通过反相微乳液法制备了以Fe3O4为核,磺酸官能化的硅基材料为壳层的磁性酸性催化剂.首先制备纳米Fe3O4磁核,然后涂层包覆苯基修饰的纳米级硅层,最后进行苯基磺化修饰,制得固体酸催化剂Fe3O4@Si/Ph-SO3H.在果糖脱水制备5-羟甲基糠醛反应中,该催化剂表现出较好的催化活性,优于传统催化剂A-15,且与均相无机酸催化活性相当.当采用二甲基亚砜作溶剂,在110 oC下反应3 h,果糖转化率达到99%,5-羟甲基糠醛收率为82%.另外,该催化剂经磁法回收后可多次重复使用.
A magnetically recyclable acid catalyst composed of an Fe3O4 core and sulfonic acid functionalized silica shell has been prepared using the reverse microemulsion method. The Fe3O4 core was coated with a phenyl modified silica shell nanolayer, and the phenyl groups were subsequently sulfonated to generate a solid sulfonic acid catalyst. The resulting acid catalyst showed higher activity than the conventional A-15 catalyst and comparable activity to several homogeneous sulfonic acid catalysts for the dehydration of fructose to 5-hydroxymethylfurfural (HMF). This process gave a fructose conversion of 99%with an HMF yield of 82%following 3 h in dimethylsulfoxide at 110 °C. Fur-thermore, the catalyst could be magnetically separated and recycled several times without losing its activity.
参考文献
| [1] | Shi S;Guo H J;Yin G C .[J].CATALYSIS COMMUNICATIONS,2011,12:731. |
| [2] | Jia X Q;Ma J P;Che P H;Lu F Miao H Gao J Xu J .[J].J Energy Chem,2013,22:93. |
| [3] | Tong X L;Ma Y;Li Y D .[J].Carbohydrate Research,2010,345:1698. |
| [4] | Kim Y H;Shin S;Yoon H J;Kim J W Cho J K Lee Y S .[J].CATALYSIS COMMUNICATIONS,2013,40:18. |
| [5] | Li, Y.;Liu, H.;Song, C.;Gu, X.;Li, H.;Zhu, W.;Yin, S.;Han, C..The dehydration of fructose to 5-hydroxymethylfurfural efficiently catalyzed by acidic ion-exchange resin in ionic liquid[J].Bioresource Technology: Biomass, Bioenergy, Biowastes, Conversion Technologies, Biotransformations, Production Technologies,2013:347-353. |
| [6] | Wang F F;Wu H Z;Liu C L;Yang R Z Dong W S .[J].Carbohydrate Research,2013,368:78. |
| [7] | 马继平,于维强,王敏,贾秀全,路芳,徐杰.催化选择转化多羟基化合物制备高附加值化学品研究进展[J].催化学报,2013(03):492-507. |
| [8] | Wang L;Zhang J;Zhu L F;Meng X J Xiao F S .[J].J Energy Chem,2013,22:241. |
| [9] | Villa A;Schiavoni M;Fulvio P F;Mahurin S M Dai S Mayes R T Veith G M Prati L .[J].J Energy Chem,2013,22:305. |
| [10] | Binder, JB;Raines, RT .Simple Chemical Transformation of Lignocellulosic Biomass into Furans for Fuels and Chemicals[J].Journal of the American Chemical Society,2009(5):1979-1985. |
| [11] | Sievers C;Musin I;Marzialetti T;Valenzuela Olarte M B Agrawal P K Jones C W .[J].ChemSusChem,2009,2:665. |
| [12] | Asghari F S;Yoshida H .[J].Industrial and Engineering Chemistry Research,2006,45:2163. |
| [13] | Yang Y;Hu C W;Abu-Omar M M .[J].Green Chemistry,2012,14:509. |
| [14] | Deng T S;Cui X J;Qi Y Q;Wang Y X Hou X L Zhu Y L .[J].Chemistry Communications,2012,48:5494. |
| [15] | Ren Q H;Huang Y Z;Ma H;Wang F Gao J Xu J .[J].Bioresources,2013,8:1563. |
| [16] | Li C Z;Zhao Z K;Cai H L;Wang A Q Zhang T .[J].Biomass and Bioenergy,2011,35:2013. |
| [17] | Ordomsky, V.V.;Sushkevich, V.L.;Schouten, J.C.;Van Der Schaaf, J.;Nijhuis, T.A..Glucose dehydration to 5-hydroxymethylfurfural over phosphate catalysts[J].Journal of Catalysis,2013:37-46. |
| [18] | O'Neill R;Ahmad M N;Vanoye L;Aiouache F .[J].Industrial and Engineering Chemistry Research,2009,48:4300. |
| [19] | Yan H P;Yang Y;Tong D M;Xiang X Hu C W .[J].CATALYSIS COMMUNICATIONS,2009,10:1558. |
| [20] | Qi X H;Watanabe M;Aida T M;Smith R L Jr .[J].Green Chemistry,2009,11:1327. |
| [21] | Guo X C;Cao Q;Jiang Y J;Guan J Wang X Y Mu X D .[J].Carbohydrate Research,2012,351:35. |
| [22] | Qi X H;Guo H X;Li L Y;Smith R L Jr .[J].ChemSusChem,2012,5:2215. |
| [23] | Ordomsky V V;Schouten J C;van der Schaaf J;Nijhuis T A .[J].CHEMICAL ENGINEERING JOURNAL,2012,207-208:218. |
| [24] | Narita, A;Naka, K;Chujo, Y .Facile control of silica shell layer thickness on hydrophilic iron oxide nanoparticles via reverse micelle method[J].Colloids and Surfaces. A, Physicochemical and Engineering Aspects,2009(1/3):46-56. |
| [25] | Maity D;Agrawal D C .[J].Journal of Magnetism and Magnetic Materials,2007,308:46. |
| [26] | Sun YB;Ding XB;Zheng ZH;Cheng X;Hu XH;Peng YX .Surface initiated ATRP in the synthesis of iron oxide/polystyrene core/shell nanoparticles[J].European Polymer Journal,2007(3):762-772. |
| [27] | Singh N;Kumar R;Sachan P K .[J].CHEMICAL ENGINEERING,2013,2013:1. |
| [28] | Wang M;Chen C;Ma J P;Xu J .[J].Journal of Materials Chemistry,2011,21:6962. |
| [29] | Cannas C;Musinu A;Ardu A;Orru?F Peddis D Casu M Sanna R Angius F Diaz G Piccaluga G .[J].CHEMISTRY OF MATERIALS,2010,22:3353. |
| [30] | Chen C;Zhang Q H;Gao J;Zhang W Xu J .[J].JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY,2009,9:1589. |
| [31] | Zhang X C;Zhang Z;Wang F;Wang Y H Song Q Xu J .[J].Journal of Molecular Catalysis A:Chemical,2013,377:102. |
| [32] | Huang Z;Pan W Y;Zhou H B;Qin F Xu H L Shen W .[J].ChemSusChem,2013,6:1063. |
| [33] | Zhang J;Weitz E .[J].ACS Catal,2012,2:1211. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%