(2-3):665. |
[12] | Smet PF;Korthout K;Van Haecke JE;Poelman D .Using rare earth doped thiosilicate phosphors in while light emitting LEDs: Towards low colour temperature and high colour rendering[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2008(1/3):264-268. |
[13] | Lu J;Du F P;Zhu R;Huang Y L, Seo H J .Phase forma-tions and tunable red luminescence of Na2CaMg1-xMnx(PO4)2(x=0.05-1.0)[J].Journal of Materials Chemistry,2011,21:16398. |
[14] | Du F P;Nakai Y;Tsuboi T;Huang Y L Seo H J .Lumi-nescence properties and site occupations of Eu3+ions doped in double phosphates Ca9R(PO4)7(R=Al,Lu)[J].Journal of Materials Chemistry,2011,21:4669. |
[15] | Kyeong Youl Jung;Joo Hyun Kim;Yun Chan Kang .Luminescence enhancement of Eu-doped calcium magnesium silicate blue phosphor for UV-LED application[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2009(6):615-619. |
[16] | 陈莹,袁轩一,陈克新,崔巍,葛一瑶.Effect of starting composition and post-anneal on the structure and luminescence properties of Eu-doped Ca-α-SiAlON phosphors prepared by combustion synthesis[J].稀土学报(英文版),2014(06):501-507. |
[17] | Poort S H M;Janssen W;Blasse G .Optical properties of Eu2+-activated orthosilicates and orthophosphates[J].J Al-loys Compd,1997,260(1-2):93. |
[18] | Li Y Y;Li Y X;Wu Y L;Sun W L .Preparation and photo luminescent properties of zinc oxide phosphor[J].Journal of Luminescence,2007,127:177. |
[19] | R. Jabbarov;N. Musayeva;F. Scholz;T. Wunderer;A. N.Turkin;S. S.Shirokov;A. E. Yunovich .Preparation and optical properties of Eu~(2+) doped CaGa_2S_4-CaS composite bicolor phosphor for white LED[J].Physica Status Solidi, A. Applied Research,2009(2):287-292. |
[20] | Xie R J;Hirosaki N;Mitomo M .Oxynitride/nitride phos-phors for white light-emitting diodes(LEDs)[J].J Electro-ceram,2008,21:370. |
[21] | Kechele J A;Oeckler O;Stadler F;Schnick W .Structure elucidation of BaSi2O2N2-A host lattice for rare-earth doped luminescent materials in phosphor-converted(pc)-LEDs[J].Solid State Sciences,2009,11:537. |
[22] | Piao, XQ;Machida, K;Horikawa, T;Yun, BG .Acetate reduction synthesis of Sr2Si5N8:Eu2+ phosphor and its luminescence properties[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2010(1):8-12. |
[23] | Nakano, T;Kawakami, Y;Uematsu, K;Ishigaki, T;Toda, K;Sato, M .Novel Ba-Sc-Si-oxide and oxynitride phosphors for white LED[J].Journal of Luminescence,2009(12):1654-1657. |
[24] | Poort SHM.;Blasse G.;Meyerink A. .LIFETIME MEASUREMENTS IN EU2+-DOPED HOST LATTICES[J].The journal of physics and chemistry of solids,1997(9):1451-1456. |
[25] | Zhang, XM;Li, WL;Seo, HJ .Luminescence and energy transfer in Eu2+, Mn2+ co-doped Li4SrCa(SiO4)(2) for white light-emitting-diodes[J].Physics Letters, A,2009(38):3486-3489. |
[26] | RAO Yang,HU Xiaoye,LIU Tao,ZHOU Xinmu,ZHOU Xuezhen,LI Yongxiu.Pr3+-doped Li2SrSiO4 red phosphor for white LEDs[J].稀土学报(英文版),2011(03):198-201. |
[27] | Chawla S;Kumar N;Chander H .Broad yellow orange emission from SrAl2O4:Pr3+ phosphor with blue excitation for application to white LEDs[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2009(2):114-118. |
[28] | Jia W;Jia D;Rodriguez T;Evans DR;Meltzer RS;Yen WM .UV excitation and trapping centers in CaTiO3 : Pr-3[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2006(0):13-18. |
[29] | Inaguma, Y;Okamoto, M;Tsuchiya, T;Katsumata, T .Occupation site of Pr and luminescent properties in Pr-doped perovskite-type lithium ion-conducting oxides, A(0.6)Li(0.3)Ti(0.5)Ta(0.5)O(3): Pr (A=Ca and Sr)[J].Solid state ionics,2008(21/26):788-792. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%