利用光学显微镜、拉伸和冲击试验机、显微硬度计等对高温运行前后12Cr1MoV 钢焊接接头的组织及力学性能进行了研究。结果表明：高温运行后,焊接接头组织中除了原始组织中的铁素体和珠光体外,还出现颗粒状析出物,热影响区和焊缝处组织中出现了贝氏体；焊接接头的屈服强度和抗拉强度分别由高温运行前的455,625 MPa 下降为430和583 MPa,平均冲击功从160 J下降为124 J；冲击断口上有许多裂纹,裂纹上有明显的台阶,断裂方式为塑性断裂；高温运行后母材和焊缝区的硬度分别为190,265 HV,焊缝的硬度符合供货方技术要求,而母材硬度超标。
The microstructures and mechanical properties of 12Cr1MoV steel welded joints before and after high temperature service were studied by optical microscopy,impact and tension test and micro-hardness test.The results show that after high temperature service,the microstructure of the welded joint consisted of not only ferrite and pearlite existed in the original structure but also granular precipitates.And the bainite was also found in the microstructures of heat affected zone and weld seam.The yield strength and tensile strength of the welded joint decreased from 455,625 MPa before high temperature service to 430 MPa and 583 MPa respectively and the average impact energy decreased from 1 60 J to 124 J.Many cracks were observed at the impact fracture surface and obvious steps existed on them.The facture mode was plastic fracture.The hardness of base metal and weld seam after high temperature service were 1 90 HV and 265 HV respectively,and the hardness of weld seam met the technical requirement of the supplier while that of base metal exceeded badly.
参考文献
| [1] | 张红旗 .基于图像处理技术的12Cr1MoV钢金相组织分析研究[D].内蒙古农业大学,2013. |
| [2] | 侯伟鹏.12Cr1MoV钢主蒸汽管道焊接工艺[J].管道技术与设备,2011(03):45-47. |
| [3] | 杨淑红;郭福祥.电站锅炉过热器的失效分析与寿命评估[J].电力学报,2010(3):235-238. |
| [4] | 梁秀兰;有移亮;张峥.12Cr1MoV锅炉过热器管长期过热开裂原因分析[J].机械工程学报,2014(8):81-86. |
| [5] | 杨瑞成;孟威;陈奎;王晖.12Cr1MoV高温时效过程的动力学研究[J].材料科学与工艺,2008(1):19-22. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%