通过显微组织分析、室温及高温力学性能测试、XRD 和 SEM 分析等方法,研究了稀土 Pr 对 Al-5Mg 合金的显微组织、凝固区间和室/高温力学性能的影响。实验结果表明,Al-5Mg 合金中加入稀土 Pr 使合金凝固区间变窄,细化了合金组织；Pr 的加入净化了合金组织,减少了合金组织杂质缺陷,提高了合金性能；Pr 的加入对合金有固溶和强化相强化作用,β-Al11 Pr3强化相具有较高的高温稳定性能,提高了合金的高温性能。
Effects of Pr on microstructure,solidification interval and room/high temperature mechanical pro-perties of of Al-5Mg alloy were studied by microscopic analysis,room/high temperature mechanical property test, SEM and X-ray analysis methods.Experiments show that rare earth Pr can narrow the solidification interval and refine the microstructure and improve its tensile properties at both room temperature and high temperature.The addition of Pr can purify the microstructure and reduce the impurity and defects,and improve the performance of alloy.The rare earth Pr plays an important role on both solid solution strengthening and phase reinforcement.β-Al1 1 Pr3 strengthening phase has high heat stability,and can improve the high temperature properties of the alloy.
参考文献
| [1] | 舒滢;黄张洪;彭雯雯;曾卫东;赵永庆.铸态Ti40阻燃钛合金高温拉伸力学性能及断裂行为研究[J].材料导报,2014(20):84-87,98. |
| [2] | 陈祥;陈康华;方华婵.稀土Pr对Al-Zn-Mg-Cu-Zr合金组织和性能的影响[J].粉末冶金材料科学与工程,2009(3):147-151. |
| [3] | 李桂荣;王宏明;赵玉涛;陈刚;陈登斌;韩剑;戴起勋.稀土钇对7055铝合金熔炼和凝固过程的作用机制[J].稀有金属材料与工程,2010(1):80-84. |
| [4] | 高原;张维;李冰;袁琳;陈选楠.稀土（钇）对钨钼原子扩散系数的影响[J].稀有金属材料与工程,2012(12):2154-2156. |
| [5] | 李海;杨迎新;郑子樵;王芝秀.少量Sc对7055铝合金组织与性能的影响[J].材料科学与工艺,2006(1):46-49. |
| [6] | 杨军军;聂祚仁;金头男;阮海琼;左铁镛.稀土铒在Al-Zn-Mg合金中的存在形式与细化机理[J].中国有色金属学报,2004(4):620-626. |
| [7] | 韩剑;戴起勋;李桂荣;陈登斌;赵玉涛;刘瑜;陈刚;程晓农.稀土钇对7055铝合金铸态组织的影响[J].材料工程,2009(4):67-70. |
| [8] | 张新明;彭卓凯;陈健美;邓运来.耐热镁合金及其研究进展[J].中国有色金属学报,2004(9):1443-1450. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%