Trivalent samarium doped barium molybdate (BaMoO4:Sm3+) red phosphor was successfully synthesized by hydrothermal method. The crystal structure, morphology and photoluminescent property were characterized by X-ray diffraction, field environ-mental scanning electron microscopy and photoluminescence spectroscopy. The results indicated that the synthesized BaMoO4:Sm3+ phosphor consisted of a pure phase with an octahedral structure. The main excitation peaks were located at 362, 404, 445 and 477 nm, respectively, and were obviously observed. The main emission peaks were located at 533, 566, 602 and 646 nm, respectively. The phosphors exhibited a red performance at 646 nm, which was appropriate for the ultraviolet-light emitting diode (UV-LED) and blue LED. The luminescent intensity of BaMoO4:Sm3+ increased with an increase in the doping amount of Sm3+. The luminescent intensity had the optimal value forx=0.03. When the doping amount of Sm3+ was further increased, the concentration quenching phenomenon was observed. Monovalent lithium (Li+) cation was used as a charge compensator. The luminescence intensity first increased with in-creasing Li+ doping concentration, and then decreased. The optimal content of Li+ was about 2%. The BaMoO4:Sm3+ phosphor pre-pared in this study could act as superior red phosphor for white LEDs.
参考文献
| [1] | ZHANG Yanfang;LI Lan;ZHANG Xiaosong;XI Qun.Temperature effects on photoluminescence of YAG:Ce3+ phosphor and performance in white light-emitting diodes[J].稀土学报（英文版）,2008(03):446-449. |
| [2] | Cavalli E.;Bovero E.;Belletti A..Optical spectroscopy of CaMoO4 : Dy3+ single crystals[J].Journal of Physics. Condensed Matter,200220(20):5221-5228. |
| [3] | Zhiguo Xia;Daimei Chen.Synthesis and Luminescence Properties of BaMoO_4:Sm~(3+) Phosphors[J].Journal of the American Ceramic Society,20105(5):1397-1401. |
| [4] | LI Zhao;ZHAO Xicheng;JIANG Yuanru.Hydrothermal preparation and photoluminescent property of LiY(MoO4)2:Pr3+red phosphors for white light-emitting diodes[J].稀土学报（英文版）,2015(1):33-36. |
| [5] | Qiang Gong;Xuefeng Qian;Hongliang Cao.Novel Shape Evolution of BaMoO_4 Microcrystals[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,200639(39):19295-19299. |
| [6] | Jamalaiah BC;Kumar JS;Babu AM;Suhasini T;Moorthy LR.Photoluminescence properties of Sm3+ in LBTAF glasses[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,20094(4):363-369. |
| [7] | B. Vengala Rao;U. Rambabu;S. Buddhudu.Emission analysis of Sm~(3+) :Ca_4GdO(BO_3)_3 powder phosphor[J].Materials Letters,200714/15(14/15):2868-2871. |
| [8] | 董国义;侯春彩;杨志平;刘鹏飞;董宏岩;梁小双.新型红色荧光粉Ca0.5Sr0.5MoO4∶Sm3+的制备及光学性能[J].光电子·激光,2014(1):89-95. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%