利用 XRD、OM、SEM、TEM 测试技术和室温拉伸试验研究均匀化热处理对 Mg?7Gd?3Y?1Nd?1Zn?0.5Zr(质量分数，%)合金显微组织及力学性能的影响。结果发现，铸态组织主要由α-Mg、(Mg, Zn)3RE相和堆垛层错组成，热处理使(Mg, Zn)3RE部分回溶、晶界附近的堆垛层错消失，但沿着晶界产生了块状14H型长周期堆垛有序(LPSO)相。铸态合金的抗拉强度、屈服强度和伸长率分别为187 MPa、143 MPa和3.1%；而经均匀化热处理后合金的抗拉强度、屈服强度和伸长率分别为229 MPa、132 MPa和7.2%。
X-ray diffraction (XRD), optical microscopy (OM), scanning electronic microscopy (SEM), transmission electron microscopy (TEM) and tensile tests at room temperature (RT) were performed to investigate the effect of homogenization on microstructure evolution and mechanical properties of Mg?7Gd?3Y?1Nd?1Zn?0.5Zr (mass fraction,%) alloy. The results indicate that the microstructure of the as-cast alloy is composed of α-Mg, (Mg, Zn)3RE phase and stacking fault (SF), the homogenization results in the disappearance of (Mg, Zn)3RE phase and stacking fault (SF) as well as the emergence of 14H-type long-period stacking ordered (LPSO) phase. The ultimate tensile strength (UTS), yield strength (YS) and elongation of the as-cast alloy are 187 MPa, 143 MPa and 3.1%, and the UTS, YS and elongation of the as-homogenized alloy are 229 MPa, 132 MPa and 7.2%, respectively.
参考文献
| [1] | 唐平英;吴萌萌;唐壁玉;王继伟;彭立明;丁文江.Mg97Y2Zn1合金中18R型长周期有序相的微观结构[J].中国有色金属学报（英文版）,2011(4):801-806. |
| [2] | 曹丽杰;吴玉娟;彭立明;王渠东;丁文江.具有长周期结构的Mg-Gd-Zn-Zr合金的微结构和摩擦学行为[J].中国有色金属学报（英文版）,2014(12):3785-3791. |
| [3] | H. Yan;R.S. Chen;E.H. Han.Room-temperature ductility and anisotropy of two rolled Mg–Zn–Gd alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201015(15):3317-3322. |
| [4] | Nayyeri, G.;Mahmudi, R.;Salehi, F..The microstructure, creep resistance, and high-temperature mechanical properties of Mg-5Sn alloy with Ca and Sb additions, and aging treatment[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201021/22(21/22):5353-5359. |
| [5] | G. Nayyeri;R. Mahmudi.The microstructure and impression creep behavior of cast, Mg–5Sn–xCa alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20107/8(7/8):2087-2098. |
| [6] | Zhikun Qu;Xuhe Liu;Ruizhi Wu;Milin Zhang.The superplastic property of the as-extruded Mg–8Li alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201013/14(13/14):3284-3287. |
| [7] | Qiuming Peng;Jianli Wang;Yaoming Wu.The effect of La or Ce on ageing response and mechanical properties of cast Mg-Gd-Zr alloys[J].Materials Characterization,20084(4):435-439. |
| [8] | Xu, L.;Liu, C.;Wan, Y.;Wang, X.;Xiao, H..Effects of heat treatments on microstructures and mechanical properties of Mg-4Y-2.5Nd-0.7Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:1-6. |
| [9] | D.D. Yin;Q.D. Wang;Y. Gao.Effects of heat treatments on microstructure and mechanical properties of Mg-11Y-5Gd-2Zn-0.5Zr (wt.%) alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20115(5):1696-1704. |
| [10] | Zhang, J.;Chen, C.;Que, Z.;Cheng, W.;Xu, J.;Kang, J..18R and 14H long-period stacking ordered structures in the Mg _(93.96)Zn _2Y _4Sr _(0.04) alloy and the modification effect of Sr on X-phase[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:81-88. |
| [11] | T. Itoi;T. Seimiya;Y. Kawamura;M. Hirohashi.Long period stacking structures observed in Mg_(97)Zn_1Y_2 alloy[J].Scripta materialia,20042(2):107-111. |
| [12] | Shintaro Yoshimoto;Michiaki Yamasaki;Yoshihito Kawamura.Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloys with 14H Long Period Ordered Structure[J].Materials transactions,20064(4):959-965. |
| [13] | Rui Zhen;Yangshan Sun;Feng Xue.Effect of heat treatment on the microstructures and mechanical properties of the extruded Mg-11Gd-lZn alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2013:273-278. |
| [14] | Michiaki Yamasaki;Minami Sasaki;Masahiko Nishijima.Formation of 14H long period stacking ordered structure and profuse stacking faults in Mg-Zn-Gd alloys during isothermal aging at high temperature[J].Acta materialia,200720(20):6798-6805. |
| [15] | Xu, C.;Zheng, M.Y.;Wu, K.;Wang, E.D.;Fan, G.H.;Xu, S.W.;Kamado, S.;Liu, X.D.;Wang, G.J.;Lv, X.Y..Effect of cooling rate on the microstructure evolution and mechanical properties of homogenized Mg-Gd-Y-Zn-Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2013:364-370. |
| [16] | Zhang, X.;Meng, L.;Fang, C.;Peng, P.;Ja, F.;Hao, H..Effect of Nd on the microstructure and mechanical properties of Mg-8Gd-5Y-2Zn-0.5Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2013:19-24. |
| [17] | Zhi Cheng Li;Hong Zhang;Lu Liu;Yong Bo Xu.Growth and morphology of β phase in an Mg-Y-Nd alloy[J].Materials Letters,200424(24):3021-3024. |
| [18] | J. F. Nie and B. C. Muddle.CHARACTERISATION OF STRENGTHENING PRECIPITATE PHASES IN A Mg-Y-Nd ALLOY[J].Acta materialia,20008(8):1691-1703. |
| [19] | Mayumi Suzuki;Tsuyoshi Kimura;Junichi Koike.Effects of zinc on creep strength and deformation substructures in Mg-Y alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20040(0):706-709. |
| [20] | D. Egusa;E. Abe.The structure of long period stacking/order Mg-Zn-RE phases with extended non-stoichiometry ranges[J].Acta materialia,20121(1):166-178. |
| [21] | Zhe Leng;Jinghuai Zhang;Tianlong Zhu;Ruizhi Wu;Milin Zhang;Shujuan Liu;Jianfeng Sun;Li Zhang.Microstructure and mechanical properties of Mg-(6,9)RY-4Zn alloys by extrusion and aging[J].Materials & design,2013Dec.(Dec.):713-719. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%