以硅藻土为模板,糠醇为碳源,合成了模板炭材料,并用KOH活化制备多孔炭材料.利用XRD、拉曼光谱、SEM及N2吸附对其结构进行表征,并对比研究了活化前后炭材料的电化学性能.结果表明:活化后模板炭的无序度增加,电化学性能有显著的提高.在1 A·g-1的电流密度下,活化后的多孔炭比容量为45.0～69.2 F·91;在20A·g-1充放电时,比电容保持率仍可达45％以上.说明活化后的多孔炭材料具有良好的电化学性能,是较好的双层电容器电极材料.
Diatomite-templated carbon was prepared with diatomite as template and furfuryl alcohol (FA) as carbon resource,which was further activated with potassium hydroxide as activating agent.The prepared carbon materials were characterized by means of X-ray diffraction (XRD),Raman spectroscopy,scanning electron microscopy (SEM) and N2 adsorption.Simultaneously,the electrochemical properties of the porous carbon before and after activation were studied.The results show that the porous carbon after activation has higher degree of disorder in chemical structure and better electrochemical properties rather than the one before activation.The specific capacitance of the porous carbon was in the range from 45.0 to 69.2 F·g~ by the current density of 1 A·g-1 and the capacitance retention remains more than 45％ by the current density of 20 A· g1.These results show that the porous carbon after activation has good electrochemical performance and it's an ideal material for electric double layer capacitor.
参考文献
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%