通过氢气还原改性和浓硝酸氧化处理对石油焦基活性炭(ACs)进行改性.采用氮气吸附和脱附等温线计算改性ACs的BET比表面积、 DFT孔径分布及孔容,以XPS方法表征改性ACs的表面含氧官能团种类及含量,改性ACs的电化学性能通过直流循环充放电、循环伏安等表征.结果表明:浓硝酸处理后,ACs比表面积和孔容均稍有减少,表面含氧官能团和比电容明显增加,内阻和自放电显著增大;氢气改性后,ACs比表面积和孔容亦稍有减少,孔径分布的变化使比电容明显增加,氧化官能团的减少降低了内阻并减少了自放电.即,氢气改性ACs的电化学性能明显提高,增加了比电容,降低了内阻和自放电.
Petroleum coke-based activated carbons(ACs)were modified through H2 reduction and HNO3 oxidation. Pore structures and surface chemistry of the ACs were characterized by N2 adsorption and X-ray photoelectron spectroscopy. The Brunauer-Emmett-Teller surface areas of ACs were slightly decreased after such treatment. Although surface oxygen groups(especially carbonyl groups)were generated when ACs were treated by HNO3, electric double layer capacitance, internal resistance(IR), equivalent series resistance(ESR), and self-discharge of an AC electrode exhibited a remarkable increase. At the same time, the number of surface oxygen groups of ACs modified by H2 remarkably decreased and the capacitance was markedly increased , while IR, ESR, and self-discharge decreased. This reduction modification of ACs is beneficial in improving electrochemical properties and probably provides suitable pores for electrolyte to penetrate electrochemically.
参考文献
| [1] | Conway B E.Electrochemical Supercapacitors:Scientific Fundamentals and Technological Applications[M].New York:Kluwer Academic Publisher/Prenum Press,1999 |
| [2] | Keiichi Okajima;Keigo Ohta;Masao Sudoh .Capacitance behavior of activated carbon fibers with oxygen-plasma treatment[J].Electrochimica Acta,2005(11):2227-2231. |
| [3] | E. Raymundo-Pinero;K. Kierzek;J. Machnikowski .Relationship between the nanoporous texture of activated carbons and their capacitance properties in different electrolytes[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(12):2498-2507. |
| [4] | K. Kierzek;E. Frackowiak;G. Lota;G. Gryglewicz;J. Machnikowski .Electrochemical capacitors based on highly porous carbons prepared by KOH activation[J].Electrochimica Acta,2004(4):515-523. |
| [5] | D. Lozano-Castello;D. Cazorla-Amoros;A. Linares-Solano .Influence of pore structure and surface chemistry on electric double layer capacitance in non-aqueous electrolyte[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(9):1765-1775. |
| [6] | M. J. Bleda-Martinez;J. A. Macia-Agullo;D. Lozano-Castello .Role of surface chemistry on electric double layer capacitance of carbon materials[J].Carbon: An International Journal Sponsored by the American Carbon Society,2005(13):2677-2684. |
| [7] | M.J. Bleda-Martinez;D. Lozano-Castello;E. Moralion .Chemical and electrochemical characterization of porous carbon materials[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(13):2642-2651. |
| [8] | Kinoshita K.Carbon:Electrochemical and Physicochemical Properties[M].New York:John Wiley﹠Sons,1988:293-387. |
| [9] | Leon y Leon C A;Radovic L R.Interfacial chemistry and electrochemistry of carbon surfaces[A].New York:Dekker,1994:213-310. |
| [10] | Biniak S;Swiatkowski A;Pakula M.Electrochemical studies of phenomena at active carbon-electrolyte solution interfaces[A].New York:Dekker,2001:125-225. |
| [11] | H. Yang;M. Yoshio;K. Isono .Improvement of Commercial Activated Carbon and Its Application in Electric Double Layer Capacitors[J].Electrochemical and solid-state letters,2002(6):A141-A144. |
| [12] | Toyoda M;Tani Y;Soneda Y .Exfoliated carbon fibers as an electrode for electric double layer capacitors in a 1 mol/dm(3) H2SO4 electrolyte[J].Carbon: An International Journal Sponsored by the American Carbon Society,2004(14):2833-2837. |
| [13] | Aik Chong Lua;Ting Yang .Effect of activation temperature on the textural and chemical properties of potassium hydroxide activated carbon prepared from pistachio-nut shell[J].Journal of Colloid and Interface Science,2004(2):594-601. |
| [14] | Gregg S J;Sing K S W.Adsorption,Surface Area and Porosity[M].New York:Academic Press,Inc,1982:85. |
| [15] | Takahagi T;Ishitani A .XPS studies by use of the digital difference spectrum technique of functional groups on the surface of carbon fiber[J].Carbon,1982,22(01):43-46. |
| [16] | Moreno-Castilla C.;Carrasco-Marin F.;Lopez-Ramon MV. .Changes in surface chemistry of activated carbons by wet oxidation[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(14):1995-2001. |
| [17] | H.P.Boehm .Surface oxides on carbon and their analysis: a critical assessment[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(2):145-149. |
| [18] | Yue ZR;Wang L;Gardner SD;Pittman CU;Jiang W .Surface characterization of electrochemically oxidized carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(11):1785-1796. |
| [19] | Desimoni E;Casella G I;Salvi A M .XPS/XAES study of carbon fibres during thermal annealing under UHV conditions[J].Carbon,1992,30(04):521-526. |
| [20] | Desimoni E;Casella G I;Salvi A M et al.XPS investigation of ultra-high-vacuum storage effects on carbon fibre surfaces[J].Carbon,1992,30(04):527-531. |
| [21] | Zielke U.;Hoffman WP.;Huttinger KJ. .SURFACE-OXIDIZED CARBON FIBERS .1. SURFACE STRUCTURE AND CHEMISTRY[J].Carbon: An International Journal Sponsored by the American Carbon Society,1996(8):983-998. |
| [22] | Grazyna Gryglewicz;Ewa Lorenc-Grabowska;Grzegorz Lota;Elzbieta Frackowiak .Effect of pore size distribution of coal-based activated carbons on double layer capacitance[J].Electrochimica Acta,2005(5):1197-1206. |
| [23] | Chmiola J;Yushin G;Dash R et al.Effect of pore size and surface area of carbide derived carbons on specific capacitance[J].Journal of Power Sources,2006,158(01):765-772. |
| [24] | Fang B;Wei Y-Z;Kumagai M .Modified carbon materials for high-rate EDLCs application[J].Journal of Power Sources,2006,155(02):487-491. |
| [25] | R. Koetz;M. Hahn;R. Gallay .Temperature behavior and impedance fundamentals of supercapacitors[J].Journal of Power Sources,2006(2):550-555. |
| [26] | Wu X;Chen R;Cao G; et al.Room temperature molten salt as electrolyte for carbon nanotube-based electric double layer capacitors[J].Journal of Power Sources,2006,158(01):773-778. |
| [27] | Haichao Liang;Fang Chen;Rengui Li;Lu Wang;Zhenghua Deng .Electrochemical study of activated carbon-semiconducting oxide composites as electrode materials of double-layer capacitors[J].Electrochimica Acta,2004(21):3463-3467. |
| [28] | Reddy R N;Reddy R G .Porous structured vanadium oxide electrode material for electrochemical capacitors[J].Journal of Power Sources,2006,156(02):700-704. |
| [29] | Pei-Zhe Cheng;Hsisheng Teng .Electrochemical responses from surface oxides present on HNO_3-treated carbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(11):2057-2063. |
| [30] | K. Jurewicz;K. Babel;R. Pietrzak .Capacitance properties of multi-walled carbon nanotubes modified by activation and ammoxidation[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(12):2368-2375. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%