(NH4)2SiF6预处理可对SBA-15介孔材料的表面缺陷进行补硅修正以及表面疏水化,从而明显改善SBA-15材料的水热稳定性.结果表明,用摩尔分数为5％的(NH4)2SiF6水溶液,按引入1％的SiO2计量对SBA-15进行处理后,其水热稳定性明显改善,在100℃沸水中处理14d,或在800℃下用100％水蒸气处理12h后,均保持较好的介观有序度、形貌及六方孔道结构,比表面积分别高达310和213 m2/g,但(NH4)2SiF6处理量过高,SBA-15水热稳定性反而下降.
参考文献
| [1] | Beck J S;Vartuli J C;Roth W J;Leonowicz M E Kresge C T Schmitt K D Chu C T W Olson D H Sheppard E W McCullen S B Higgins J B Schlenker J L .[J].Journal of the American Chemical Society,1992,114:10834. |
| [2] | Kresge C T;Leonowicz M E;Roth W J;Vartuli J C Beck J S .[J].Nature,1992,359:710. |
| [3] | Zhao DY.;Feng JL.;Chmelka BF.;Stucky GD.;Huo QS. .Nonionic triblock and star diblock copolymer and oligomeric surfactant syntheses of highly ordered, hydrothermally stable, mesoporous silica structures[J].Journal of the American Chemical Society,1998(24):6024-6036. |
| [4] | Zhao D Y;Feng J L;Huo Q S;Melosh N Fredrickson G H Chmelka B F Stucky G D .[J].Science,1998,279:548. |
| [5] | Bagshaw SA;Prouzet E;Pinnavaia TJ .TEMPLATING OF MESOPOROUS MOLECULAR SIEVES BY NONIONIC POLYETHYLENE OXIDE SURFACTANTS[J].Science,1995(5228):1242-1244. |
| [6] | Liu X Y;Tian B Z;Yu C Z;Gao F,Xie S H,Tu B,Che R C,Peng L M,Zhao D Y .[J].Angewandte Chemie International Edition,2002,41:3876. |
| [7] | Yu C Z;Tian B Z;Fan B;Stucky G D,Zhao D Y.[J].Chemical Communications,2001:2726. |
| [8] | Tanev P T;Chibwe M;Pinnavaia T J .[J].Nature,1994,368:321. |
| [9] | Tanev PT;Pinnavaia TJ .A NEUTRAL TEMPLATING ROUTE TO MESOPOROUS MOLECULAR SIEVES[J].Science,1995(5199):865-867. |
| [10] | 张微,徐恒泳,毕亚东,李文钊.介孔分子筛SBA-15的改性研究进展[J].化工进展,2007(02):152-157. |
| [11] | Ryoo R;Jun S .[J].Journal of Physical Chemistry B,1997,101:317. |
| [12] | Galarneau A;Nader M;Guenneau F;Renzo F D Gedeon A .[J].Journal of Physical Chemistry C,2007,111:8268. |
| [13] | Zhang F Q;Yan Y;Yang H F;Meng Y Yu C Z Tu B Zhao D Y .[J].Journal of Physical Chemistry B,2005,109:8723. |
| [14] | Han Y;Li N;Zhao L;Li D F Xu X Z Wu S Di Y Li C J Zou Y C Yu Y Xiao F S .[J].Journal of Physical Chemistry B,2003,107:7551. |
| [15] | Lai X Y;Tu J C;Wang H;Du J Yang M Mao D Xing C J Wang D Li X T .[J].Chemical Research in Chinese Universities,2009,25:773. |
| [16] | On D T;Kaliaguine S .[J].Journal of the American Chemical Society,2003,125:618. |
| [17] | Chen G D;Wang L Z;Lei J Y;Zhang J L .[J].Microporous and Mesoporous Materials,2009,124:204. |
| [18] | Li CL;Wang YQ;Guo YL;Liu XH;Guo Y;Zhang ZG;Wang YS;Lu GZ .Synthesis of highly ordered, extremely hydrothermal stable SBA-15/Al-SBA-15 under the assistance of sodium chloride[J].Chemistry of Materials: A Publication of the American Chemistry Society,2007(26):173-178. |
| [19] | 于善青,赵瑞玉,刘晨光.强酸性介质中用三嵌段共聚物模板合成介孔硅基分子筛Ⅰ.样品的表征及共溶剂、共表面活性剂对样品颗粒外貌的影响[J].石油学报(石油加工),2004(04):79-83. |
| [20] | Selvaraj M;Park D W;Ha C S .[J].Microporous and Mesoporous Materials,2011,138:94. |
| [21] | Du Y C;Liu S;Zhang Y L;Nawaz F Ji Y Y Xiao F S .[J].Microporous and Mesoporous Materials,2009,121:185. |
| [22] | Du Y C;Lan X J;Liu S;Ji Y Y Zhang Y L Zhang W P Xiao F S .[J].Microporous and Mesoporous Materials,2008,112:225. |
| [23] | Selvaraj M;Kawi S .An optimal direct synthesis of CrSBA-15 mesoporous materials with enhanced hydrothermal stability[J].Chemistry of Materials: A Publication of the American Chemistry Society,2007(3):509-519. |
| [24] | Yang, DJ;Xu, Y;Wu, D;Sun, Y .One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity[J].Journal of Solid State Chemistry,2008(9):2401-2405. |
| [25] | Ye F;Dong Z W;Zhang H J .[J].Materials Letters,2010,64:1441. |
| [26] | Song K;Guan J Q;Wang Z Q;Xu C Kan Q B .[J].Applied Surface Science,2009,255:5843. |
| [27] | Sun, H.;Tang, Q.;Du, Y.;Liu, X.;Chen, Y.;Yang, Y. .Mesostructured SBA-16 with excellent hydrothermal, thermal and mechanical stabilities: Modified synthesis and its catalytic application[J].Journal of Colloid and Interface Science,2009(1):317-323. |
| [28] | Wei J W;Shi J J;Pan H;Su Q F Zhu J B Shi Y .[J].Microporous and Mesoporous Materials,2009,117:596. |
| [29] | Xia Q H;Hidajat K;Kawi S .[J].Materials Letters,2000,42:102. |
| [30] | Jiang T L;Tao H X;Ren J W;Liu X H Wang Y Q Lu G Z .[J].Microporous and Mesoporous Materials,2011,142:341. |
| [31] | Chen G D;Wang L Z;Lei J Y;Zhang J L .[J].Microporous and Mesoporous Materials,2009,124:204. |
| [32] | Xu M;Wang W;Seiler M;Buchholz A Hunger M .[J].Journal of Physical Chemistry B,2002,106:3202. |
| [33] | Chen J H;Li Q H;Xu R R;Xiao F S .[J].Angewandte Chemie International Edition,1995,34:2694. |
| [34] | Sindorf D W;Maciel G E .[J].Journal of Physical Chemistry,1982,86:5208. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%