通过光学显微镜、扫描电镜、能谱和X射线衍射分析和拉伸实验等试验分析方法,研究不同热轧变形量(54％、75％)对5052铝合金微观组织和力学性能的影响.结果显示,变形量可显著影响5052铝合金的热变形组织及其力学性能.随着轧制变形量的增加,晶粒被显著拉长,晶界处粗大第二相沿晶界被拉长,甚至被破碎.但是其第二相的组成并没有随着轧制变形量的增加而变化,铸态和轧制态的5052铝合金均由α-Al、Al82Fe18和Mg2Si三相组成.同时随着轧制变形量的增加,其综合力学性能提高,即沿轧制方向且轧制量为75％时的5052铝合金呈现出最优的综合力学性能.
参考文献
| [1] | 任文达 .5052铝合金变形行为及退火处理对其微观组织与性能的影响[D].中南大学,2007. |
| [2] | Wei Wen;J.G. Morris .The effect of cold rolling and annealing on the serrated yielding phenomenon of AA5182 aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):204-216. |
| [3] | 潘复生;张丁非.铝合金及应用[M].北京:化学工业出版社,2007:1. |
| [4] | Zhu Hanliang;Ghosh A K;Maruyama K .Effect of cold rolling on microstructure and material properties of 5052 alloy sheet produced by continuous casting[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2006,419(1-2):115. |
| [5] | Liu W C;Man C S et al.Effect of hot and cold deformation on the recrystallization texture of continuous cast AA 5052 aluminum alloy[J].Scripta Materialia,2005,53(11):1273. |
| [6] | 李良福.国外新型铝合金的研制概况[J].有色金属加工,2007(02):23-24,42. |
| [7] | 王雷,黄汝刚,袁文生.铝合金轧制成形的研究与现状[J].锻压装备与制造技术,2012(05):17-20. |
| [8] | 钱宝华 .加工工艺对5052铝合金板材组织及性能的影响[D].重庆:重庆大学,2008. |
| [9] | 蔡辉.5052铝合金材料研究进展[J].铝加工,2011(06):33-39. |
| [10] | 陈文华 .5052铝合金铸轧工艺及组织研究[D].东北大学,2010. |
| [11] | 梁海建,刁浩岩,吴晓炜,王勇.工业铝合金5052超塑性研究[J].热加工工艺,2012(06):32-34. |
| [12] | 许晓静,蒋凌,陆文俊,卢予东,费震旦,成城.轧制及后续热处理对5052铝合金拉伸性能与晶体取向的影响[J].稀有金属材料与工程,2014(01):245-248. |
| [13] | Liu W C;Morris J G .Effect of hot and cold deformation on theβ fiber rolling texture in continuous cast AA 5052 aluminum alloy[J].Scripta Materialia,2005,52(12):1317. |
| [14] | Y. C. Chen;Y. Y. Huang;C. P. Chang;P. W. Kao .The effect of extrusion temperature on the development of deformation microstructures in 5052 aluminium alloy processed by equal channel angular extrusion[J].Acta materialia,2003(7):2005-2015. |
| [15] | Tsai TL.;Sun PL.;Kao PW.;Chang CP. .Microstructure and tensile properties of a commercial 5052 aluminum alloy processed by equal channel angular extrusion[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):144-151. |
| [16] | 易成,关绍康,卢广玺,赵红亮,王盼.退火工艺对铸轧5052铝合金组织和性能的影响[J].材料热处理学报,2011(04):52-57. |
| [17] | 张登峰.5052铝合金板材生产工艺研究[J].有色金属加工,2013(02):16-18. |
| [18] | 于翠翠 .5052铝合金冷轧织构与力学性能的研究[D].燕山大学,2010. |
| [19] | 解正业,李仕雄.5052 H32板材生产工艺研究[J].有色金属加工,2005(01):25-26,32. |
| [20] | 海朝智,马建华.5052H34铝合金板材生产工艺研究[J].轻合金加工技术,2000(12):14-17. |
| [21] | 李周兵,闫亮明,沈健.热轧变形量对7055铝合金组织与力学性能的影响[J].特种铸造及有色合金,2013(01):1-4. |
| [22] | 任伟才,彭国胜,陈康华,陈送义,刘显东.轧制变形量对Al-Zn-Mg-Cu合金组织与力学性能以及腐蚀性能的影响[J].粉末冶金材料科学与工程,2013(06):807-813. |
| [23] | 崔忠圻.金属学与热处理[M].哈尔滨:哈尔滨工业大学出版社,2007:199. |
| [24] | 周振平,李荣德,马建超,王毅.Mg对初生Al3Fe形貌及其生长过程的影响[J].热加工工艺,2004(05):15-17. |
| [25] | 王振玲,王宏伟,魏尊杰,曹磊.Al-9.6%Mg合金高压凝固组织及稳定性[J].中国有色金属学报,2007(03):384-389. |
| [26] | 易成 .退火工艺对铸轧5052铝合金组织和性能的影响[D].郑州大学,2010. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%