研究了 DZ408合金在950℃，1000℃和1050℃，应变比为0．05条件下的低周疲劳性能。结果表明：平均应变为正时，非对称循环应变控制会产生平均应力松弛现象，且随着温度与应变幅的增大，平均应力松弛速率增大；在950℃，1000℃和1050℃时，材料具有 Massing 特性，采用修正的 SWT 模型能很好地预测不同温度下应变比为0．05的低周疲劳寿命，且给出了修正 SWT 模型参数随温度变化的关系式Δεt 2σmax ＝（－38．9＋0．101 T）N（0．96－0．0014T）。
The total strain-controlled low cycle fatigue(LCF)behaviors of directionally solidified(DS)superalloy DZ408 at 950 ℃, 1000 ℃ and 1050 ℃ for R =0.05 were investigated.The results of LCF tests indicate that the mean stress relaxation is occurred under asymmetric straining .The rate of mean stress relaxation is increased with the increase of temperature and strain amplitude.The alloy has Massing characteristic at 950 ℃,1000 ℃ and 1050 ℃ for R =0.05.All the LCF data obtained under various temperatures are well correlated by the modified SWT approach for lifetime prediction,and also the relationship between temperature and parameter of modi-fied SWT model are obtained.
参考文献
| [1] | 杨海青;李青;肖程波;胡聘聘;林山峰.Re及时效时间对耐腐蚀镍基定向合金组织和持久寿命的影响[J].材料工程,2015(6):31-37. |
| [2] | 刘金龙;石多奇;杨晓光;包宇;王井科.应变比对定向凝固高温合金DZ125低循环疲劳行为影响的研究[J].材料工程,2010(12):47-50,60. |
| [3] | 丁智平;陈吉平;尹泽勇;杨治国.非对称循环载荷下镍基单晶合金低周疲劳寿命预测[J].航空材料学报,2006(4):6-10. |
| [4] | 张仕朝;于慧臣;李影.GH3044的高温低周疲劳性能研究[J].航空材料学报,2013(1):100-104. |
| [5] | 刘维维;唐定中;李嘉荣;刘世忠;熊继春.抽拉速率对DD6单晶高温合金650℃低周疲劳性能的影响[J].航空材料学报,2012(2):8-12. |
| [6] | Chih-Kuang Lin;Yi-Lin Pai.Low-cycle fatigue of austempered ductile irons at various strain ratios[J].International Journal of Fatigue,19991(1):45-54. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%