通过XRF和XRD分析除硅铜冶炼水淬渣的元素和物相特性,结合动力学分析,开展除硅铜渣硫酸化浸出的实验研究,考察了硫酸浓度、浸出时间、液固比、温度、粒径大小对铜和锌浸出率的影响.结果表明:在机械搅拌下,硫酸的浓度为2.5 mol/L,浸出时间为120 min,液固比(m/m)为4∶1,温度为70℃,粒径大小为200目时铜和锌的浸出率最高,此时铜和锌的浸出率分别为76.2％和98.3％.
参考文献
| [1] | Maxim I. Muravyov;Natalya V. Fomchenko;Alexey V. Usoltsev.Leaching of copper and zinc from copper converter slag flotation tailings using H_2SO_4 and biologically generated Fe_2(SO_4)_3[J].Hydrometallurgy,2012:40-46. |
| [2] | Ahmed I M;Nayl A A;Daoud J A.Leaching and recovery of zinc and copper from brass slag by sulfuric acid[J]][J].J Saudi Chem Soc |
| [3] | Ayse Vildan Bese .Effect of ultrasound on the dissolution of copper from copper converter slag by acid leaching[J].Ultrasonics sonochemistry,2007(6):790-796. |
| [4] | Ewa Rudnik;Lidia Burzynska;Wanda Gumowska .Hydrometallurgical recovery of copper and cobalt from reduction-roasted copper converter slag[J].Minerals Engineering,2009(1):88-95. |
| [5] | F. Carranza;N. Iglesias;A. Mazuelos .Ferric leaching of copper slag flotation tailings[J].Minerals Engineering,2009(1):107-110. |
| [6] | 张林楠 .铜渣中有价组分的选择性析出研究[D].东北大学,2005. |
| [7] | 陈远望.智利铜炉渣贫化方法概述[J].世界有色金属,2001(09):53-58. |
| [8] | 曹景宪;王丙恩 .中国铁矿的开发与利用[J].中国矿业,1994,3(05):17. |
| [9] | 刘纲,朱荣.当前我国铜渣资源利用现状研究[J].矿冶,2008(03):59-63. |
| [10] | 黄志,徐建平,马春艳,罗亚楠.硫酸盐还原菌处理重金属离子[J].重庆理工大学学报（自然科学版）,2013(03):43-46. |
| [11] | 陈茂生;韩子荣;陈锦 .从铜冶炼渣中分离出铁、铜、硅组分的方法[P].中国,201010223703.2,2010-11-17. |
| [12] | 邓小华 .铜镉渣中回收金属锌、铜、镉的研究[D].同济大学,2005. |