采用0.3 MPa压力对DD6单晶高温合金进行水吹砂，然后用电子束物理气相沉积的方法在DD6合金基体上制备了热障涂层，将带热障涂层试样置于1100℃空气气氛中分别进行50 h和100 h热暴露，在1100℃/130 MPa条件下测试持久性能。研究了水吹砂及高温热暴露对带热障涂层DD6合金组织的影响。结果表明：0.3 MPa压力水吹砂制备热障涂层并高温热暴露后没有发现再结晶组织；热暴露过程中，基体和涂层之间的元素会发生不同程度的互扩散；表面残余应力和元素互扩散导致了γ′相粗化方向的变化；性能测试后试样断口附近的涂层与基体界面下方局部区域形成了二次反应区。
In order to investigate the effect of water grit-blasting and high temperature thermal exposure on the microstructures of DD6 alloy with TBCs, DD6 single crystal superalloy specimens were water grit-blasted with 0. 3 MPa pressure, then the specimens were coa-ted with thermal barrier coatings by electron beam physical vapor deposition ( EB-PVD) . Specimens with TBCs were exposed at 1100℃ for 50 and 100 hours in the air respectively, and then these specimens were subjected to stress-rupture tests under the condition of 1100 ℃/130 MPa. The results show that grit-blasting doesn’ t lead into the recrystallization, thermal exposure can induce element in-terdiffusion between the bond coat and alloy substrate, the residual stress and element diffusion lead into the changes ofγ′phase coar-sing direction. After stress rupture tests, the secondary reaction zone emerges into a local area.
参考文献
| [1] | 刘纯波;林锋;蒋显亮.热障涂层的研究现状与发展趋势[J].中国有色金属学报,2007(1):1-13. |
| [2] | 文生琼;何爱杰;王皓.热障涂层在航空发动机涡轮叶片上的应用[J].燃气涡轮试验与研究,2009(1):59-62. |
| [3] | 赵洪雷;王松涛;韩万金;冯国泰.联合应用现代优化方法与S2流面计算进行多级涡轮的气动设计[J].燃气涡轮试验与研究,2007(1):27-31. |
| [4] | 吴小梅;贺世美;李建平;何利民.EB-PVD热障涂层对IC10合金力学性能的影响[J].航空材料学报,2009(6):77-80. |
| [5] | 郑亮;肖程波;张国庆;顾国红;李鑫;刘晓光;薛明;唐定中.高Cr铸造镍基高温合金K4648与陶瓷型芯的界面反应研究[J].航空材料学报,2012(3):10-22. |
| [6] | 董建民;李嘉荣;牟仁德;赵金乾;史振学;刘世忠.高温热处理对带热障涂层DD6单晶高温合金互扩散行为及持久断裂特征的影响[J].材料工程,2014(6):51-55,61. |
| [7] | 熊继春;李嘉荣;刘世忠;韩梅.合金状态对单晶高温合金DD6再结晶的影响[J].中国有色金属学报,2010(7):1328-1333. |
| [8] | 李志强;黄朝晖;谭永宁;张强;张宏炜;贾新云;王艳丽.表面再结晶对DD5镍基单晶高温合金组织和力学性能的影响[J].航空材料学报,2011(5):1-5. |
| [9] | 张义文;王福明;胡本芙.Hf含量对FGH97合金γ/γ'晶格错配度的影响[J].稀有金属材料与工程,2012(6):989-993. |
| [10] | 侯介山;丛培娟;周兰章;秦学智;袁超;郭建亭.Hf对抗热腐蚀镍基高温合金微观组织和力学性能的影响[J].中国有色金属学报,2011(5):945-953. |
| [11] | 姚锐;郭洪波;彭徽;宫声凯.NiCrAlYSi涂层/DD6单晶高温合金界面再结晶和互扩散行为[J].航空学报,2011(4):751-757. |
| [12] | 钟锦岩;牟仁德;何英;何利民.NiCoCrAlYHf涂层与一种Ni基单晶高温合金循环氧化行为研究[J].材料工程,2013(8):28-35. |
| [13] | J.D.Nystrom.Discontinuous Cellular Precipitation in a High-Refractory Nickel-Base Superalloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,199712(12):2443-2452. |
| [14] | 王娟;彭徽;陈国忠;郭洪波;宫声凯.Ru过渡层对NiCoCrAlY涂层与DD6单晶高温合金界面扩散行为的影响[J].航空学报,2011(4):758-764. |
| [15] | 熊玉明;李明升;李松林.热障涂层与镍基高温合金界面的互扩散行为[J].粉末冶金材料科学与工程,2007(2):63-69. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%