采用四辛基溴化铵(TOAB)改善纳米二氧化硅颗粒(SiO2)的分散性,并在 SiO2表面进行聚对苯二甲酸丁二醇酯(pCBT)的接枝改性。以不同含量改性的 SiO2(0.1%~2%(质量分数))与环状聚对苯二甲酸丁二醇酯(CBT)熔融共混,原位聚合制得 SiO2/pCBT 纳米复合材料。纳米复合材料的结晶性能和力学性能表征结果表明：随着 SiO2含量的增多,结晶度逐渐提高；与纯 pCBT 相比,添加1%(质量分数)SiO2的复合材料的杨氏模量提高了22%,断裂吸收能提高约56%；此外,SiO2还能显著提高 pCBT 纳米复合材料的弹性模量和玻璃化转变温度。
The dispersion of nano SiO2 particles was improved by using tetraoctylammonium bromide(TOAB) as dispersing agent.SiO2 was successfully modified by grafting polybutylene terephthalate (pCBT)onto the surface. The pCBT nanocomposites containing different contents of modified SiO2 (0.1wt% -2wt%)were prepared via melt mixing and in-situ polymerization process.The samples were thoroughly characterized by SEM,TG,DSC,DMA and tensile tests.The results showed that the degree of crystallinity was gradually increased with the increase of SiO2 con-tent.The Young′s modulus and fracture energy of nanocomposites with 1wt% modified SiO2 increased by 22% and 56%,respectively.In addition,the elastic modulus and glass transition temperature of nanocomposites were also im-proved by adding SiO2 .
参考文献
| [1] | Hakme C;Stevenson I;Maazouz A;Cassagnau P;Boiteux G;Seytre G.In situ monitoring of cyclic butylene terephtalate polymerization by dielectric sensing[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,200747/51(47/51):4362-4365. |
| [2] | K. van Rijswijk;H.E.N. Bersee.Reactive processing of textile fiber-reinforced thermoplastic composites - An overview[J].Composites, Part A. Applied science and manufacturing,20073(3):666-681. |
| [3] | Andrew J. Hall;Phillp Hodge.Recent research on the synthesis and applications of cyclic oligomers][J].Reactive & functional polymers,19991/3JULY(1/3JULY):133-139. |
| [4] | Brunelle DJ.;Serth-Guzzo J.;Takekoshi T.;Evans TL.;Pearce EJ.;Wilson PR.;Bradt JE..Semicrystalline polymers via ring-opening polymerization: Preparation and polymerization of alkylene phthalate cyclic oligomers[J].Macromolecules,199815(15):4782-4790. |
| [5] | Hilde Parton;Joris Baets;Ignaas Verpoest;Bart Goderis;Jacques Devaux;Pascale Lipnik.Properties of poly(butylene terephthatlate) polymerized from cyclic oligomers and its composites[J].Polymer: The International Journal for the Science and Technology of Polymers,200523(23):9871-9880. |
| [6] | Ishak ZAM;Shang PP;Karger-Kocsis J.A modulated dsc study on the in situ polymerization of cyclic butylene terephthalate oligomers[J].Journal of thermal analysis and calorimetry,20063(3):637-641. |
| [7] | J. BAETS;J. DEVAUX;I. VERPOEST.Toughening of Basalt Fiber-Reinforced Composites with a Cyclic Butylene Terephthalate Matrix by a Nonisothermal Production Method[J].Advances in Polymer Technology,20102(2):70-79. |
| [8] | Jianqiang Zhang;Zongbao Wang;Bingjie Wang.Living lamellar crystal initiating polymerization and brittleness mechanism investigations based on crystallization during the ring-opening of cyclic butylene terephthalate oligomers[J].Polymer chemistry,20135(5):1648-1656. |
| [9] | Gabor Romhany;Janos Vigh;Ralf Thomann.pCBT/MWCNT Nanocomposites Prepared by In situ Polymerization of CBT After Solid-Phase High-Energy Ball Milling of CBT with MWCNT[J].Macromolecular materials and engineering,20116(6):544-550. |
| [10] | Balogh, G.;Hajba, S.;Karger-Kocsis, J.;Czigány, T..Preparation and characterization of in situ polymerized cyclic butylene terephthalate/graphene nanocomposites[J].Journal of Materials Science,20136(6):2530-2535. |
| [11] | Xiang Wang;Lei Wang;Qiang Su;Junping Zheng.Use of unmodified SiO_2 as nanofiller to improve mechanical properties of polymer-based nanocomposites[J].Composites science and technology,2013Dec.(Dec.):52-60. |
| [12] | Wang, Xiang;Wang, Peipei;Jiang, Yu;Su, Qiang;Zheng, Junping.Facile surface modification of silica nanoparticles with a combination of noncovalent and covalent methods for composites application[J].Composites science and technology,2014Nov.(Nov.):1-8. |
| [13] | Sun SS;Li CZ;Zhang L;Du HL;Burnell-Gray JS.Effects of surface modification of fumed silica on interfacial structures and mechanical properties of poly(vinyl chloride) composites[J].European Polymer Journal,20067(7):1643-1652. |
| [14] | Mathieu Bailly;Marianna Kontopoulou;Khalil El Mabrouk.Effect of polymer/filler interactions on the structure and rheological properties of ethylene-octene copolymer/nanosilica composites[J].Polymer: The International Journal for the Science and Technology of Polymers,201023(23):5506-5515. |
| [15] | Jerome F.O'Keefe.Identification of polymers by IR spectroscopy[J].Rubber World: The Technical Service Magazine for The Rubber Industry,20043(3):27-32. |
| [16] | D. Qian;E. C. Dickey;R. Andrews.Load transfer and deformation mechanisms in carbon nanotube-polystyrene composites[J].Applied physics letters,200020(20):2868-2870. |
| [17] | B. Wetzel;P. Rosso;F. Haupert.Epoxy nanocomposites - fracture and toughening mechanisms[J].Engineering Fracture Mechanics,200616(16):2375-2398. |
| [18] | Cardwell BJ.;Yee AF..Toughening of epoxies through thermoplastic crack bridging[J].Journal of Materials Science,199822(22):5473-5484. |
| [19] | J.Lee;A.F.Yee.Inorganic particle toughening I: micro-mechanical deformations in the fracture of glass bead filled epoxies[J].Polymer: The International Journal for the Science and Technology of Polymers,20012(2):577-588. |
| [20] | G.Broza;M.Kwiatkowska;Z.Roslaniec;K.Schulte.Processing and assessment of poly(butylene terephthalate)nanocompo-sites reinforced with oxidized single wall carbon nanotubes[J].Polymer: The International Journal for the Science and Technology of Polymers,200516(16):5860-5867. |
| [21] | Sandler J.;Broza G.;Nolte M.;Schulte K.;Lam YM.;Shaffer MSP..Crystallization of carbon nanotube and nanofiber polypropylene composites[J].Journal of Macromolecular Science. Physics,20033/4(3/4):479-488. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%