研究了封隔器常用的两种铬钼钢35CrMo和42CrMo在不同温度和压力条件下的腐蚀行为,并考察了腐蚀前后两种材料力学性能的变化.通过失重法得出了两种材料在不同条件下的腐蚀速率.结果表明:在相同的温度、压力条件下,42CrMo试样的腐蚀速率比35CrMo试样的大;两种材料的腐蚀速率均随温度的升高先增加后下降,随压力的升高而增加;腐蚀前42CrMo试样的抗拉强度和抗弯曲强度都比35CrMo试样的大,表明42CrMo钢的力学性能要优于35CrMo钢的,但腐蚀后42CrMo试样力学性能的降低程度要比35CrMo试样的多,这表明腐蚀越严重,材料的力学性能损失越大.
参考文献
| [1] | 张立新;沈泽俊;李益良;张国文;高向前.我国封隔器技术的发展与应用[J].石油机械,2007(8):58-60,74. |
| [2] | Charis A. Apostolopoulos;Sotiris Demis;Vagelis G. Papadakis.Chloride-induced corrosion of steel reinforcement - Mechanical performance and pit depth analysis[J].Construction and Building Materials,2013Jan.(Jan.):139-146. |
| [3] | Xinxin Wang;Yimin Gao;Kuang Li;Jingbo Yan;Yefei Li;Jianbo Feng.Effect of yttrium on the corrosion behaviour of 09CrCuSb alloy in concentrated sulphuric acid[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013Apr.(Apr.):369-375. |
| [4] | 毛红艳;蔡庆伍;武会宾;孙超凡;梁金明;周洪宝.合金元素和碳含量对E36船板钢腐蚀行为的影响[J].腐蚀与防护,2013(6):499-502. |
| [5] | J. O. Park;S. Matsch;H. Bohni.Effects of Temperature and Chloride Concentration on Pit Initiation and Early Pit Growth of Stainless Steel[J].Journal of the Electrochemical Society,20022(2):B34-B39. |
| [6] | 林冠发;白真权;赵新伟;郑茂盛;路民旭.CO2腐蚀产物膜形态结构与温度和压力的关系[J].石油机械,2005(2):1-4. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%