针对高端夹层玻璃的老化问题,选用荧光紫外灯,对其主要粘结材料———透明聚氨酯胶片分别进行0/200/300/500 h的照射,借助紫外/可见光分光光度计、傅里叶红外光谱仪、扫描电镜等设备,研究照射过程中材料颜色、结构、微观形貌的变化。扫描电镜显示照射时间延长到500 h,材料表面出现龟裂。实验发现胶片的老化起始于硬段及软段部位与N,O相连的α位置的碳原子,在紫外光及氧气的联合作用下产生氢过氧化物；该过氧化合物一部分继续氧化成C—O,一部分通过β分裂,使C—N,C—O键断裂,致使材料龟裂。
According to the ageing problem of laminated transparency, the trasparent polyurethane film used as interlayer had been irra-diated by fluorescent ultraviolet lamp for 0 h, 200 h, 300 h, and 500 h respectively. With the aid of ultraviolet / visible spectropho-tometer, FTIR and SEM etc. , the color, structure and morphology of the materials were studied. SEM shows that when the irradiation time is increased to 500 h, the film surface cracks. The UV degradation mechanisms are that —CH2— of the position connecting the O and N from hard segment and the soft segment are easy to oxidize and produce hydrogen peroxide under UV and oxygen, which is furtherly oxidized to C—O, and some part of the C—O and C—N bonds is cracked throughβscission, and then the materials are fractured.
参考文献
| [1] | Ricky S.C. Woo;Honggang Zhu;Christopher K.Y. Leung;Jang-Kyo Kim.Environmental degradation of epoxy-organoclay nanocomposites due to UV exposure: Part II residual mechanical properties[J].Composites science and technology,20089(9):2149-2155. |
| [2] | Ricky S.C. Woo;Yanghai Chen;Honggang Zhu.Environmental degradation of epoxy-organoclay nanocomposites due to UV exposure. Part I: Photo-degradation[J].Composites science and technology,200715/16(15/16):3448-3456. |
| [3] | A. Boubakri;N. Guermazi;K. Elleuch;H.F. Ayedi.Study of UV-aging of thermoplastic polyurethane material[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20107/8(7/8):1649-1654. |
| [4] | Bajsic EG.;Sendijarevic A.;Sendijarevic V.;Frish KC.;Rek V..THE EFFECT OF DIFFERENT MOLECULAR WEIGHT OF SOFT SEGMENTS IN POLYURETHANES ON PHOTOOXIDATIVE STABILITY[J].Polymer Degradation and Stability,19963(3):223-233. |
| [5] | L. Irusta;M.J. Fernandez-Berridi.Photooxidative behaviour of segmented aliphatic polyurethanes[J].Polymer Degradation and Stability,19991(1):113-119. |
| [6] | Qin HL;Zhang SM;Liu HJ;Xie SB;Yang MS;Shen DY.Photo-oxidative degradation of polypropylene/montmorillonite nanocomposites[J].Polymer: The International Journal for the Science and Technology of Polymers,20059(9):3149-3156. |
| [7] | Delor F.;Duteurtre X.;Cardinet C.;Lemaire J.;Lacoste J.;Barrois-Oudin N..Oxidation of rubbers analysed by HATR/IR spectroscopy[J].Polymer Degradation and Stability,19982(2):395-401. |
| [8] | Gijsman P..New synergists for hindered amine light stabilizers[J].Polymer: The International Journal for the Science and Technology of Polymers,20025(5):1573-1579. |
| [9] | Zhao QL;Li XG;Gao J.Aging of ethylene-propylene-diene monomer (EPDM) in artificial weathering environment[J].Polymer Degradation and Stability,200710(10):1841-1846. |
| [10] | Rosu, D;Rosu, L;Cascaval, CN.IR-change and yellowing of polyurethane as a result of UV irradiation[J].Polymer Degradation and Stability,20094(4):591-596. |
| [11] | Wilhelm C.;Gardette JL..Infrared analysis of the photochemical behaviour of segmented polyurethanes: aliphatic poly(ether-urethane)s[J].Polymer: The International Journal for the Science and Technology of Polymers,199824(24):5973-5980. |
| [12] | Bhavesh G.Kumar;Raman P.Singh;Toshio Nakamura.Degradation of Carbon Fiber-reinforced Epoxy Composites by Ultraviolet Radiation and Condensation[J].Journal of Composite Materials,200224(24):2713-2733. |
| [13] | R.P.Singh;Namrata S.Tomer;S.Veera Bhadraiah.Photo-oxidation studies on polyurethane coating: effect of additives on yellowing of polyurethane[J].Polymer Degradation and Stability,20013(3):443-446. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%