缺陷容限设计方法充分考虑直升机的特点,将损伤容限设计思想巧妙地应用于直升机的设计中,通过缺陷容限值保证关键动部件的服役安全.本文采用疲劳极限反推的方法测试了三种尺寸的缺陷容限门槛值,分别采用有限元法和Y.Murakami公式计算缺陷容限门槛值,结果表明:含有265μm,374 μm,480μm缺陷尺寸的三种试件缺陷容限门槛值基本相同;缺陷容限门槛值明显低于长裂纹门槛值,采用长裂纹门槛值作为缺陷容限门槛值会导致偏于危险的结果;有限元法与Y.Murakami公式应力强度因子计算结果非常接近,Y.Murakami公式计算结果略低于有限元法.
参考文献
| [1] | 柳文林,穆志韬,段成美.直升机动部件寿命管理的损伤容限方法[J].中国工程科学,2005(02):76-80. |
| [2] | 万少杰.直升机机体结构疲劳和损伤容限设计[J].直升机技术,2004(04):1-6. |
| [3] | 曾玖海,曾本银,史斯佃.直升机动部件安全寿命和破损安全相结合定寿技术[J].直升机技术,2003(03):15-20. |
| [4] | 金平,陈跃良,段成美.直升机动部件定寿技术研究[J].航空学报,2002(03):255-258. |
| [5] | 吴德锋,隋福成,毛春见.先进飞机典型结构关键部位损伤容限分析研究[J].飞机设计,2010(05):16-19. |
| [6] | 张纪奎,程小全,郦正能.基于损伤容限设计的机体金属材料力学性能综合表征与评价[J].材料工程,2010(07):49-53. |
| [7] | U. Zerbst;S. Beretta;G. K6hler.Safe life and damage tolerance aspects of railway axles - A review[J].Engineering Fracture Mechanics,2013:214-271. |
| [8] | TELESMAN J;GHOSN L J .The unusual near-threshold FCG behavior of a single crystal superalloy and the resolved shear stress as the crack driving force[J].Engineering Fracture Mechanics,1989,34:1183-1196. |
| [9] | SALVADORI A;GIACOMINI A .The most dangerous flaw orientation in brittle materials and structures.International Journal of Fracture[J].International Journal of Fracture,2013,183(1):19-28. |
| [10] | Simon A. Barter .The quantification of fatigue crack initiators in aluminium alloy 7050-T7451 using quantitative f ractography[J].International journal of structural integrity,2011(3):243-263. |
| [11] | L. Molent;Q. Sun;A. J. Green .Characterisation of equivalent initial flaw sizes in 7050 aluminium alloy[J].Fatigue & Fracture of Engineering Materials and Structures,2006(11):916-937. |
| [12] | Tianwen Zhao;Yanyao Jiang .Fatigue of 7075-T651 aluminum alloy[J].International Journal of Fatigue,2008(5):834-849. |
| [13] | Newman Jr J C .A crack closure model for predicting fatigue crack growth under aircraft spectrum loading[J].ASTM STP,1981,748:53-84. |
| [14] | 中国航空研究院.应力强度因子手册[M].北京:科学出版社,1993 |
| [15] | MURAKAMI Y .Growth and stability of interacting surface flaws of arbitrary shape[J].Engineering Fracture Mechanics,1983,17(3):193-210. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%