对新型 ADB610低碳贝氏体钢进行了焊条电弧焊接，采用柔度法得到了焊接接头裂纹长度(a )和循环寿命(N )的关系曲线；根据 a-N 曲线采用一次七点递增多项式拟合方法计算了母材、热影响区和焊缝的疲劳裂纹扩展速率(da/dN )，并和应力强度因子范围(ΔK )数据进行回归拟合，得到了以 Paris 公式表达的焊接接头各区域的疲劳裂纹扩展速率表达式。结果表明：在疲劳裂纹扩展的初期和中期，焊缝的裂纹扩展速率最慢，母材区裂纹扩展速率最快；在裂纹扩展末期，三区域的裂纹扩展速率相近。
The ADB610 steel was welded using shielded metal arc welding method,and the fatigue crack length (a )vs.fatigue life (N )curves was measured by using crack compliance method.Base on a-N curves,the fatigue crack propagation rates of each sample from base material (BM),heat affected zone (HAZ)and weld seam (WS)were calculated by fitting a polynomial to a strip of 7 data points and linear regression fitted with stress intensity factor range (ΔK ).The formula based on Paris of (da/dN )and (ΔK )was obtained.The results show that the fatigue crack growth rate in BM was higher than that in HAZ and WS,and that in WS was the slowest during the early and middle stage of crack growth;during the last stage of crack growth the difference of fatigue crack growth rate in three regions was not significant.
参考文献
| [1] | 徐灏.疲劳强度[M].北京:高等教育出版社,1988 |
| [2] | 佐藤邦彦;向井喜彦;豊田政田;张伟昌,严茑飞,徐晓.焊接接头的强度与设计[M].北京:机械工业出版社,1983 |
| [3] | 王希靖,李树伟,牛勇,张杰.A7075搅拌摩擦焊疲劳裂纹扩展速率试验分析[J].焊接学报,2008(09):5-7. |
| [4] | 霍立兴.焊接结构的断裂行为及评定[M].北京:机械工业出版社,2000 |
| [5] | 张天会,闫沛军,徐人平,薛彬.低碳贝氏体ADB610钢焊接缺陷统计分析研究[J].热加工工艺,2009(13):151-153. |
| [6] | :GB/T 6398-2000.金属材料疲劳裂纹扩展速率试验方法[S].北京:中国标准出版社,2000. |
| [7] | PARIS P C;ERDOGEN F .A critical analysis of crack propagation Laws[J].Journal of Basic Engineering Transactions：ASME Series D,1963,85(3):528-534. |
| [8] | 史耀武,史轩.HG80钢及其焊接接头的疲劳裂纹扩展[J].机械工程材料,2003(08):5-7,43. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%