利用激光处理技术在灰铸铁表面加工了4种具有非光滑形态的试样，对比研究非光滑形态对对磨副的影响规律。结果表明：非光滑表面对对磨副的损伤机理与光滑试样不同，为非光滑表面凸起对对磨副的微观切削作用。非光滑表面对磨副的磨损质量均远大于未处理试样的对磨副，以对磨副磨损质量为评价指标，条状、环状、点状和网状对对磨副的损伤作用依次减小，损伤最小的网状对磨副其质量损失仅为等面积比下的条状对磨副的55．66％，在相同的单元体面积比和几乎相同的显微硬度条件下，通过调整单元体的形态可以有效地减轻对对磨副的损伤作用。这是由于不同形态的非光滑表面在磨损过程中的载荷分配机制不同。
Four biomimetic non‐smoothed surface specimens with different shapes were prepared by la‐ser processing .Tests were conducted on MMU‐5G wear and abrasion test machine to study the influ‐encing rule of non‐smoothed surfaces on counter pairs .The results show that the mass loss of the fric‐tion pair matching with the non‐smoothed units is much greater than the ones matching with the smooth specimens .The pairs matching with different non‐smoothed units suffer differently .The non‐smoothed surface protruding zone exerts micro cutting on counter pairs .The striation causes the grea‐test mass loss of the pairs than the other non‐smoothed units ,w hich almost doubles the damage of the grid ones suffering the least .The difference in pairs damage is attributed to the different mechanism of undertaking the load in the process of w ear .T he damage can be alleviated effectively by changing the shapes of the units without increasing or decreasing the area ratio of the non‐smoothed units .
参考文献
| [1] | 任露泉;杨卓娟;韩志武.生物非光滑耐磨表面仿生应用研究展望[J].农业机械学报,2005(7):144-147. |
| [2] | 孙娜;周宏;单宏宇;李孝艳;任露泉.激光制备仿生非光滑表面蠕墨铸铁的耐磨性[J].吉林大学学报（工学版）,2009(5):1157-1161. |
| [3] | 宋起飞;周宏;李跃;王磊;单宏宇;张志辉;任露泉.仿生非光滑表面铸铁材料的常温摩擦磨损性能[J].摩擦学学报,2006(1):24-27. |
| [4] | 陈莉;周宏;赵宇;任露泉.不同形态和间隔非光滑表面模具钢的磨损性能[J].机械工程学报,2008(3):173-176. |
| [5] | 戴振东;佟金;任露泉.仿生摩擦学研究及发展[J].科学通报,2006(20):2353-2359. |
| [6] | 杨卓娟;韩志武;任露泉.55号钢仿生非光滑表面高温耐磨性试验[J].农业机械学报,2008(12):196-199. |
| [7] | 任露泉;王再宙;韩志武.仿生非光滑表面滑动摩擦磨损试验研究[J].农业机械学报,2003(2):86-88,92. |
| [8] | 卢广林;邱小明;白杨;伦辛杰;邓宝清;任露泉.c-BN仿生耐磨复合材料的微观结构和耐磨性能[J].吉林大学学报（工学版）,2011(1):73-77. |
| [9] | CHEN Li;ZHOU Hong;ZHANG Zhi-hui;REN Lu-quan.Properties of 3Cr2W8V Die Steel With Striations Processed by Laser[J].钢铁研究学报（英文版）,2009(04):39-43. |
| [10] | Zhou H;Chen L;Wang W;Ren LQ;Shan HY;Zhang ZH.Abrasive particle wear behavior of 3Cr2W8V steel processed to bionic non-smooth surface by laser[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20051/2(1/2):323-327. |
| [11] | Na Sun;Hongyu Shan;Hong Zhou;Darong Chen;Xiaoyan Li;Wen Xia;Luquan Ren.Friction and wear behaviors of compacted graphite iron with different biomimetic units fabricated by laser cladding[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,201219(19):7699-7706. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%