对X90管线钢埋弧焊焊接接头在500～600℃高温回火处理,之后进行拉伸、硬度和冲击测试,并利用扫描电镜对焊接接头显微组织及断口进行分析.结果表明,回火处理后的试样组织多边形类晶粒增多,且M/A组织逐渐分解;其中抗拉强度在回火温度为600℃时下降幅度最大;冲击韧性在550℃时达到峰值208.70 J,提高了41.9％;回火温度在500～600℃时,试样呈软化-硬化的规律.试验结果表明,经过550℃热处理后的焊接接头塑韧性得到明显改善,其具有良好的综合性能,这一好的性能归因于组织内M/A淬硬相的分解、位错的重组合并及较少的析出相.
参考文献
| [1] | 霍松波;姜金星;黄一新;左秀荣;张展展.X80管线钢焊接接头组织及性能的研究[J].材料与冶金学报,2013(2):136-141. |
| [2] | Zhao, W.;Wang, W.;Chen, S.;Qu, J..Effect of simulated welding thermal cycle on microstructure and mechanical properties of X90 pipeline steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201124(24):7417-7422. |
| [3] | D. J. Abson;Y. Tkach;I. Hadley.A Review of Postweld Heat treatment Code Exemptions[J].Welding Journal,20063(3):63-69. |
| [4] | P.C. Chung;Yoonjin Ham;Sanghoon Kim;Jeongho Lim;Changhee Lee.Effects of post-weld heat treatment cycles on microstructure and mechanical properties of electric resistance welded pipe welds[J].Materials & design,2012Feb.(Feb.):685-690. |
| [5] | 夏佃秀;王学林;李秀程;由洋;尚成嘉.X90级别第三代管线钢的力学性能与组织特征[J].金属学报,2013(3):271-276. |
| [6] | A. Yu. Ivanov;R. V. Sulyagin;V. V. Orlov.FORMATION OF STRUCTURE IN THE HEAT-AFFECTED ZONE AND PROPERTIES OF WELDED JOINTS OF PIPE STEELS OF STRENGTH CLASSES X80 AND X90[J].Metal Science and Heat Treatment,201211/12(11/12):560-566. |
| [7] | 武会宾;尚成嘉;杨善武;侯华兴;马玉璞;于功利.超细化低碳贝氏体钢的回火组织及力学性能[J].金属学报,2004(11):1143-1150. |
| [8] | 刘庆冬;刘文庆;王泽民;周邦新.回火马氏体中合金碳化物的3D原子探针表征Ⅰ.形核[J].金属学报,2009(11):1281-1287. |
| [9] | 张可;雍岐龙;孙新军;李昭东;赵培林;陈守东.回火温度对高Ti微合金直接淬火高强钢组织及性能的影响[J].金属学报,2014(8):913-920. |
| [10] | 柴锋;杨才福;张永权;徐洲.粒状贝氏体对超低碳含铜时效钢粗晶热影响区冲击韧性的影响[J].钢铁研究学报,2005(1):42-46. |
| [11] | 李振江;肖纳敏;李殿中;张俊勇;罗永建;张瑞雪.G18CrMo2-6钢回火组织及冲击韧性研究[J].金属学报,2014(7):777-786. |
| [12] | 郝宪朝;高明;张龙;赵秀娟;刘奎.退火态12Cr13不锈钢显微组织及其对冲击韧性的影响[J].金属学报,2011(7):912-916. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%