采用CMT4104电子万能拉伸试验机分别进行温度为870℃,应变速率为3.3×104s-1的恒应变速率和温度为850～890℃,应变速率为3.3×10-5～3.3×10-3 s-1的应变速率循环法超塑性拉伸实验.结果表明:在变形过程中存在动态回复与动态再结晶现象,并采用Avrami方程描述了动态再结晶动力学行为;基于应变速率循环法获得了TC4 DT合金的本构模型,再通过1stopt软件加以回归拟合,得到较为精确的TC4 DT合金超塑性变形本构方程.
参考文献
| [1] | 曹春晓.选材判据的变化与高损伤容限钛合金的发展[J].金属学报,2002(z1):4-11. |
| [2] | SINHA V;SOBOYEJOW W O .An investigation of the effects of colony microstructure on fatigue crack growth in Ti-6Al-4V[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2001,319-321:607-612. |
| [3] | 李辉,曲恒磊,赵永庆,曾卫东,冯亮,陈军.显微组织对Ti-6Al-4V ELI合金疲劳裂纹扩展速率的影响[J].稀有金属快报,2006(03):26-29. |
| [4] | SWIFT T .Damage tolerance capability[J].International Journal of Fatigue,1994,16(01):75-96. |
| [5] | Arrieta AJ;Striz AG .Optimal design of aircraft structures with damage tolerance requirements[J].Structural and multidisciplinary optimization,2005(2):155-163. |
| [6] | 陈学海,陈康华,董朋轩,彭国胜,陈送义.7085铝合金的热变形组织演变及动态再结晶模型[J].中国有色金属学报,2013(01):44-50. |
| [7] | YANGJ H;LIU Q Y;SUN D B et al.Recrystallization behavior of deformed austenite in high strength microalloyed pipeline steel[J].Journal of Iron and Steel Research International,2009,16(01):75-80. |
| [8] | 王智祥,刘雪峰,谢建新.AZ91镁合金高温变形本构关系[J].金属学报,2008(11):1378-1383. |
| [9] | 喻淼真,王高潮,郑漫庆,徐雪峰.TC4-DT合金应变诱发最大m值超塑性变形研究[J].航空材料学报,2014(03):15-20. |
| [10] | 喻淼真,王高潮,郑漫庆,王志录,徐雪峰.TC4-DT合金改锻工艺及超塑性变形行为[J].塑性工程学报,2013(05):1-6. |
| [11] | 张庭芳 .镁合金板料热拉深成形实验与数值模拟研究[D].南昌大学,2008. |
| [12] | 刘智恩.材料科学基础[M].西安:西北工业大学出版社,2008:273-274. |
| [13] | Yong-Cheng Lin;Ming-Song Chen .Numerical simulation and experimental verification of microstructure evolution in a three-dimensional hot upsetting process[J].Journal of Materials Processing Technology,2009(9):4578-4583. |
| [14] | 范定兵,王高潮,赵晓宾.Ti-15-3超塑性研究[J].南昌航空工业学院学报（自然科学版）,2007(01):26-29. |
| [15] | 耿启冬,王高潮,董洪波.TA15合金应变速率循环超塑性研究[J].热加工工艺,2008(11):43-45,48. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%