以全动态DSC扫描实验为基础,结合半经验的唯象模型获得了基于唯象模型的具有双峰反应特性的高韧性双马来酰亚胺5429树脂的固化动力学参数,建立相应的唯象动力学模型。以5429树脂在180℃条件下,恒温不同时间的DSC实验数据为基础,利用DiBenedetto方程研究等温条件下固化度与加热时间的关系并得到玻璃化转变温度与固化时间的关系表达式,并采用凝胶盘法得到5429树脂不同温度下的凝胶时间,建立了凝胶时的固化度和玻璃化转变温度之间的函数关系,在此基础上绘制了T T T图,从T T T图中得到的5429树脂的最优固化工艺曲线与其标准固化工艺曲线一致。
The phenomenological model of 5429 resin was established by cure kinetic parameters of the bismaleimide (5429) with double‐heating wave reaction characteristics gained by dynamic DSC analysis combining with the phenomenological model .Also ,based on the DSC experimental data of 5429 resins at 180℃ with different heating time ,the relationship between curing degree and heating time of 5429 resin was investigated with DiBenedetto equation under isothermal condition ,and the equation of glass transition temperature and curing time were obtained .The gel time of 5429 resin was gained at differ‐ent time by gelation disk .The functional relationship between conversion at gelation and glass transi‐tion temperature of 5429 resin was also obtained .Then ,the time‐temperature‐transition (TTT) dia‐gram was presented based on the above results .The optimum curing curve of 5429 resin concluded from T T T diagram is consistent with the standard curing curve .
参考文献
[1] | Liu XY;Yu YF;Li SJ.Study on cure reaction of the blends of bismaleimide and dicyanate ester[J].Polymer: The International Journal for the Science and Technology of Polymers,200611(11):3767-3773. |
[2] | 王芳芳;张彦飞;杜瑞奎;刘亚青;赵贵哲.耐高温双马来酰亚胺树脂体系的流变性能[J].高分子材料科学与工程,2013(9):53-57. |
[3] | L.Nunez;F.Fraga;A.Castro;M.R.Nunez;M.Villanueva.TTT cure diagram for an epoxy system diglycidyl ehter of bisphenol A/1,2 diamine cyclohexane/calcium carbonate filler[J].Polymer: The International Journal for the Science and Technology of Polymers,20018(8):3581-3587. |
[4] | 张明;安学锋;唐邦铭;益小苏.高性能双组份环氧树脂固化动力学研究和TTT图绘制[J].复合材料学报,2006(1):17-25. |
[5] | PIZZI A.;LU X.;GARCIA R..Lignocellulosic Substrates Influence on TTT and CHT Curing Diagrams of Polycondensation Resins[J].Journal of Applied Polymer Science,19996(6):915-925. |
[6] | Nunez L.;Nunez MR.;Villanueva M.;Fraga F..Effects of diffusion on the kinetic study and TTT cure diagram for an epoxy/diamine system[J].Journal of Applied Polymer Science,199810(10):1931-1938. |
[7] | Wu, G.;Kou, K.;Chao, M.;Zhuo, L.;Zhang, J.;Li, N..Preparation and characterization of bismaleimide-triazine/epoxy interpenetrating polymer networks[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2012:44-50. |
[8] | 程群峰;方征平;益小苏;廖建伟;唐邦铭;许亚洪.双马来酰亚胺树脂体系的固化动力学和TTT图[J].材料工程,2007(z1):188-192. |
[9] | 石凤;段跃新;梁志勇;张佐光.RTM专用双马来酰亚胺树脂体系化学流变特性[J].复合材料学报,2006(1):56-62. |
[10] | 胡睿;王汝敏;强雪原;马瑞婷.新型烯丙基化合物改性双马来酰亚胺树脂的制备及研究[J].工程塑料应用,2013(9):10-14. |
[11] | 梁滨;陈立新;曹魏;聂玉峰;李都宁.碳纤维/改性双马来酰亚胺复合材料RFI成型工艺数值模拟[J].复合材料学报,2011(6):59-64. |
[12] | 张晨乾;安学锋;董慧民;闫丽;高军鹏.反应性聚醚砜对RTM用6421BMI树脂性能的影响[J].热固性树脂,2012(06):33-36. |
[13] | Premkumar S;Chozhan CK;Alagar M.Studies on thermal, mechanical and morphological behaviour of caprolactam blocked methylenediphenyl diisocyanate toughened bismaleimide modified epoxy matrices[J].European Polymer Journal,20088(8):2599-2607. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%