以天然气分输减压阀阀体用1．6220铸钢为研究对象，采用低温拉伸以及低温冲击试验方法研究了其热轧态和调质态的力学性能随试验温度的变化规律，获得了其韧脆转变温度，观察了不同温度下冲击试样的断口形貌.结果表明：随着试验温度的降低，该铸钢的屈服强度和抗拉强度显著提高，断面收缩率和伸长率逐渐下降；调质处理明显改善了铸钢的低温力学性能，调质态铸钢的屈服强度、抗拉强度、塑性均比热轧态的高，韧脆转变温度由热轧态的2．76℃降低到－14．46℃；随着温度的降低，铸钢的断裂形式由韧性断裂向解理断裂转变.
With 1.6220 cast steel for pressure regulating valve body of natural gas transportation as the research object,the change law of mechanical properties versus temperature of the hot rolled and quenched &tempered cast steels was studied by the low temperature tensile test and impact test,and then the ductile-brittle transition temperature was calculated.The fracture morphology at different temperatures was also observed.The results show that with the decrease of the temperature,the yield strength and tensile strength of the cast steel increased and the percentage reduction of area and elongation reduced.The quenching and tempering treatment significantly improved the low temperature mechanical properties of the cast steel.The yield strength,tensile strength and plasticity of the quenched & tempered cast steel were higher than those of hot rolled one,and the ductile-brittle transition temperature of the cast steel in quenching & tempering state decreased to -14.46 ℃ from 2.76 ℃ in hot rolled state.With the temperature decrease,the fracture pattern of the cast steel changed from cleavage fracture into dimple fracture.
参考文献
| [1] | 李红英.浅论低温对金属材料性能的影响[J].现代矿业,2011(04):113-115. |
| [2] | 王元清;周晖;胡宗文;石永久;陈宏.钢结构厚板力学性能的低温试验研究[J].土木建筑与环境工程,2011(5):7-12. |
| [3] | 奚望;王元清;石永久.钢轨钢材低温力学性能的试验研究[J].铁道工程学报,2006(8):25-29. |
| [4] | 王元清;林云;张延年;石永久;陈宏.高强度钢材Q460C低温力学性能试验[J].沈阳建筑大学学报（自然科学版）,2011(4):646-652. |
| [5] | Yanmin Wu;Yuanqing Wang;Yongjiu Shi;Jianjing Jiang.Effects of low temperature on properties of structural steels[J].北京科技大学学报(英文版),2004(05):442-448. |
| [6] | 张世英;郭金;张伟强.40CrNi2Mo钢的低温力学性能[J].机械工程材料,2010(11):79-82. |
| [7] | 惠亚军;赵爱民;赵征志;黄耀;李文远.生产工艺对690MPa级工程机械用钢组织与力学性能的影响[J].机械工程材料,2013(8):55-58. |
| [8] | 蒋长虹;惠亚军;赵爱民;赵征志;黄耀;李蕾;李文远;武会宾.回火温度对690 MPa级工程机械用钢组织与性能的影响[J].材料热处理学报,2013(6):103-109. |
| [9] | 张凯;易小刚;彭倩筠;曾邵华;周水波.热处理工艺对工程机械用1000 MPa级高强钢组织与性能的影响[J].机械工程材料,2014(4):29-34. |
| [10] | 张玉玲;潘际炎.低温对钢材及其构件性能影响研究综述[J].中国铁道科学,2003(2):89-96. |
| [11] | 陈国庆.电力机车常用材料低温机械性能分析[J].电力机车与城轨车辆,2004(02):37-38. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%