采用慢应变速率试验、电化学测试、失重试验以及扫描电镜观察等方法研究了模拟深海环境中阴极极化电位作用下高强钢的腐蚀规律.结果表明:施加阴极极化电位由-0.71 V(vs Ag/AgCl,下同)负移至-0.85 V,腐蚀速率由0.245 0 mm/a减小到0.006 6mm/a,在-0.71～-0.90 V电位区间,高强钢主要为韧性断裂;当极化电位等于或负于-0.95 V后,断口开始呈现典型脆性断裂特征,高强钢已进入氢脆的危险区.可以确定最佳的阴极保护电位区间为-0.76～-0.94 V.
参考文献
| [1] | 许立坤;马力;邢少华;程文华.海洋工程阴极保护技术发展评述[J].中国材料进展,2014(2):106-113. |
| [2] | D. Hardie;E.A. Charles;A.H. Lopez.Hydrogen embrittlement of high strength pipeline steels[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,200612(12):4378-4385. |
| [3] | X.S. Du;Y.J. Su;J.X. Li;L.J. Qiao;W.Y. Chu.Inhibitive effects and mechanism of phosphates on the stress corrosion cracking of brass in ammonia solutions[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012Jul.(Jul.):69-75. |
| [4] | Pasupathi Sivakumar;Vincenzo Tricoli.Novel Pt-Ru nanoparticles formed by vapour deposition as efficient electrocatalyst for methanol oxidation, Part II. Electrocatalytic activity[J].Electrochimica Acta,20067(7):1235-1243. |
| [5] | 郝文魁;刘智勇;王显宗;李晓刚.舰艇用高强钢强度及其耐蚀性现状及发展趋势[J].装备环境工程,2014(1):54-62. |
| [6] | 杨兆艳;闫永贵;马力;张桂玲.阴极极化对907钢氢脆敏感性的影响[J].腐蚀与防护,2009(10):701-703. |
| [7] | 黄晓艳;刘波.舰船用结构材料的现状与发展[J].船舶,2004(3):21-24. |
| [8] | 常娥;闫永贵;李庆芬;马力.阴极极化对921A钢海水中氢脆敏感性的影响[J].中国腐蚀与防护学报,2010(1):83-88. |
| [9] | 高海平;张慧霞;郭为民;侯健;周娟;宋泓清.阴极极化对高强钢焊接件应力腐蚀敏感性的影响[J].装备环境工程,2014(1):7-12,29. |
| [10] | 张慧霞;戚霞;邓春龙;王伟伟.极化电位下高强钢腐蚀疲劳裂纹扩展的表征[J].腐蚀科学与防护技术,2011(3):228-232. |
| [11] | 谭文志;杜元龙.阴极保护导致ZC-120钢在海水中环境氢脆[J].材料保护,1988(03):10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%