观察了1260℃与1240℃固溶温度热处理后DZ8合金的显微组织,比较了两者的拉伸与持久性能.结果表明:采用1260℃固溶温度热处理,DZ8合金存在少于1％的γ+γ'共晶相,但富Hf相发生初熔;采用1240℃固溶温度热处理,合金未发现初熔但仍存在12％左右的γ+γ'共晶相.DZ8合金分别采用1260℃与1240℃固溶温度热处理后,室温、700℃与980℃拉伸性能以及980℃/205 MPa持久性能相当,但采用1260℃固溶温度热处理的D28合金其760℃/725 MPa持久性能较采用1240℃固溶温度热处理的有所下降.
参考文献
| [1] | 张剑;骆宇时;赵云松;杨帅;贾玉亮;崔丽丽;许剑伟;唐定中.一种低密度镍基单晶高温合金的组织与性能研究[J].航空材料学报,2011(z1):90-93. |
| [2] | M. Hantcherli;F. Pettinari-Sturmel;B. Viguier.Evolution of interfacial dislocation network during anisothermal high-temperature creep of a nickel-based superalloy[J].Scripta materialia,20123/4(3/4):143-146. |
| [3] | R.R. Unocic;N. Zhou;L. Kovarik.Dislocation decorrelation and relationship to deformation microtwins during creep of a γ' precipitate strengthened Ni-based superalloy[J].Acta materialia,201119(19):7325-7339. |
| [4] | J.S. Van Sluytman;T.M. Pollock.Optimal precipitate shapes in nickel-base y-y' alloys[J].Acta materialia,20124(4):1771-1783. |
| [5] | N. Bozzolo;N. Souai;R.E. Loge.Evolution of microstructure and twin density during thermomechanical processing in a γ-γ' nickel-based superalloy[J].Acta materialia,201213/14(13/14):5056-5066. |
| [6] | 佘力;陈荣章;王涛.定向凝固铸造高温合金DZ125热处理工艺的研究[J].材料热处理学报,2002(4):13-15. |
| [7] | 马文有;李树索;乔敏;宫声凯;郑运荣;韩雅芳.热处理对镍基单晶高温合金微观组织和高温持久性能的影响[J].中国有色金属学报,2006(6):937-944. |
| [8] | 宁礼奎;郑志;金涛;唐颂;刘恩泽;佟健;于永泗;孙晓峰.热处理对一种新型镍基单晶高温合金组织与性能的影响[J].金属学报,2014(8):1011-1018. |
| [9] | 曹腊梅;李相辉;陈晶阳;薛明;张勇.固溶温度对第三代镍基单晶高温合金DD10组织的影响[J].材料工程,2011(10):23-27. |
| [10] | 刘丽荣;金涛;赵乃仁;王志辉;孙晓峰;管恒荣;胡壮麒.一种镍基单晶高温合金蠕变机制的研究[J].金属学报,2005(11):1215-1220. |
| [11] | 袁超;郭建亭;杨洪才.铸造镍基高温合金的蠕变阻力[J].金属学报,2002(11):1149-1156. |
| [12] | 袁超;郭建亭;冀光.一种低成本镍基铸造高温合金的高温力学行为[J].材料工程,2004(5):12-15,39. |
| [13] | 苏勇;田素贵;于慧臣;于莉丽.镍基单晶高温合金中温稳态蠕变期间的变形机制[J].金属学报,2015(12):1472-1480. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%