基于气体捕捉法制备泡沫钛三明治结构工艺,对以钢包套+Ti-6Al-4V板+Ti-6Al-4V粉的封装工艺制备的泡沫Ti-6Al-4V三明治结构预制坯进行了900℃下不同变形量的轧制,并进行了950℃/10 h的等温发泡.通过SEM对不同状态的三明治结构芯部孔洞状态进行观察和测量,探究了轧制变形量对泡沫Ti-6Al-4V三明治结构预制坯等温发泡行为的影响.结果表明:轧制主要是以沿轧制方向拉长孔洞和增加孔洞连通的方式影响泡沫Ti-6Al-4V三明治结构芯部,且轧制变形量越大越严重,但对孔洞内壁形态及孔洞在垂直于轧向平面内的形态未产生影响.当预制坯轧制变形量为80％时,经等温发泡成功制备了面板厚度为362 μm,芯部孔隙率达到40％的泡沫Ti-6Al-4V三明治结构,其在高应变速率下抗压强度达到824.8 MPa,400℃下热导率仅为致密金属的52.8％.
参考文献
| [1] | Hideo Nakajima.Fabrication, properties and application of porous metals with directional pores[J].Progress in materials science,20077(7):1091-1173. |
| [2] | O. Smorygo;A. Marukovich;V. Mikutski;A.A. Gokhale;G. Jagan Reddy;J. Vinod Kumar.High-porosity titanium foams by powder coated space holder compaction method[J].Materials Letters,2012:17-19. |
| [3] | Effect of pore size on the tensile behavior of open-cell Ti foams: Experimental results[J].Materials Letters,20108(8):935. |
| [4] | Douglas T. Queheillalt;Kevin A. Gable;Haydn N.G. Wadley.TEMPERATURE DEPENDENT CREEP EXPANSION OF Ti-6Al-4V LOW DENSITY CORE SANDWICH STRUCTURES[J].Scripta materialia,20013(3):409-414. |
| [5] | RAVI VANCHEESWARAN;DOUGLAS T. QUEHEILLALT;DANA M. ELZEY.Simulation of the Creep Expansion of Porous Sandwich Structures[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,20017(7):1813-1821. |
| [6] | 王哲磊;任学平;侯红亮;王耀奇.封装条件对气体捕捉法制备泡沫Ti-6Al-4V的影响[J].粉末冶金材料科学与工程,2015(3):362-367. |
| [7] | 王哲磊;任学平;侯红亮;王耀奇;逯伟.基于气体捕捉法的泡沫Ti－6Al－4V等温发泡规律研究[J].材料科学与工艺,2015(4):1-6. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%