以FeSO4·7H2 O ，LiOH · H2 O和 H3 PO4为原料，葡萄糖为改性剂，采用微波水热法合成具有正交晶系橄榄石结构的LiFePO4／C复合材料。借助XRD ，SEM ，EDS和电化学性能测试等分析，研究葡萄糖对产物组成、结构、微观形貌和电化学性能的影响。结果表明：葡萄糖改性后，LiFePO4结构中Fe ，P和O原子间的结合增强，颗粒尺寸减小，表面有碳层包覆，电化学性能提高。LiFePO4／C在0．1 C倍率下的首次放电比容量为125．6mAh／g ；1．0 C倍率下的首次放电比容量为106．2mAh／g ，30次循环后的容量保持率为91．3％。
Orthorhombic LiFePO4/C composite material with olivine structure was prepared by micro‐wave hydrothermal method using FeSO4 · 7H2 O ,LiOH · H2 O and H3 PO4 as raw materials ,with glu‐cose as carbon source and modifier .T he influence of glucose on the composition ,structure ,morphol‐ogy and electrochemical performance of LiFePO4 was investigated by means of XRD ,SEM ,EDS and constant current charge‐discharge cycling .The results show that the as‐obtained LiFePO4/C exhibits stronger bonding among Fe ,P and O atoms ,finer particle size and improved electrochemical proper‐ties than the pristine LiFePO4 .From the SEM image ,the LiFePO4 is coated by carbon in the LiFe‐PO4/C composite .The LiFePO4/C shows the initial discharge capacity of 125 .6mAh/g at 0 .1C .Even at a rate of 1.0C ,it still can deliver a discharge capacity of 106.2mAh/g ,the capacity retention is 91.3% after 30 cycles .
参考文献
| [1] | Liu, HW;Tang, DG.The low cost synthesis of nanoparticles LiFePO4/C composite for lithium rechargeable batteries[J].Solid state ionics,200833/34(33/34):1897-1901. |
| [2] | Sunhye Lim;Chong S. Yoon;Jaephil Cho.Synthesis of Nanowire and Hollow LiFePO4 Cathodes for High-Performance Lithium Batteries[J].Chemistry of Materials: A Publication of the American Chemistry Society,200814(14):4560-4564. |
| [3] | 从长杰;张向军;卢世刚;江丹平.纳米磷酸铁锂的制备及电化学性能研究[J].无机化学学报,2011(7):1319-1323. |
| [4] | She-huang Wu;Mao-Sung Chen;Chao-Jung Chien;Yen-Pei Fu.Preparation and characterization of Ti~(4+)-doped LiFePO_4 cathode materials for lithium-ion batteries[J].Journal of Power Sources,20091(1):440-444. |
| [5] | 王震坡;刘文;王悦;赵春松;张淑萍;陈继涛;周恒辉;张新祥.Mg、Ti离子复合掺杂改性磷酸铁锂正极材料及其电池性能[J].物理化学学报,2012(9):2084-2090. |
| [6] | 王伟;赵领;张峥;刘兴泉.混合铁源制备碳包覆磷酸铁锂[J].电池,2014(1):24-27. |
| [7] | Liu, H;Xie, JY;Wang, K.Synthesis and characterization of LiFePO4/(C+Fe2P) composite cathodes[J].Solid state ionics,200827/32(27/32):1768-1771. |
| [8] | Muxina Konarova;Izumi Taniguchi.Preparation Of Lifepo_4/c Composite Powders By Ultrasonic Spray Pyrolysis Followed By Heat Treatment And Their Electrochemical Properties[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,200812(12):3305-3317. |
| [9] | Lee SB;Cho SH;Cho SJ;Park GJ;Park SH;Lee YS.Synthesis of LiFePO4 material with improved cycling performance under harsh conditions[J].Electrochemistry communications,20089(9):1219-1221. |
| [10] | Daiwon Choi;Prashant N. Kumta.Surfactant based sol-gel approach to nanostructured LiFePO_4 for high rate Li-ion batteries[J].Journal of Power Sources,20072(2):1064-1069. |
| [11] | Zhongli Wang;Shaorui Su;Chunyang Yu;Yu Chen;Dingguo Xia.Synthesises, Characterizations And Electrochemical Properties Of Spherical-like Lifepo_4 By Hydrothermal Method[J].Journal of Power Sources,20082(2):633-636. |
| [12] | 孙莹 .微波水热法制备LiFePO4电池阴极材料的研究[D].陕西科技大学,2012. |
| [13] | Haiyan Gao;Lifang Jiao;Wenxiu Peng;Guang Liu;Jiaqin Yang;Qianqian Zhao;Zhan Qi;Yuchang Si;Yijing Wang;Huatang Yuan.Enhanced electrochemical performance of LiFePO_4/C via Mo-doping at Fe site[J].Electrochimica Acta,201127(27):9961-9967. |
| [14] | Youyong Liu;Chuanbao Cao.Enhanced electrochemical performance of nano-sized LiFePO_4/C synthesized by an ultrasonic-assisted co-precipitation method[J].Electrochimica Acta,201016(16):4694-4699. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%