运用View cast对所设计的铸铁模消失模铸造工艺进行数值模拟,预测工艺方案所产生的缩孔、缩松的大小和位置.模拟结果显示,铸件实现了顺序凝固,无明显缩孔、缩松缺陷.此外,铸件设置加强肋保证了铸铁模在使用过程中不会因冷热交变产生挠曲变形.利用消失模铸造生产的铸铁模组织以针状铁素体和珠光体为主,加热至500℃、700℃,试样组织和硬度没有明显变化,加热至900℃时发生了铁素体向奥氏体转变,冷却后生成均匀分布的珠光体以及细小的铁素体.氧化实验分析发现,温度对试样的氧化速率有较大影响,主要是因为不同温度下试样表面生成不同的氧化膜,使试样的氧化速率有较大的差异.
The simulation software View cast was used to predict the sizes and positions of the shrinkage in the casting-pattern produced by lost foam casting.The result showed that the sequence solidification was achieved in the casting process;no defect was observed which are satisfied with the technical requirements.Reinforcing rib was de-signed to ensure that the cast iron mould was not deformed in the process of the cold and heat.The microstructure of the material which was observed under the optical microscope was mainly based on acicular ferrite and pearlite.When heated to 500 ℃ and 700 ℃,there was no obvious changes of the hardness and organization.While heated to 900 ℃, ferrite austenite transformation,and the uniform distribution of pearlite after cooling,at the same time,the samples had significant decrease in hardness.It can be learned from the analysis of oxidation experiments that the temperatures have great influence on the oxidation rate of sample,and reason for this phenomenon is that different thickness of oxide films were formed under different temperatures,as a result,the oxidation rate of the samples treated under dif-ferent temperatures is different.
参考文献
| [1] | 刘子利.消失模铸造充型过程的研究进展及展望[J].铸造,2000(04):213. |
| [2] | 陈尧剑;黄天佑;康进武;胡永沂.消失模铸造制模设备国内外现状及展望[J].中国铸造装备与技术,2002(4):1-4. |
| [3] | 秦国治.铸铁、铸钢的消失模铸造工艺[J].铸造设备研究,2007(05):25-27,54. |
| [4] | 朱丽娟;周源;王明娜;张喻;董秀奇.消失模负压铸造浇注系统设计的探讨[J].铸造技术,2009(7):942-944. |
| [5] | 米国发;何斌锋.计算机模拟在铸钢阀体工艺优化中的应用[J].热加工工艺,2009(11):60-62,65. |
| [6] | 米国发;何斌锋.计算机模拟在铸钢后桥工艺优化中的应用[J].航天制造技术,2008(2):44-48. |
| [7] | 宁玫;李志群;孙梅红;张志远;杨翠丽.魏氏组织形成机理及对钢管性能影响的分析研究[J].天津冶金,2008(5):118-124. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%