采用自制的CuMnNiCo钎料对氧化物弥散强化(ODS)合金MGH956进行钎焊实验,分析了钎焊过程中各种组织的形成过程,研究了不同的钎焊温度对接头组织和性能的影响.结果表明:在1000～1050℃保温20min工艺下钎焊MGH956合金,均可获得良好的钎焊成形效果,钎焊接头由钎缝中心区的Cu-Mn基固溶体和两侧扩散反应区的Fe-Mn基固溶体组成,并含有三种不同的化合物相.钎焊温度为1030℃和1050℃时,接头的室温拉伸断裂发生在钎缝中心处,断口主要呈沿晶脆性断裂特征.钎焊温度的提高使沿晶界分布的脆性(Mn,Ni)-Si相减少,有利于改善钎焊接头强度,钎焊接头的室温抗拉强度最高可达到母材强度的75％.
参考文献
| [1] | 淮军锋,郭万林,李天文,袁鸿,姜维.氧化物弥散强化高温合金MGH956的基本焊接性研究[J].材料工程,2008(09):52-55. |
| [2] | 张胜,侯金保,郭德伦,张蕾.MGH956合金TLP扩散连接接头组织分析[J].航空材料学报,2003(z1):104-108. |
| [3] | Zhang, C.H.;Kimura, A.;Kasada, R.;Jang, J.;Kishimoto, H.;Yang, Y.T. .Characterization of the oxide particles in Al-added high-Cr ODS ferritic steels[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2011(1/3):221-224. |
| [4] | 任家烈;吴爱萍.先进材料的连接[M].北京:机械工业出版社,2000:77-78. |
| [5] | 谢伟峰,雷玉成,任闻杰.等离子超声电弧焊接MGH956合金激励频率的计算机优化[J].航空材料学报,2013(01):38-44. |
| [6] | Khan TI.;Al-Badri A. .Reactive brazing of ceria to an ODS ferritic stainless steel[J].Journal of Materials Science,2003(11):2483-2488. |
| [7] | R.K. Saha;S. Wei;T.I. Khan .A comparison of microstructural developments in TLP diffusion bonds made using ODS Ni alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):319-327. |
| [8] | Noto, H.;Ukai, S.;Hayashi, S. .Transient liquid-phase bonding of ODS steels[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2011(1/3):249-252. |
| [9] | R.K. Roy;S. Singh;M.K. Gunjan;A.K. Panda;A. Mitra .Joining of 304SS and pure copper by rapidly solidified Cu-based braze alloy[J].Fusion engineering and design,2011(4/5):452-455. |
| [10] | 张胜,侯金保,郭德伦,魏友辉.镍基合金中间层TLP连接MGH956合金接头组织分析[J].航空制造技术,2007(01):84-86. |
| [11] | VILLARS P;PRINCE A;OKAMTO H.Handbook of Ternary Alloy Phase Diagrams[M].New York:ASM International,1995:5675-5683. |
| [12] | R.K. Roy;A.K.Panda;S.K.Das;Govind;A.Mitra .Development of a copper-based filler alloy for brazingstainless steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):312-315. |
| [13] | RAGHAVAN V .Cr-Fe-Mn(Chromium-Iron-Manganese)[J].Journal of Phase Equilibria,1994,15(5):530-531. |
| [14] | Ustinovshikov Y.;Pushkarev B.;Igumnov I. .Fe-rich portion of the Fe-Cr phase diagram: electron microscopy study[J].Journal of Materials Science,2002(10):2031-2042. |
| [15] | 周媛,毛唯,李晓红.BNi82CrSiB钎料钎焊DD6单晶合金接头组织及力学性能研究[J].材料工程,2007(05):3-6. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%