采用天然气为前躯体在不同压力下使用化学气相渗积法制备炭/炭复合材料.利用甲烷分解热力学与沉积动力学研究了渗积压力对渗积速率和热解炭组织结构的影响.采用偏光显微镜观察热解炭的组织结构.结果表明:随着渗积压力的增加,初始渗积速率增大；但在渗积后期,渗积速率随着渗积压力的增大而降低,导致在高渗积压力下相同时间制备样品的最终密度降低.热解炭组织结构对渗积压力具有很强的依赖性.在低压(1 kPa)下渗积得到的热解炭基体全部为粗糙层结构.在适中的压力(3kPa,5 kPa,10 kPa)下,以炭纤维为圆心由内到外依次得到各向同性和粗糙层热解炭,整个基体以粗糙层为主.在15kPa下,得到的热解炭组织结构为各向同性和光滑层组织.
Carbon/carbon composites were fabricated by chemical vapor infiltration of needled carbon fiber felts (70％porosity) with natural gas as precursor at different infiltration pressures.The thermodynamics of methane pyrolysis and the densification kinetics were used to investigate the influence of infiltration pressure on the infiltration rate and the microstructure of pyrocarbon.The microstructure of pyrocarbon was examined by polarized light microscopy.Results showed that the initial infiltration rate increased with pressure,whereas it decreased with pressure during the later stages of infiltration,which led to a decrease in the final density of the samples.The pyrocarbon microstructure depended markedly on the infiltration pressure at the given deposition temperature.Rough laminar (RL) carbon is formed as the matrix at the lowest pressure (approximately 1kPa).At medium pressures (3,5,and 10kPa),isotropic (ISO) carbon is formed,followed by RL carbon,in the radial direction of the carbon fiber,with RL being the major matrix.Smooth laminar and ISO structures are the major phases at high pressures ( 15 kPa).
参考文献
| [1] | Latit M. Manocha .High performance carbon-carbon composites[J].Sadhana: Academy Proceedings in Engineering Science,2003(1/2):349-358. |
| [2] | Golecki I .Rapid vapor-phase densification of refractory composites[J].Material Science &Engineering A,1997,R20:37-124. |
| [3] | Buckley J D;Edie D D.Carbon/carbon materials and composites[M].New Jersey:Noyes Publications,1993:267-279. |
| [4] | T. L. DHAMI;O. P. BAHL;P. K. JAIN .CARBON-CARBON COMPOSITES MADE WITH OXIDISED PAN (PANEX) FIBERS[J].Carbon: An International Journal Sponsored by the American Carbon Society,1995(11):1517-1524. |
| [5] | Z.J.Hu;W.G.Zhang;K.J.Huttinger;B.Reznik;D.Gerthsen .Influence of pressure, temperature and surface area/volume ratio on the texture of pyrolytic carbon deposited from methane[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(4):749-758. |
| [6] | Brüggert M;Hu Z;Hüttinger K J .Chemistry and kinetics of chemical vapor deposition of pyrocarbon VI.Influence of temperature using methane as a carbon source[J].Carbon,1999,37:2021-2030. |
| [7] | T. CHEN;W. GONG;G. LIU .Influence of graphite foils on I-CVI densification rate and microstructure of obtained pyrolytic carbon of carbon-carbon composites[J].Composites, Part A. Applied science and manufacturing,2005(11):1494-1498. |
| [8] | Li AJ;Deutschmann O .Transient modeling of chemical vapor infiltration of methane using multi-step reaction and deposition models[J].Chemical Engineering Science,2007(18/20):4976-4982. |
| [9] | Yujie Hu;Ruiying Luo;Yunfeng Zhang;Jincao Zhang;Jinsong Li .Effect of preform density on densification rate and mechanical properties of carbon/carbon composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(3):797-801. |
| [10] | Koyo Norinaga;Olaf Deutschmann;Klaus J. Huttinger .Analysis of gas phase compounds in chemical vapor deposition of carbon from light hydrocarbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(9):1790-1800. |
| [11] | Xiaowen Wu;Ruiying Luo;Jincao Zhang .Deposition mechanism and microstructure of pyrocarbon prepared by chemical vapor infiltration with kerosene as precursor[J].Carbon: An International Journal Sponsored by the American Carbon Society,2009(6):1429-1435. |
| [12] | Jiping Wang;Junmin Qian;Zhihao Jin;Guanjun Qiao .Microstructure of C/C composites prepared by chemical vapor infiltration method with vaporized kerosene as a precursor[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):162-167. |
| [13] | Wu X W;Luo R Y;Zhang J C et al.Kinetics of thermal gradient chemical vapor infiltration of large-size carbon/carbon composites with vaporized kerosene[J].Materials Chemistry and Physics,2009,113(2-3):616-621. |
| [14] | Reznik B.;Huttinger KJ.;Gerthsen D. .Micro- and nanostructure of the carbon matrix of infiltrated carbon fiber felts[J].Carbon: An International Journal Sponsored by the American Carbon Society,2001(2):215-229. |
| [15] | Zhang WG.;Hu ZJ.;Huttinger KJ. .Chemical vapor infiltration of carbon fiber felt: optimization of densification and carbon microstructure[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(14):2529-2545. |
| [16] | Benzinger W.;Huttinger KJ. .Chemical vapor infiltration of pyrocarbon - II. The influence of increasing methane partial pressure at constant total pressure on infiltration rate and degree of pore filling[J].Carbon: An International Journal Sponsored by the American Carbon Society,1998(7/8):1033-1042. |
| [17] | Benzinger W.;Huttinger K.J. .Chemistry and kinetics of chemical vapor infiltration of pyrocarbon-IV. Investigation of methane/hydrogen mixtures[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(6):931-940. |
| [18] | Benzinger W.;Huttinger K.J. .Chemistry and kinetics of chemical vapor infiltration of pyrocarbon-VI. Mechanical and structural properties of infiltrated carbon fiber felt[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(8):1311-1322. |
| [19] | W.G. Zhang;K.J. Huttinger .Densification of a 2D carbon fiber preform by isothermal, isobaric CVI: Kinetics and carbon microstructure[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(12):2325-2337. |
| [20] | Lieberman M L;Pierson H L .Effect of gas phase conditions on resultant matrix pyroearbon[J].Carbon,1974,12:233-242. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%