Tungsten powders and Ce doped powders were prepared by hydrogen reduction combined with the liquid-solid doping method. The phase composition, particle size and powder morphology of Ce doped tungsten powders were analyzed by X-ray diffrac-tion, scanning electron microscopy and transmission electron microscopy, respectively. The results indicated that 10000 ppm Ce doped tungsten oxide powders were consisted of WO3 phase and Ce4W9O33 phase. The hydrogen reduction of Ce doped tungsten powders was basically accomplished at 800 oC for 3 h. The size of Ce doped W powders was remarkably decreased compared to the undoped W powders. The phase of Ce4W9O33 was reduced to Ce2 (WO4)3 phase and Ce2W2O9 phase during the process of hydrogen reduction. Moreover, Ce2 (WO4)3 phase and Ce2W2O9 phase were observed form their morphologies, where the doping content of Ce was more than 100 ppm. The ternary phase embedding into W particles was assigned to Ce2 (WO4)3, while the ternary phase distrib-uting among W particles corresponded to Ce2W2O9. The phase of Ce2 (WO4)3 might be the nucleus of W particles and increase the number of the nucleus. And the particles of Ce2W2O9 covered WO2 particles and might inhibit the growth of W particles. These two reasons resulted in the decrease of the size of Ce doped W particles. Uniform fine W powders were fabricated with the doping content of Ce more than 100 ppm.
参考文献
| [1] | Gu D D, Li Y L, Wang H Q, Jia Q B, Zhang G Q. Micro-structural development and its mechanism of mechanical alloyed nanocrystalline W-10Ni alloy reinforced with Y2O3 nanoparticles. Int. J. Refract. Met. Hard. Mater., 2014, 44:113.,2014. |
| [2] | MA Tengfei,CHEN Ziyong,NIE Zuoren,HUANG Hui.Microstructure of Al-Ti-B-Er refiner and its grain refining performance[J].稀土学报（英文版）,2013(06):622-627. |
| [3] | Trojanova Z, Donic T, Lukac P, Palcek P, Chalupova M, Tillova E, Bastovansky R. Tensile and fracture properties of an Mg-RE-Zn alloy at elevated temperatures. J. Rare Earths, 2014, 32(6):564.,2014. |
| [4] | Yu H, Chen S N, Yang W, Zhang Y L, Chen S H. Effects of rare element and pressure on the microstructure and mechanical property of AZ91D alloy. J. Alloys Compd., 2014, 589:479.,2014. |
| [5] | Zhao M Y, Zhou Z J, Ding Q M, Zhong M, Arshad K. Ef-fect of rare earth elements on the consolidation behavior and microstructure of tungsten alloys. Int. J. Refract. Met. Hard. Mater., 2015, 48:19.,2015. |
| [6] | Aguirre-Dela Torre E, Pérez-Bustamante R, Camarillo-Cisneros J, Gómez-Esparza C D, Medrano-Prieto H M, Martínez-Sánchez R. Mechanical properties of the A356 aluminum alloy modified with La/Ce. J. Rare Earths, 2013, 31(8):811.,2013. |
| [7] | Zhu G, Liu Y, Ye J W. Influence of Ce-Co pre-alloyed powder addition on the microstructure and mechanical properties of Ti(C,N)-based cermets. Int. J. Refract. Met. Hard. Mater., 2013, 37:134.,2013. |
| [8] | 沈德久,马豪杰,郭长虹,蔡景瑞,李国龙,何东磊,杨庆祥.Effect of cerium and lanthanum additives on plasma electrolytic oxidation of AZ31 magnesium alloy[J].稀土学报（英文版）,2013(12):1208-1213. |
| [9] | 姜华伟,李捷,耿浩然,王庆磊.Influence of cooling rate and addition of lanthanum and cerium on formation of nanoporous copper by chemical dealloying of Cu15Al85 alloy[J].稀土学报（英文版）,2013(11):1119-1124. |
| [10] | Ahmad M, Ahmed E, Zafar F, Khalid N R, Niaz N A, Hafeez A, Ikram M, Khan M A, Hong Z L. Enhanced photocata-lytic activity of Ce-doped ZnO nanopowders synthesized by combustion method. J. Rare Earths, 2015, 33(3):255.,2015. |
| [11] | Han Y, Fan J L, Liu T, Cheng H C, Tian J M. The effect of trace nickel additive and ball milling treatment on the near-full densification behavior of ultrafine tungsten pow-der. Int. J. Refract. Met. Hard. Mater., 2012, 34:18.,2012. |
| [12] | Battabyal M, Schaublin R, Spatig P, Baluc N. W-2 wt.%Y2O3 composite:Microstructure and mechanical proper-ties. Mater. Sci. Eng., A, 2012, 538:53.,2012. |
| [13] | Lin N, He Y H, Wu C H, Jiang Y. Influence of copper content on the microstructure and hardness of copper-doped tungsten carbide-cobalt bulk at the elevated tem-perature. Int. J. Refract. Met. Hard. Mater., 2013, 38:140.,2013. |
| [14] | Wang J S, Wang X, Liu W, Gao T, Wang Y M. A study of Eu2O3, Sc2O3 co-doped tungsten matrix impregnated cathode. J. Phys. Chem. Solids, 2011, 72:1128.,2011. |
| [15] | Pang C S, Luo J, Guo Z M, Guo M, Hou T. Inhibition of tungsten particle growth during reduction of V-doped WO3 nanoparticles prepared by co-precipitation method. Int. J. Refract. Met. Hard. Mater., 2010, 28:343.,2010. |
| [16] | Venables D S, Brown M E. Reduction of tungsten oxides with hydrogen and with hydrogen and carbon. Thermo-chim. Acta, 1996, 285:361.,1996. |
| [17] | 卢平,沈春英,丘泰.溶胶-凝胶法制备稀土CeO2掺杂纳米钨粉的研究[J].粉末冶金技术,2008(06):455-458. |
| [18] | Lu P, Shen C Y, Qiu T. Preparation of sub-micro tungsten powder doped with CeO2. Powder Metallurgy Industry, 2008, 18(2):455.,2008. |
| [19] | Schubert W D, Lassner E. Tungsten blue oxide. Int. J. Re-fract. Met. Hard. Mater., 1995, 13(1-3):111.,1995. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%