利用X射线衍射织构分析技术和电子背散射衍射微织构分析技术,对0.20mm CGO硅钢薄板在高温退火缓慢升温过程中表层和次表层的织构演变规律进行了研究.结果表明:0.20mm CGO硅钢在高温退火过程中经历了低温回复、初次再结晶、初次再结晶晶粒长大和二次再结晶形成最终锋锐Goss织构的演变过程.Goss取向晶粒最初起源于变形回复基体中残存于{111}<112>形变带上少量的Goss晶粒亚结构,600℃保温2h后,Goss取向晶粒率先从变形基体中转变形核,在随后的升温过程中逐渐发生再结晶,Goss取向晶粒在此过程中并不具有尺寸优势,700℃时初次再结晶完成,基体中以γ纤维织构和{112}<110>织构为主;随着退火温度的升高,Goss晶粒的含量和平均晶粒尺寸逐渐增加,在900～1000℃之间,Goss取向晶粒迅速“吞噬”其他取向晶粒形成锋锐的Goss织构,1000℃时已经发生了二次再结晶.
参考文献
| [1] | Xia ZS;Kang YL;Wang QL.Developments in the production of grain-oriented electrical steel[J].Journal of Magnetism and Magnetic Materials,200823(23):3229-3233. |
| [2] | Rajmohan, N;Hayakawa, Y;Szpunar, JA.Importance of fractions of highly mobile boundaries in abnormal growth of Goss grains[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,19991(1):8-16. |
| [3] | A. L. Etter;T. Baudin;R. Penelle.Influence of the Goss grain environment during secondary recrystallisation of conventional grain oriented Fe-3[J].Scripta materialia,200211(11):725-730. |
| [4] | Nakano M.;Arai KI.;Fukunaga H.;Ishiyama K..NEW PRODUCTION METHOD OF 100-MU-M-THICK GRAIN-ORIENTED 3-PERCENT SILICON STEEL SHEETS[J].Journal of Applied Physics,19978 Pt.2a(8 Pt.2a):4098-4100. |
| [5] | 王慧敏;杨平;崔凤娥;蒋奇武;金文旭.二次冷轧法与三次冷轧法制备取向硅钢薄带的织构转变规律[J].中国体视学与图像分析,2013(4):348-355. |
| [6] | 毕娜;张宁;杨平.取向硅钢薄带形变再结晶组织及织构演变[J].北京科技大学学报,2015(1):50-56. |
| [7] | 付勇军;蒋奇武;金文旭;杨平.取向硅钢高温退火样品晶粒尺寸、取向及磁性能关系的研究[J].电子显微学报,2010(1):43-47. |
| [8] | A. SAMET-MEZIOU;A.L. ETTER;T. BAUDIN.TEM Study of Recovery and Recrystallization Mechanisms After 40 percent Cold Rolling in an IF-Ti Steel[J].Scripta materialia,20058(8):1001-1006. |
| [9] | 颜孟奇;钱浩;杨平;宋惠军;邵媛媛;毛卫民.电工钢中黄铜织构行为及其对Goss织构的影响[J].金属学报,2012(1):16-22. |
| [10] | Mengqi Yan;Hao Qian;Ping Yang;Weimin Mao;Qiwu Jian;Wenxu Jin.Analysis of Micro-texture during Secondary Recrystallization in a Hi-B Electrical Steel[J].材料科学技术学报：英文版,2011(11):1065-1071. |
| [11] | 崔凤娥;杨平;毛卫民.取向硅钢中高斯晶粒异常长大选择性行为[J].北京科技大学学报,2010(9):1157-1162. |
| [12] | 李阳;毛卫民.取向电工钢中Goss晶粒生长的取向环境[J].材料研究学报,2010(1):33-36. |
| [13] | Jae Young Park;Kyu Seok Han;Jong Soo Woo.Influence of primary annealing condition on texture development in grain oriented electrical steels[J].Acta materialia,20027(7):1825-1834. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%