为解决分布在西部盐湖地区出现的煤矿矿区钢材腐蚀问题,结合煤矿矿区实际环境,采用实验、理论分析等方法研究了镁水泥混凝土中钢筋的腐蚀.采用CS350电化学工作站,研究镁水泥混凝土中钢筋的电化学腐蚀,结合SEM微观实验和EDS元素扫描结果,对镁水泥混凝土中裸露钢筋腐蚀状况进行描述.研究表明:美加力涂层钢筋状态良好,未出现腐蚀状态;锌美特涂层钢筋出现了低腐蚀现象;而裸露钢筋表面出现了严重腐蚀.钢筋涂层防腐蚀性美加力涂层较好,锌美特涂层次之;涂层钢筋虽然防腐效果不同,但对裸露钢筋的防腐蚀性能有明显有利影响.
In order to solve reinforced corrosion on coal mine area in the salt lake of the west, in combination with the practical environment of coal mine area, experiment and theory analysis methods were used to study the reinforced corrosion in magnesium cement concrete. By CS350 electrochemical workstation, a study on the electrochemical corrosion of reinforced in magnesium cement concrete was carried out. Combined with the SEM and EDS, status of bare reinforced corrosion in magnesium cement concrete was described. Results showed that state of steel bar with MAGNI coating was better, and did not produce corrosion;steel bar with ZINTEK coating resulted in phenomena of low corrosion; the corrosion of bare steel bar on surface was serious. The order from high to low anticorrosion performance of the coating is from MAGNI to ZINTEK coating. Anticorrosive effects of coating on steel bar are in very different level, but the coating positively affects anticorrosion performance of the steel bar.
参考文献
| [1] | 王琦;邵行;李术才;王德超;李为腾;王富奇;刘文江;张世国.方钢约束混凝土拱架力学性能及破坏机制[J].煤炭学报,2015(4):922-930. |
| [2] | 顾宝珊;弋慧丽;杨培燕;宫丽.树脂含量对半无机型无铬无取向硅钢涂层性能的影响[J].材料科学与工艺,2013(6):109-115. |
| [3] | 周俊龙;欧忠文;江世永;陈乔;陈云;陈寒斌;许春霞.掺阻锈剂掺合料海水海砂混凝土护筋性探讨[J].建筑材料学报,2012(1):69-74. |
| [4] | 张书禹;王晓超;张文战;薛守洪.恶劣大气环境中输变电金属设施防腐蚀涂层制备及性能[J].腐蚀与防护,2015(2):201-205. |
| [5] | 乔宏霞;刘尧;周茗如;余红发;董金美;冯坚.氯氧镁水泥钢筋混凝土轴压构件力学性能[J].煤炭学报,2013(z2):337-342. |
| [6] | 王莹;俞宏英;程远;孙冬柏.X80钢在伊川土壤模拟溶液中的腐蚀行为[J].材料科学与工艺,2013(3):129-136. |
| [7] | Jamari, Siti Khumaira Mohd;Kasi, Ramesh;Ismail, Leeana;Nor, Nur Amirah Mat;Rau, S. Rames;Subramaniam, T. Ramesh;Balakrishnan, Vengadaesvaran;Arof, Abdul Kariem Mohd.Acrylic polyol/silicone coating corrosion protection analysis using electrochemical impedance spectroscopy[J].Pigment & Resin Technology,20151(1):41-47. |
| [8] | Luciana VR de Messano;Barbara LIgnacio;Maria HCB Neves;Ricardo Coutinho.In situ Colonization of Marine Biofilms on UNS S32760 Duplex Stainless Steel Coupons in Areas with Different Water Qualities: Implications for Corrosion Potential Behavior[J].船舶与海洋工程学报（英文版）,2014(3):346-353. |
| [9] | 王金虎;翟文杰.电势对硅片摩擦电化学材料去除特性的影响[J].哈尔滨工业大学学报,2014(7):20-24,31. |
| [10] | 周松兵;陈步明;郭忠诚;徐瑞东;张永春;杨海涛.锌电沉积用Al/Pb－Ag－Sn阳极的电化学性能研究[J].材料科学与工艺,2015(1):108-114. |
| [11] | 马志鸣;赵铁军;巴光忠;管庭.冻融环境下引气混凝土的抗钢筋锈蚀能力研究[J].建筑科学与工程学报,2014(3):85-89. |
| [12] | 伊廷锋;刘计;王振波;陈体衔;刘孝伟;郝国栋;左朋建.阀控密封铅酸电池正极板栅在不同硫酸电解液中的电化学行为[J].哈尔滨工业大学学报,2014(10):65-68. |
| [13] | 卢亦焱;齐波;李杉;李娜.FRP 加固混凝土柱钢筋锈蚀电化学特性[J].华中科技大学学报（自然科学版）,2015(1):34-38. |
| [14] | 陈翠翠;蔡景顺;刘建忠;刘加平.新型氨基醇阻锈剂在氯盐污染钢筋混凝土中的应用[J].硅酸盐学报,2015(4):393-399. |
| [15] | 姬永生;张领雷;马会荣;王志龙;周敏.氯离子诱发混凝土中钢筋锈蚀的锈蚀层分析[J].中南大学学报（自然科学版）,2012(11):4484-4490. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%