钢筋锈蚀导致混凝土耐久性的降低问题一直受到全世界的广泛关注，迁移型有机阻锈剂可以有效提升混凝土的耐久性，并与混凝土结构有着很好的相容性，且在经济上优于普通掺入型无机阻锈剂。从混凝土工程钢筋锈蚀原因、迁移型阻锈剂的阻锈机理进行分析，进而介绍迁移型阻锈剂的国内外研究情况以及迁移型阻锈剂的性能试验和评价方法，最后就迁移型阻锈剂相关应用的问题进行总结。
Steel bar corrotion-induced durability degradation has received extensive attention from all over the world.Migrating corrosion inhibitor can improve the durability of concrete effectively,and it′s well compatible with structure of concrete.The economy of migrating corrosion inhibitor is also superior than inorganic corrosion inhibitor. In this paper,the corrosion reason of concrete and mechanism of migrating corrosion inhibitor are analyzed.Subse-quently,domestic and foreign developments of migrating corrosion inhibitor are introduced,also with the property tes-ting and evaluation method of migrating corrosion inhibitor.Finally,Application problems of migrating corrosion in-hibitor are summarized.
参考文献
| [1] | 周福根;袁泉利;曹存宁.跨江（海）大型桥梁主体结构的涂层防护与维护[J].全面腐蚀控制,2011(10):24-32. |
| [2] | 张敬书;汪朝成.钢筋混凝土基础的腐蚀与防护措施[J].中国科学院研究生院学报,2010(2):145-153. |
| [3] | 洪乃丰.混凝土中钢筋腐蚀与防护技术（6）--钢筋阻锈剂和阴极保护[J].工业建筑,2000(01):57-60. |
| [4] | 张小冬;周庆;陈烈.钢筋阻锈剂的应用发展概况[J].施工技术,2004(6):52-53. |
| [5] | 洪乃丰.钢筋阻锈剂的发展与应用[J].工业建筑,2005(06):68-70,79. |
| [6] | 张大全;高立新;周国定.国内外缓蚀剂研究开发与展望[J].腐蚀与防护,2009(9):604-610. |
| [7] | 刘志勇;缪昌文;周伟玲;刘加平.迁移性阻锈剂对混凝土结构耐久性的保持和提升作用[J].硅酸盐学报,2008(10):1494-1500. |
| [8] | 韩巍巍,田佳琳,蔡伟.钢筋阻锈剂研究进展[C].第八届全国混凝土耐久性学术交流会论文集,2012:38-43. |
| [9] | 李伟华;裴长岭;何桥;侯保荣.混凝土中钢筋腐蚀与钢筋阻锈剂[J].材料开发与应用,2007(5):57-60. |
| [10] | 潘崇根;杨小草;徐强;盛建松;詹树林;杨辉.阻锈剂在海洋工程高性能混凝土中的研究进展[J].材料导报,2013(21):97-100,138. |
| [11] | 郑靓,余其俊,杨墨,韦江雄.混凝土中钢筋阻锈剂的作用研究[C].第十届全国水泥和混凝土化学及应用技术会议,2007 |
| [12] | 徐永模.迁移性阻锈剂--钢筋混凝土阻锈剂的新发展[J].硅酸盐学报,2002(1):94-101. |
| [13] | 马新伟;邙静喆;范征宇.钢筋阻锈剂的新发展[J].低温建筑技术,2004(6):7-8. |
| [14] | E. Rakanta;Th. Zafeiropoulou;G. Batis.Corrosion protection of steel with DMEA-based organic inhibitor[J].Construction and Building Materials,2013Jul.(Jul.):507-513. |
| [15] | M. Ormellese;M. Berra;F. bolzoni.Corrosion inhibitors fro chlorides induced corrosion in reinforced concrete structures[J].Cement and Concrete Research,20063(3):536-547. |
| [16] | M. Ormellese;F. Bolzoni;S. Goidanich;M. P. Pedeferri;A. Brenna.Corrosion inhibitors in reinforced concrete structures Part 3 - migration of inhibitors into concrete[J].Corrosion Engineering, Science and Technology,20114(4):334-339. |
| [17] | L. Holloway;K. Nairn;M. Forsyth.Concentration monitoring and performance of a migratory corrosion inhibitor in steel-reinforced concrete[J].Cement and Concrete Research,20048(8):1435-1440. |
| [18] | T.A. Soylev;C. McNally;M.G. Richardson.The effect of a new generation surface-applied organic inhibitor on concrete properties[J].Cement & concrete composites,20075(5):357-364. |
| [19] | 贺奎;王二坡;王万金;夏义兵;李海峰;王靖.AMCI迁移型防腐阻锈剂的性能研究[J].混凝土,2010(8):61-63. |
| [20] | 曹琨;付玉彬;李伟华;李云菊;侯保荣.迁移型阻锈剂对混凝土钢筋的保护作用[J].材料保护,2010(6):68-71. |
| [21] | 李遵云;杨林;屠柳青.新型迁移型钢筋阻锈剂对混凝土耐久性能的影响[J].新型建筑材料,2014(3):9-12. |
| [22] | 张大全;安仲勋;潘庆谊;周国定;高立新.吗啉多元胺对混凝土钢筋的阻锈作用[J].材料保护,2004(8):4-6. |
| [23] | H. E. JAMIL;A. SHRIRI;R. BOULIF.Corrosion behaviour of reinforcing steel exposed to an amino alcohol based corrosion inhibitor[J].Cement & concrete composites,20056(6):671-678. |
| [24] | J. Tritthart.Transport of a surface-applied corrosion inhibitor in cement paste and concrete[J].Cement and Concrete Research,20036(6):829-834. |
| [25] | 刘宗玉 .钢筋混凝土电迁移阻锈及除盐试验研究[D].哈尔滨工业大学,2013. |
| [26] | James M. Gaidis.Chemistry of corrosion inhibitors[J].Cement & concrete composites,20043(3):181-189. |
| [27] | L.Dhouibi;E.Triki;A. Raharinaivo.The application of electrochemical impedance spectroscopy to determine the long-term effectiveness of corrosion inhibitors for steel in concrete[J].Cement & concrete composites,20021(1):35-43. |
| [28] | H. E. Jamil;A. Shriri;R. Boulif;C. Bastos;M. R. Montemor;M. G. S. Ferreira.Electrochemical behaviour of ammo alcohol-based inhibitors used to control corrosion of reinforcing steel[J].Electrochimica Acta,200417/18(17/18):2753-2760. |
| [29] | W. Morris;M. Vazquez.A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides[J].Cement and Concrete Research,20022(2):259-267. |
| [30] | 唐军务;李森林;蔡伟成;胡明;朱雅仙.钢筋混凝土结构电渗阻锈技术研究[J].海洋工程,2008(3):83-88. |
| [31] | 金伟良;黄楠;许晨;毛江鸿.双向电渗对钢筋混凝土修复效果的试验研究--保护层阻锈剂、氯离子和总碱度的变化规律[J].浙江大学学报（工学版）,2014(9):1586-1594,1609. |
| [32] | 张俊喜;鲁进亮;蒋俊;邬永成;王昆;屈文俊.以醇胺类缓蚀剂为电解质的电化学再碱化修复效果研究[J].建筑材料学报,2012(2):200-205. |
| [33] | 沈长斌;薛钰芝.咪唑啉类缓蚀剂的结构特性及其缓蚀性能[J].大连铁道学院学报,2003(4):88-91. |
| [34] | 张光华;卢凤纪;谢曙辉.双烷基咪唑啉季铵盐在酸洗液中缓蚀性能的研究[J].西北轻工业学院学报,2001(2):29-32. |
| [35] | 余其俊;费飞龙;韦江雄;胡捷;艾志勇.阳离子型咪唑啉阻锈剂的合成及防腐蚀性能[J].华南理工大学学报（自然科学版）,2012(10):134-141. |
| [36] | 屈文俊;王哲;温华杰.迁移型阻锈剂对碳化混凝土耐久性的维护作用[J].建筑科学与工程学报,2011(3):1-8. |
| [37] | 王二强.海防工程水泥基迁移性钢筋阻锈涂料的研究[C].中国硅酸盐学会水泥分会首届学术年会论文集,2009:1-6. |
| [38] | 黄俊友;胡晓东;洪定海;李志清;刘农.电化学注入阻锈剂对混凝土中Cl-腐蚀钢筋的阻锈效果[J].建筑材料学报,2011(4):546-549. |
| [39] | 陈翠翠;周伟玲;刘加平.新型有机阻锈剂对钢筋的阻锈作用[J].建筑材料学报,2011(1):136-139,144. |
| [40] | 李志清;胡晓东;杨星;黄俊友;翁松干;郭刘超.迁移型阻锈剂内掺的阻锈效果及其对水泥凝结时间的影响[J].材料导报,2014(12):123-126. |
| [41] | 屈文俊;王哲.表面应用迁移型阻锈剂研究新进展[J].结构工程师,2009(6):150-154. |
| [42] | 黄莹;张小冬;金怀林.有机复合迁移型钢筋阻锈剂性能试验研究[J].施工技术,2012(4):74-76,83. |
| [43] | 赵曦;张小冬;周庆.迁移型钢筋阻锈剂渗透深度的XPS研究[J].混凝土与水泥制品,2004(4):5-7. |
| [44] | 高杰.表面涂抹阻锈剂对低强度混凝土耐久性影响的试验研究[J].混凝土,2011(07):140-142. |
| [45] | 张雪松.钢筋阻锈剂对混凝土碳化影响的试验研究[J].露天采矿技术,2011(01):74-75,78. |
| [46] | 蒙玮;庄庆平;汪兴达;秦明强;李遵云.复合氨基醇类钢筋阻锈剂阻锈效果及对混凝土性能影响研究[J].建材世界,2013(3):5-8. |
| [47] | 张航;陈国福;宋开伟;焦文容;汪文全;陈希才.适用于海水海砂混凝土阻锈剂的作用机理[J].材料导报,2014(20):116-121. |
| [48] | P. Kern;D. Landolt.Adsorption of organic corrosion inhibitors on iron in the active and passive state, a replacement reaction between inhibitor and water studied with the rotating quartz crystal microbalance[J].Electrochimica Acta,20014(4):589-598. |
| [49] | 王嵬;张大全;张万友;周国定.国内外混凝土钢筋阻锈剂研究进展[J].腐蚀与防护,2006(7):369-373. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%