为研究 TC21钛合金时效时析出α相的长大动力学，采用 JMatPro 软件模拟计算得到了钛合金时效相平衡时α相和β相的化学成分与时效温度的关系，计算得到了在500~900℃下等温时效时析出α相的长大速率与温度的关系式，并进行了试验验证。结果表明：在750℃以下等温时效时，析出α相的长大速率较慢，时效温度高于800℃时，长大速率随温度升高而迅速增加，这是由合金元素的扩散系数随温度的变化而决定的；试验得到的 TC21钛合金在900℃等温时效时析出α相的长大速率与模拟计算得到的结果一致，析出α相的生长速率随温度升高不断增大。
In order to study the growth kinetics ofαphase precipitation in TC21 titanium alloy during ageing treatment,the relationship between the elemental composition ofβandαphase and aging temperature was obtained using JMatPro software.The equation between the αphase growth rate and aging temperature of 500-900 ℃ was also obtained by calculation and verified by experiment.The results show that when the aging temperature was below 750 ℃,the αphase growth rate increased slowly,while the temperature higher than 800 ℃,the growth rate increased rapidly with temperature rising,as the element diffusion coefficient increased with the aging temperature rising.The α phase growth rate obtained by observing the microstructure of TC21 titanium alloy after isothermal aged at 900 ℃ was consistent with the simulated result.Theαphase growth rate increased with the increase of aging temperature.
参考文献
| [1] | 付艳艳,宋月清,惠松骁,米绪军.航空用钛合金的研究与应用进展[J].稀有金属,2006(06):850-856. |
| [2] | 李启鹏,李伟,杨磊,王学德.航空用钛合金抗微动疲劳表面改性技术的研究进展[J].机械工程材料,2012(11):9-13. |
| [3] | 陈健,刘雪飘,梁欢.铜镍钴铍合金的时效相变动力学方程[J].机械工程材料,2011(01):19-21,25. |
| [4] | 甘国强;李萍;薛克敏 等.热变形参数对 TA15 合金组织的影响及其相变动力学[J].功能材料,2011,42(5):828-831. |
| [5] | 常辉,E. Gautier,F. Bruneseaux,周廉.Ti-B19钛合金的β→α+β等温相变动力学[J].稀有金属材料与工程,2006(11):1695-1699. |
| [6] | 张颖楠,赵永庆,曲恒磊,李辉,冯亮,郭红超,黄定坤.热处理对TC21合金显微组织和室温拉伸性能的影响[J].稀有金属,2004(01):34-38. |
| [7] | 费玉环,周廉,曲恒磊,赵永庆,冯亮.两相区热处理对TC21钛合金显微结构的影响[J].稀有金属材料与工程,2007(11):1928-1932. |
| [8] | 刘宗昌;任惠平.金属固态相变教程[M].北京:冶金工业出版社,2003:20-23. |
| [9] | 朱知寿,王新南,童路,刘东升.新型TC21钛合金相变行为和相组成研究[J].稀有金属快报,2006(12):23-27. |
| [10] | 葛鹏;赵永庆;周廉.超高强结构钛合金成分设计中的钼当量选择与多组元化[A].北京:中国材料研究学会,2003:504-507. |
| [11] | 李哲,秦林,马连军,范爱兰,张万祯,唐宾.Ti-6Al-4V表面等离子合金层中渗Mo的扩散系数[J].中国有色金属学报,2010(06):1137-1142. |
| [12] | 冯亮,李金山,黄磊,常辉,崔予文,周廉.Ti-Mo二元合金在β相区的互扩散行为[J].中国有色金属学报,2009(10):1766-1771. |
| [13] | 郑子樵.材料科学基础[M].长沙:中南大学出版社,2005:193-209. |
| [14] | 徐东,祭程,唐正友,朱苗勇.SCM435钢贝氏体中碳原子的扩散行为[J].过程工程学报,2013(01):17-22. |
| [15] | 赵永庆;洪权;葛鹏.钛及钛合金金相图谱[M].长沙:中南大学出版社,2010:65-98. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%