以间苯二酚和甲醛为前驱体,分别采用赖氨酸或氨水共聚体系制备了两种具有分等级孔道结构的块体含氮多孔炭.采用氮气吸附/脱附,透射电子显微镜,扫描电子显微镜及元素分析技术分别对其物理和化学性质进行了表征.在三电极体系和两电极体系下,研究了其作为超级电容器电极材料的电化学行为.结果表明:这两种氮掺杂块体多孔炭具有相似的孔道结构,但电容行为明显不同.其中赖氨酸体系制备的多孔炭氮含量比较高,表现出良好的电化学行为,其质量比电容可达199F·g-1,经过1000充放电循环比电容仅有1.6%的损失.
Two nitrogen-doped carbon monoliths with hierarchical porosity over a large size range were prepared by polymerization of resorcinol and formaldehyde in the presence of an organic amine, L-lysine, and an inorganic base, ammonium hydroxide under ambient conditions. Their physical and chemical features were characterized by N2 sorption,transmission and scanning electron microscopy, and elemental analysis. Their electrochemical properties as the electrodes of supercapacitors were evaluated under both a three-electrode system and a two-electrode system. Results show that the two types of nitrogen-doped carbon possess similar pore structures, but have distinct electrochemical performances. The L-lysine incorporated carbon monolith has a high nitrogen content,a high spectific capacitance of 199F·g-1,and a 1.6% loss in the specific capacitance after 1000 charge-discharge cycles, indicating a long-term cycling stability.
参考文献
| [1] | PATRICE SIMON;YURY GOGOTSI .Materials for electrochemical capacitors[J].Nature materials,2008(11):845-854. |
| [2] | Conway B E.Electrochemical Supercapacitors:Scientific Fundamentals and Technological Applications[M].New York:Kluwer Academic Publishers,1999 |
| [3] | W. Xing;S.Z. Qiao;R.G. Ding .Superior electric double layer capacitors using ordered mesoporous carbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(2):216-224. |
| [4] | Nam Dong Kim;Wooyoung Kim;Ji Bong Joo;Seogil Oh;Pil Kim;Younghun Kim;Jongheop Yi .Electrochemical capacitor performance of N-doped mesoporous carbons prepared by ammoxidation[J].Journal of Power Sources,2008(1):671-675. |
| [5] | V.Ruiz;C.Blanco;R.Santamaria .An activated carbon monolith as an electrode material for supercapacitors[J].Carbon: An International Journal Sponsored by the American Carbon Society,2009(1):195-200. |
| [6] | Gamby J;Taberna P L;Simon P et al.Studies and characterisations of various activated carbons used for carbon/carbon supercapacitors[J].Journal of Power Sources,2001,101:109-116. |
| [7] | Yudong Zhu;Haoquan Hu;Wen-Cui Li .Cresol-formaldehyde based carbon aerogel as electrode material for electrochemical capacitor[J].Journal of Power Sources,2006(1):738-742. |
| [8] | Li WC.;Reichenauer G.;Fricke J. .Carbon aerogels derived from cresol-resorcinol-formaldehyde for supercapacitors[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(15):2955-2959. |
| [9] | Kaisheng Xia;Qiuming Gao;Jinhua Jiang .Hierarchical porous carbons with controlled micropores and mesopores for supercapacitor electrode materials[J].Carbon: An International Journal Sponsored by the American Carbon Society,2008(13):1718-1726. |
| [10] | Li J;Wang XY;Wang Y;Huang QH;Dai CL;Gamboa S;Sebastian PJ .Structure and electrochemical properties of carbon aerogels synthesized at ambient temperatures as supercapacitors[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2008(1):19-24. |
| [11] | W. Xing;C.C. Huang;S.P. Zhuo .Hierarchical porous carbons with high performance for supercapacitor electrodes[J].Carbon: An International Journal Sponsored by the American Carbon Society,2009(7):1715-1722. |
| [12] | Yu-Qian Dou;Yunpu Zhai;Haijing Liu;Yongyao Xia;Bo Tu;Dongyuan Zhao;Xiao-Xia Liu .Syntheses of polyaniline/ordered mesoporous carbon composites with interpenetrating framework and their electrochemical capacitive performance in alkaline solution[J].Journal of Power Sources,2011(3):1608-1614. |
| [13] | 王大伟,李峰,刘敏,成会明.硝酸氧化改性SBA-15 模板合成的中孔炭电容性能研究[J].新型炭材料,2007(04):307-314. |
| [14] | Chen Z;Qin Y;Weng D et al.Design and synthesis of hierarchical nanowire composites for electrochemical energy storage[J].Advanced Functional Materials,2009,19:3420-3426. |
| [15] | Huang C W;Wu Y T;Hu C C et al.Textural and electrochemical characterization of porous carbon nanofibers as electrodes for supercapacitors[J].Journal of Power Sources,2007,172:460-467. |
| [16] | Bao, L.;Zang, J.;Li, X. .Flexible Zn_2SnO_4/MnO_2 core/shell nanocable-carbon microfiber hybrid composites for high-performance supercapacitor electrodes[J].Nano letters,2011(3):1215-1220. |
| [17] | Chmiola J;Yushin G;Gogotsi Y;Portet C;Simon P;Taberna PL .Anomalous increase in carbon capacitance at pore sizes less than 1 nanometer[J].Science,2006(5794):1760-1763. |
| [18] | Elzbieta Frackowiak;Francois Beguin .Carbon materials for the electrochemical storage of energy in capacitors[J].Carbon: An International Journal Sponsored by the American Carbon Society,2001(6):937-950. |
| [19] | Lufrano F;Staiti P .Mesoporous carbon materials as electrodes for electrochemical supercapacitors[J].International Journal of Electrochemical Science,2010,5:903-916. |
| [20] | Denisa Hulicova;Masaya Kodama;Hiroaki Hatori .Electrochemical Performance of Nitrogen-Enriched Carbons in Aqueous and Non-Aqueous Supercapacitors[J].Chemistry of Materials: A Publication of the American Chemistry Society,2006(9):2318-2326. |
| [21] | E. Frackowiak;G. Lota;J. Machnikowski;C. Vix-Guterl;F. Beguin .Optimisation of supercapacitors using carbons with controlled nanotexture and nitrogen content[J].Electrochimica Acta,2006(11):2209-2214. |
| [22] | Denisa Hulicova-Jurcakova;Mykola Seredych;Gao Qing Lu;Teresa J. Bandosz .Combined Effect Of Nitrogen- And Oxygen-containing Functional Groups Of Microporous Activated Carbon On Its Electrochemical Performance In Supercapacitors[J].Advanced functional materials,2009(3):438-447. |
| [23] | Xiaoqing Yang;Dingcai Wu;Xiaomei Chen .Nitrogen-Enriched Nanocarbons with a 3-D Continuous Mesopore Structure from Polyacrylonitrile for Supercapacitor Application[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2010(18):8581-8586. |
| [24] | Stein A;Wang Z;Fierke M A .Functíonalization of porous carbon materials with designed pore architecture[J].Advanced Materials,2009,21:265-293. |
| [25] | Guang-Ping Hao;Wen-Cui Li;Dan Qian;An-Hui Lu .Rapid Synthesis of Nitrogen-Doped Porous Carbon Monolith for CO_2 Capture[J].Advanced Materials,2010(7):853-857. |
| [26] | Fan Z J;Yan J;Zhi L J et al.A three-dimensional carbon nanotube/graphene sandwich and its application as electrode in supercapacitors[J].Advanced Materials,2010,22:3723-3728. |
| [27] | Frackowiak E;Lota G;Machnikowski J et al.Optimisation of supercapacitors using carbons with controlled nanotexture and nitrogen content[J].Electrochimica Acta,2005,51:2209-2214. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%