Biomimetic nano CeO2 materials were prepared by using bean sprouts as bio-template through impregnation and thermal decomposition. For characterization of structure, X-ray diffraction spectroscopy (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), UV-Vis diffuse reflectance spectra (UV-Vis/DRS) nitrogen adsorp-tion-desorption measurements and Labsolar H2 system were adopted. The results demonstrated that the samples prepared at 550 oC not only completely removed the original bio-template, but also retained the morphology and microstructure of bean sprouts. Then the biomorphic structure of fluorite structure CeO2 material was obtained. Micro-pores with a diameter of about 2–3 nm were distributed among the particles, which provided more favorable channel for the photocatalytic reaction. Biomimetic CeO2 materials exhibited clear red shift (50 nm) compared with powder CeO2, which could be excited by visible irradiation. Biomimetic CeO2 materials dis-played the superior photocatalytic activity for the hydrogen production by water splitting under the sunlight irradiation, the hydrogen yield could reach 400μmol/g catalyst after 6 h.
参考文献
| [1] | Xinchao Ruan;Heng Zhong;Wenbiao Cao.Photocatalytic degradation of organic pollutants by simple cerium(III) salt[J].Catalysis Communications,2013:76-79. |
| [2] | Avelino Corma;Pedro Atienzar;Hermenegildo Garcia;Jean-Yves Chane-Ching.Hierarchically mesostructured doped CeO2 with potential for solar-cell use[J].Nature materials,20046(6):394-397. |
| [3] | Masui, Toshiyuki;Nagai, Ryosuke;Imanaka, Nobuhito.Effect of the introduction of oxide ion vacancies into cubic fluorite-type rare earth oxides on the NO decomposition catalysis[J].Journal of Solid State Chemistry,2014:181-184. |
| [4] | Xiucheng Zheng;Xiaoli Zhang;Zheyu Fang.Characterization and catalysis studies of CuO/CeO_2 model catalysts[J].Catalysis Communications,20069(9):701-704. |
| [5] | Jemec, Anita;Djinovic, Petar;Crnivec, Ilja Gasan Osojnik;Pintar, Albin.The hazard assessment of nanostructured CeO2-based mixed oxides on the zebrafish Danio rerio under environmentally relevant UV-A exposure[J].Science of the Total Environment,2015:272-278. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%