以高能球磨法制备的MoSi2-CoNiCrAlY复合粉末为喂料,利用等离子喷涂技术在GH4169合金表面沉积了Mo-Si2-CoNiCrAlY涂层,采用X射线衍射仪、激光粒度分析仪和扫描电镜分析了粉末喂料及涂层的相组成和微观结构,并对涂层的显微硬度、抗热震性以及低温氧化行为进行了研究.结果表明:采用高能球磨法制备的粉末喂料是由细小纳米晶组成的多晶体,略为过筛后可直接用于热喷涂;制备的涂层组织致密,孔隙率低,且与基体形成了一定的冶金结合;其显微硬度服从威布尔分布,平均硬度值高达854.4HV0.1,热震失效寿命长达27次,500℃氧化120h后质量增加仅为0.083mg/cm2,且未发生MoSi2的“低温粉化”现象.
参考文献
| [1] | Federico Smeacetto;Monica Ferraris;Milena Salvo .Multilayer coating with self-sealing properties for carbon-carbon composites[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(11):2105-2111. |
| [2] | Yoon JK.;Kim GH.;Byun JY.;Lee JK.;Kim JS. .Formation of crack-free MoSi2/alpha-Si3N4 composite coating on Mo substrate by ammonia nitridation of Mo5Si3 layer followed by chemical vapor deposition of Si[J].Surface & Coatings Technology,2003(1):81-89. |
| [3] | 冯培忠,曲选辉,王晓虹.二硅化钼的制备与应用的新进展[J].粉末冶金工业,2005(04):46-51. |
| [4] | 赵猛,李争显,张欣,黄春良.MoSi2在高温抗氧化涂层中的应用[J].材料保护,2011(01):42-45. |
| [5] | CHOU T C;NIEH T G .Kinetics of MoSi2 pest during low temperature oxidation[J].Journal of Materials Research,1993,8(07):1606-1610. |
| [6] | 易德亮,冶银平,刘光,尹斌,周惠娣,陈建敏.等离子喷涂Al2O3-30％Ti02微米/纳米复合涂层的结构与耐磨性能[J].材料工程,2012(05):24-29. |
| [7] | WU Y S;QIU W Q;YU H Y et al.Cycle oxidation behavior of nanostructured Ni60-TiB2 composite coating spayed by HVOF technique[J].Applied Surface Science,2011,257(23):10224-10232. |
| [8] | Liu SL;Sun DB;Fan ZS;Yu HY;Meng HM .The influence of HVAF powder feedstock characteristics on the sliding wear behaviour of WC-NiCr coatings[J].Surface & Coatings Technology,2008(20):4893-4900. |
| [9] | 邹东利,阎殿然,何继宁.反应等离子喷涂TiN复相陶瓷涂层的研究[J].稀有金属材料与工程,2007(z3):225-229. |
| [10] | CHICOT D;HAGE I;DEMARECAUX P et al.Elastic properties determination from indentation tests[J].Surface and Coatings Technology,1996,81(2-3):269-274. |
| [11] | 李剑锋,丁传贤.等离子喷涂Cr3C2-NiCr涂层的Vickers硬度研究[J].硅酸盐学报,2000(03):223-228. |
| [12] | 马壮,曲文超,李智超.AZ91D热化学反应热喷涂陶瓷涂层热震性研究[J].表面技术,2008(02):52-53,78. |
| [13] | 吴姚莎 .超音速火焰喷涂纳米Ni60-TiB2复合涂层及其耐磨耐蚀性能研究[D].广州:华南理工大学,2011. |
| [14] | 毕恩兵,孙宏飞,王灿明,李冲,袁博,左俊文,文方贤.纳米陶瓷等离子喷涂层硬度的Weibull分布及与涂层组构的对应特性[J].材料保护,2012(05):24-27. |
| [15] | 李剑锋,黄静琪,季珩,丁传贤.等离子喷涂Cr2O3涂层显微硬度的工艺优化[J].硅酸盐学报,2001(01):49-53. |
| [16] | 赵宇.可靠性数据分析[M].北京:国防工业出版社,2011:95-100. |
| [17] | MILLER R A;LOWELL C E .Failure mechanisms of thermal barrier coatings exposed to elevated temperatures[J].Thin Solid Films,1982,95(03):265-273. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%