利用液压疲劳试验机,采用轴向应变控制方法在455℃下对2．25Cr1MoV 钢进行高温低周疲劳试验,通过在峰值应变拉伸时保载0,60,600 s,研究了拉伸保载时间对该钢低周疲劳行为的影响,并用扫描电镜对断口形貌进行了观察.结果表明：2．25Cr1MoV 钢呈明显的循环软化特性,拉伸保载会明显降低循环应力幅,但保载时间对循环应力幅的影响不大；拉伸保载使该钢的疲劳寿命降低,但保载时间超过60 s 后,疲劳寿命基本不受保载时间的影响；拉伸保载没有改变试验钢的疲劳断裂模式.
High temperature low cycle fatigue test was carried out on 2.25Cr1MoV steel by using a hydraulic fatigue testing system under strain-controlled mode at 455 ℃.Different tensile hold time (0,60,600 s)was imposed at peak strain to study the effect of tensile holding load time on low cycle fatigue behavior of the steel.The fracture morphology of the steel was observed by scanning electron microscopy.The results reveal that the steel showed cyclic softening characteristics.The applied tensile holding load caused the stress amplitude obviously reduced,but the holding load time had little effect on cyclic stress amplitude.The fatigue life of the steel decreased because of tensile holding,but the life changed little when holding time exceeded 60 s.The fracture mode was not changed by the tensile holding load.
参考文献
| [1] | 张智峰;李向;陈永波.加氢反应器用2.25Cr1Mo0.25V锻件的研制[J].装备机械,2014(1):20-26. |
| [2] | 徐亮;黄金国;王利;何前进;顾先山.2.25Cr-1Mo-0.25V钢性能研究及其在加氢反应器上的应用[J].化工机械,2012(6):773-777,819. |
| [3] | 杨易坤.2．25Cr-1Mo-0．25V 钢厚壁锻件性能热处理研究[J].大型铸锻件,2014(03):16-19. |
| [4] | Takashi Ogata;Masatsugu Yaguchi.Damage mechanism in weldment of 2.25Cr-1Mo steel under creep-fatigue loading[J].Engineering Fracture Mechanics,20076(6):947-955. |
| [5] | 叶小松;刘应虎;田洪波;吴明华;何鹏.采用窄间隙埋弧焊焊接2.25Cr-1Mo-0.25V钢的试验及应用研究[J].大型铸锻件,2009(5):30-33,37. |
| [6] | 宋立平;孙荣禄.2.25Cr-1Mo-0.25V钢焊缝的性能研究[J].热加工工艺,2012(21):15-17. |
| [7] | 闫佳佳;安红萍.锻态2．25Cr1Mo 0．25V 钢奥氏体晶粒长大规律的研究[J].大型铸锻件,2013(4):23-26. |
| [8] | 薛永栋;晋帅勇;汪勇;赵越;郭彪;贺强;赵阳磊.2.25Cr-1Mo-0.25V加氢模拟环锻件钢的冶炼[J].大型铸锻件,2013(2):48-50. |
| [9] | 于涛;施惠基.长期高温使用后2.25Cr-1Mo钢焊接接头热影响区的蠕变损伤[J].机械工程材料,2011(4):1-3,31. |
| [10] | Shi, D.;Liu, J.;Yang, X.;Qi, H.;Wang, J..Experimental investigation on low cycle fatigue and creep-fatigue interaction of DZ125 in different dwell time at elevated temperatures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20101(1):233-238. |
| [11] | Tarun Goswami;Hannu Hanninen.Dwell effects on high temperature fatigue behavior Part I[J].Materials & Design,20013(3):199-215. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%